No-coating air bag fabric and its making process

A technology for airbag fabric and preparation process, applied to fabrics, manufacturing tools, fabric surface trimming, etc., can solve the problems of cumbersome production and processing process, large investment in production equipment, high cost, etc., and achieves easy industrialized large-scale production, simplified The effect of low processing cost and weaving cost

Inactive Publication Date: 2007-06-27
吴江祥盛纺织染整有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The non-coated airbag fabric of high-density and high-strength nylon fabric has reliable safety performance, high success rate of one-time production, and stable product quality. It is the leading product of automotive airbag fabrics at present and for a l

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1 selects nylon industrial filament to carry out following test, selects the nylon fiber raw material that meets the requirements: measure the linear density range of nylon fiber with a balance and a skein length measuring machine to be 420D ± 2.5%, measure its fracture with an electronic monofilament strength machine The strength should be between 6.5-9.5CN / dtex, and the elongation at break should be 16-29.7%. The shrinkage in boiling water should be between 6.0-8.5% when measured by a pressure cooker and a steel ruler.

[0024] The selected nylon long fibers are warped by batch warping machines. The number of warping threads is 1050. The warp shaft hardness of the warping machine is 70°~75°. It is 150±10m / min.

[0025] The nylon fiber filament after warping is sizing with KSH400 sizing machine. The hardness of the sizing shaft of the sizing machine is 70°~75°, the sizing temperature is 130~140°C, and the sizing rate is 5~6%. The speed is 100m / min, and the ...

Embodiment 2

[0032] Embodiment 2 Select nylon industrial filaments to carry out the following tests, select nylon fiber raw materials that meet the requirements: measure the linear density range of nylon fibers with a balance and a skein length measuring machine to be 420D ± 2.5%, measure its fracture with an electronic monofilament strength machine The strength should be between 6.5-9.5CN / dtex, and the elongation at break should be 16-29.7%. The shrinkage in boiling water should be between 6.0-8.5% when measured by a pressure cooker and a steel ruler.

[0033] Use batch warping machine to warp the selected nylon long fibers. The number of warping threads is 1050. The warp shaft hardness of the warping machine is 75°~80°. It is 150±10m / min.

[0034]After warping, the nylon fiber filaments are oiled. The fabric oil is a commercially available synthetic aqueous lubricating oil. The oiling temperature is 130-140°C, the oiling rate is 4-5%, and the paddle car speed is 100m / min. , The crimp te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to View More

Abstract

The no-coating air bag fabric is tabby warp fabric of nylon yarn material, and has warp density of 18.5-19.5 /cm and weft density of 19-20 /cm. It is woven through the following steps: warping nylon yarn in a warping machine, sizing, rebeaming and tabby warp gaiting, weaving in a jet loom, desizing, and high temperature settling to obtain the no-coating air bag fabric. The process has low cost and is suitable for batch production.

Description

technical field [0001] The invention belongs to a safety airbag fabric for automobiles, in particular to a high-density, high-strength non-coated nylon filament non-coated airbag fabric and a preparation process thereof. Background technique [0002] Airbag fabric is the raw material for manufacturing automobile airbags. Its production technology has gone through several stages of development. The first generation is a sewn-type coated airbag fabric. The surface of the fabric is coated with neoprene, which has achieved the gas barrier effect; the second It is replaced by a sewn airbag fabric coated with silicone; the above-mentioned two generations of fabric mainly control the air permeability of the fabric through the coating. The third generation is sewn-type non-coated airbag fabric, which has gas barrier properties due to the structure of the fabric itself, and the fourth generation is non-coated fully formed airbag fabric, which is directly processed into a bag on the l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D03D13/00D03D1/02D03D47/32D02H3/00D01F6/60D06C7/02D06M15/11D06L1/06D06L1/14D03D15/283D03D15/50
Inventor 申素琴段亚峰盛秋华
Owner 吴江祥盛纺织染整有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products