Antibacterial mite-resistant cellulose viscose and its making method

A viscose fiber and manufacturing method technology, applied in the field of viscose fiber, can solve problems such as single function, single fiber component, and insufficient additional functions and value, so as to increase technical content, excellent washability, and enhance product added value. value effect

Inactive Publication Date: 2007-07-11
YIBIN GRACE
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current problems are: the existing production of fiber has single composition, single function, and the additional function and value have not been maximized. In recent years, with the improvement of people's living standards and the continuous enhancement of health and environmental protection awareness, single product varieties It can no longer meet the needs of the market and enterprise development. The technical content and special functions of viscose fiber need to be increased urgently, and the added value of products needs to be improved. It has become the general trend to vigorously promote the development of healthy, environmentally friendly products and green fibers. The diversification of products and the diversification of the market has become necessary

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial mite-resistant cellulose viscose and its making method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Antibacterial and anti-mite viscose fiber, the antibacterial and anti-mite viscose fiber refers to the antibacterial and anti-mite solution mixed with the viscose solution at a ratio of 0.1% and then spun, the number of monofilaments obtained is 30, and the deviation of the number of monofilaments is 0% , the residual sulfur content is 6.3mg / 100g, the oil content is 0.4%, the dyeing uniformity is 3.5, and the anti-mite rate reaches 99.6%. Antibacterial and anti-mite viscose fiber products. The antibacterial and antimite solution is a solution formed by dispersing an antibacterial and antimite agent in deionized water. The antibacterial and anti-mite powder is a mixture of quaternary ammonium salt compound and specific pyrethrum extract. Contains quaternary ammonium salt benzalkonium bromide, benzalkonium chloride 20%, pyrethrin I, II 5%.

[0035] The manufacture method of antibacterial and anti-mite viscose fiber is realized according to the following steps:

[0036] ...

Embodiment 2

[0053] Antibacterial and anti-mite viscose fiber, the antibacterial and anti-mite viscose fiber refers to mixing the anti-bacterial and anti-mite solution to the viscose solution in a ratio of 2% before spinning, and the number of monofilaments obtained is 30, and the deviation of the number of monofilaments is 0%. , the residual sulfur content is 6.3mg / 100g, the oil content is 0.4%, the dyeing uniformity is 3.5, and the anti-mite rate reaches 99.6%. Antibacterial and anti-mite viscose fiber products. The antibacterial and antimite solution is a solution formed by dispersing an antibacterial and antimite agent in deionized water. The antibacterial and anti-mite powder is a mixture of quaternary ammonium salt compound and specific pyrethrum extract. Contains quaternary ammonium salt benzalkonium bromide, benzalkonium chloride 20%, pyrethrin I, II 5%.

[0054] The manufacture method of antibacterial and anti-mite viscose fiber is realized according to the following steps:

[0...

Embodiment 3

[0072] Antibacterial and anti-mite viscose fiber. The antibacterial and anti-mite viscose fiber refers to mixing the antibacterial and anti-mite solution with the viscose solution at a ratio of 1% before spinning. The number of monofilaments obtained is 30, and the deviation of the number of monofilaments is 0%. , the residual sulfur content is 6.3mg / 100g, the oil content is 0.4%, the dyeing uniformity is 3.5, and the anti-mite rate reaches 99.6%. Antibacterial and anti-mite viscose fiber products. The antibacterial and antimite solution is a solution formed by dispersing an antibacterial and antimite agent in deionized water. The antibacterial and anti-mite powder is a mixture of quaternary ammonium salt compound and specific pyrethrum extract. Contains quaternary ammonium salt benzalkonium bromide, benzalkonium chloride 20%, pyrethrin I, II 5%.

[0073] The manufacture method of antibacterial and anti-mite viscose fiber is realized according to the following steps:

[0074...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial anti-mite viscose fiber and the manufacturing method. The fiber is characterized in that after antibacterial anti-mite solution is mixed with the viscose solution with the proportion of 0.1-2%, the spinning is run; and antibacterial anti-mite viscose fiber product with 30 of the number of monofilament, 0% of the deviation of the number of monofilament, 6. 3mg / 100g of residue, 0.4% of oil percentage, 3. 5 grade of dyeing evenness, and 99. 6% of anti-mite ratio is obtained. The manufacturing method comprises preparing antibacterial anti-mite mother solution, preparing antibacterial anti-mite matching solution, rubbing and filtering the antibacterial anti-mite matching solution, mixing with the viscose, and filtering. The invention is benefit for human health and can improve the performance and added value of viscose fiber effectively. It is favor of environmental protection.

Description

technical field [0001] The invention relates to a viscose fiber used in the fields of clothing, furniture, medical treatment and the like and a method for manufacturing the viscose fiber, and mainly relates to an antibacterial and anti-mite viscose fiber and a method for manufacturing the same. Background technique [0002] With the development of the national economy and the improvement of people's living standards, people's requirements for quality of life are also constantly improving. Health and environmental protection have become the two major fashions pursued by modern people today. Various functional fibers and textiles are more and more popular among people. The favor of the application field is gradually expanding. In daily life, mites belong to the phylum Arthropoda and are small in size, generally about 0.1-0.5 mm in size, so they cannot be seen with the naked eye. It is ubiquitous in the home environment, such as parasitizing on bedding, carpets, cushions, clot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08D01F1/10D01D5/00
Inventor 王义尹继国袁道军余兰英陈晓芳刘萌萌
Owner YIBIN GRACE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com