Synthetic method for crosslinking agent-pentaerythritol allyl ether for high molecular polymerization

A technology of pentaerythritol allyl ether and polymer polymerization, applied in ether preparation, organic chemistry and other directions, can solve the problems of poor selectivity, low polyol ether yield, dark product color, etc., to improve the reaction selectivity and yield Effect

Active Publication Date: 2007-04-11
NANJING WELL CHEM
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The above synthesis method is because the alkalinity in the reaction system is too strong, so the yield of the polyol ether of the halogenated olefin obtained by synthesis is low, the product color is deep, the by-product is many, the selectivity is poor, and the allyl group suitable for polymerization cannot be obtained. Polyol Ether

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic method for crosslinking agent-pentaerythritol allyl ether for high molecular polymerization
  • Synthetic method for crosslinking agent-pentaerythritol allyl ether for high molecular polymerization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1: Add 800g of pentaerythritol, 700g of sodium hydroxide, 1353g of allyl chloride, 450g of PEG800, and 700g of distilled water into a 5L, 316L stainless steel reaction kettle, pressurize to 0.2MPa with nitrogen, check the airtightness, heat and start stirring , stirring and reacting at a temperature of 60-120°C for 8-10 hours, sampling and analyzing the materials in the kettle, after the etherification reaction is completed, the materials are discharged while they are hot, the reaction mixture is separated from sodium chloride by centrifugation, and the filtrate is poured into the separatory tank , and add an equal volume of tap water, and add metered 20% hydrochloric acid aqueous solution to neutralize, the pH value is about 7, then static layering, the lower water layer is separated, the upper oil phase is returned to the reactor, and at a vacuum of 20mmHg, Dehydration under reduced pressure at a temperature of 100°C to 120°C to remove trace by-products of ally...

Embodiment 2

[0023] In reactor, add 800g pentaerythritol, 982g potassium hydroxide, 1353g allyl chloride, 450gPEG800, 982g distilled water, the condition and operation of synthetic pentaerythritol allyl ether are the same as embodiment 1, filter to obtain refining pentaerythritol allyl ether mixture 1100g, The yield is 81.3% (based on the amount of allyl chloride charged), and its mass composition is 10% pentaerythritol allyl disubstituted; trisubstituted 72%; tetrasubstituted 18% through gas chromatographic analysis.

Embodiment 3

[0025] Add 800g pentaerythritol, 700g sodium hydroxide, 1353g allyl chloride, 200g tetrabutylammonium bromide, 700g distilled water in the reaction kettle, the condition and operation of synthetic pentaerythritol allyl ether are the same as embodiment 1, filter to obtain refined pentaerythritol propane Allyl ether mixture 1070g, yield is 79.1% (in terms of allyl chloride charging amount), through gas chromatography analysis and identification, its mass composition is pentaerythritol allyl ether disubstituted 7%; Three substituted 70%; Four substituted twenty three%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The process of synthesizing pentaerythritol allyl ether as cross-linking agent for polymerization includes the following steps: mixing allyl chloride, alkali catalyst and pentaerythritol in the molar ratio of 3.0-5.5 to 3.0-5.5 to 1.0; etherification reaction at 60-80 deg.c for 8-10 hr under the action of phase transfer catalyst; neutralizing, water washing, desalting and filtering, degassing and refining. The phase transfer catalyst is one of ammonium tetrabutyl bromide and PEG200-PEG1000; and the alkali catalyst is sodium or potassium hydroxide in the concentration preferably of 30 %-50 %. The synthesis process has effectively raised reaction selectivity and produce yield, and the yield may reach 88 % accounting in allyl chloride.

Description

technical field [0001] The invention belongs to the technical field of halogenated olefin etherification of polyols, and relates to a synthesis method of pentaerythritol allyl ether, a crosslinking agent for polymer polymerization. Background technique [0002] Polyol allyl ether is a cross-linking agent widely used in polymer polymerization, and is widely used in the fields of pharmaceutical polymers, cosmetic polymers and emulsion polymers. At present, the synthetic methods for preparing such crosslinking agents are limited to the traditional Williamson (Cheng Liamson) method of halogenated olefins, and this method has attracted the attention of many researchers. Known Williamson (Williamson) method discloses in Japanese Patent Publication No. 48-22198, No. 54-32598, U.S. Patent No. 3312460 and German Patent No. 1021346, using sodium methylate, sodium metal, sodium hydroxide or hydroxide Aqueous or alcoholic solutions of potassium are used as alkali metallating reagents. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K5/06C07C43/178C07C41/01
Inventor 严军表余清彭文勇周霞娟
Owner NANJING WELL CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com