Water/oil resistant composition, article treated therewith, and processes for their production

a technology of composition and oil, applied in the field of water/oil resistant composition, an article treated therewith, can solve the problems of troublesome operation, substitute water/oil resistant composition, troublesome operation, etc., and achieve the effect of reducing odor, reducing odor, and reducing odor

Inactive Publication Date: 2012-09-06
ASAHI GLASS CO LTD
View PDF14 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0037]The water / oil resistant composition of the present invention can impart a sufficient water / oil resistance to a base material even though a fluorinated copolymer having Rf groups with at most 6 carbon atoms or perfluoropolyether is used, and the water / oil resistance is not substantially influenced by the pH of dilution water or the adjuvant used at the time of treating paper with the water / oil resistant composition. Further, the composition has little odor.
[0038]By the process for producing a water / oil resistant composition of the present invention, it is possible to produce a water / oil resistant composition, whereby a sufficient water / oil resistance can be imparted to a base material even though a fluorinated copolymer having Rf group with at most 6 carbon atoms or perfluoropolyether is used, and the water / oil resistance is not substantially influenced by the pH of dilution water or the adjuvant used at the time of treating paper with the water / oil resistant composition, and further the odor is little.
[0039]The article of the present invention has a sufficient water / oil resistance with a low environmental load.
[0040]By the process for producing an article of the present invention, it is possible to produce an article having a sufficient water / oil resistance with a low environmental load.

Problems solved by technology

However, the water / oil resistant composition obtained by using acetic acid for conversion of amino groups to form a salt, has the following problems.
(i) The fluorinated copolymer having amino groups converted to form a salt is cationic, and therefore, if an anionic adjuvant is used at the time of treating paper, not only no adequate water / oil resistance can be obtainable, but also agglomerates are likely to be formed thus leading to a trouble in the operation.
Also in such a case, not only no adequate water / oil resistance can be obtainable, but also agglomerates are likely to be formed, thus leading to a trouble in the operation.
However, a substitute water / oil resistant composition obtained by converting amino groups with acetic acid to form a salt in a fluorinated copolymer having RF groups with at most 6 carbon atoms or perfluoropolyether, is inadequate in the water / oil resistance, as compared with a conventional water / oil resistant composition obtained by converting amino groups with acetic acid to form a salt in a fluorinated copolymer having RF groups with at least 8 carbon atoms.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0197]Into a 500 mL glass container, 30 g of oxidized starch and 270 g of water were charged. The solution was stirred at a stirring rotational speed of 100 rpm and heated from room temperature to 95° C. over a period of 20 minutes, and then, held for 30 minutes to obtain a semi-transparent aqueous dispersion. Then, the concentration of oxidized starch was adjusted to 10 mass % by ion-exchanged water to obtain an oxidized starch dispersion.

[0198]Into a 100 mL glass container to be hermetically sealed, 1.5 g of the water / oil resistant composition W, 30 g of the oxidized starch dispersion obtained as described above, 0.3 g of a nonionic penetrating agent (acetylene glycol type) and 68.2 g of ion-exchanged water at 60° C., were added and thoroughly mixed and then maintained in a 60° C. water bath, and the mixture thereby obtained was used as a test solution.

[0199]Papers A, B and C having a size of 15 cm×25 cm were treated with the test solution by a size press method. Then, the papers ...

examples 5 to 15

[0200]Test solutions were prepared in the same manner as in Example 1 except that the water / oil resistant composition W was changed to water / oil resistant compositions 1 to 11, to obtain test papers. The results of oil resistance tests of the test papers are shown in Table 6.

examples 2 to 4 , 16 and 17

Examples 2 to 4, 16 and 17

[0201]Test solutions were prepared in the same manner as in Example 1 except that the water / oil resistant composition W was changed to the water / oil resistant compositions X to Z, 12 and 13, to obtain test papers. The results of oil resistance tests of the test papers are shown in Table 6.

TABLE 6SolidWater / oilcontent inOil resistance testresistantOrganicAdjuvant 1Adjuvant 2compositionWaterPaperPaperPaperPapercompositionPolymeracidTypeMass %TypeMass %Mass %Mass %ABCDEx.WAAcetic acidOxidized3Penetrating0.30.396.40.52.51.51starchagentEx.XBAcetic acidOxidized3Penetrating0.30.396.412starchagentEx.YDAcetic acidOxidized3Penetrating0.30.396.42.53starchagentEx.ZEAcetic acidOxidized3Penetrating0.30.396.41.54starchagentEx.1BMalic acidOxidized3Penetrating0.30.396.4335starchagentEx.2BMalic acidOxidized3Penetrating0.30.396.43.546starchagentEx.3BMalic acidOxidized3Penetrating0.30.396.4337starchagentEx.4BLactic acidOxidized3Penetrating0.30.396.434.58starchagentEx.5BMalic a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pKaaaaaaaaaaa
mass %aaaaaaaaaa
mass %aaaaaaaaaa
Login to View More

Abstract

To provide a water / oil resistant composition which can impart a sufficient water / oil resistance to a base material even though a fluorinated copolymer having an Rf group with at most 6 carbon atoms is used, said water / oil resistance being not substantially influenced by an adjuvant or the pH of dilution water, and which has little odor; an article treated therewith; and processes for their production. A water / oil resistant composition having a fluorinated copolymer dispersed or dissolved in a medium, wherein the fluorinated copolymer is one having one, some or all of amino groups in a fluorinated copolymer comprising structural units based on a monomer (a) having a C1-6 Rf group and structural units based on a monomer (b) having an amino group, converted to form a salt with an organic acid comprising an organic acid having a pKa of from 2.0 to 4.0.

Description

TECHNICAL FIELD[0001]The present invention relates to a water / oil resistant composition, an article treated therewith, and processes for their production.BACKGROUND ART[0002]Water / oil resistant paper (hereinafter referred to as fluorinated water / oil resistant paper) obtained by treating paper with a water / oil resistant composition containing a fluorinated copolymer having perfluoroalkyl groups (hereinafter referred to as RF groups), has a barrier property against a liquid such as water or oil and thus is used as e.g. wrapping paper for food products or a packaging container for food products. Further, fluorinated water / oil resistant paper has good water resistance and oil resistance while maintaining air permeability, as different from water / oil resistant paper other than the fluorinated type, and thus, it is used also as wrapping paper for fried products which disfavor moisture remaining inside, as wrapping paper for a freshness-keeping agent which requires air permeability for its...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): C09D133/14B32B27/10
CPCC09K3/18D21H17/34D21H19/20C08F222/1006C08F220/20C08F220/24C08F220/36D21H21/16Y10T428/3154C08F222/103
Inventor KAWANA, JUNSUKESUGIMOTO, SHUICHIRO
Owner ASAHI GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com