Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Application of detoxic chromium dregs as cement admixture

A technology of cement clinker and cement, applied in the direction of cement production, etc., to achieve the effects of stable stability, good color and high strength value increase rate

Active Publication Date: 2006-06-28
SICHUAN YINHE CHEM
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And will not produce secondary pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] a. Add 3kg of detoxified chromium slag, 1.3kg of natural dihydrate gypsum, and 95.7kg of cement clinker into a cement mill to grind finely to obtain finished cement.

[0025] b. The physical and chemical results of the finished product: the stability is qualified, the initial setting time is 147min, the final setting time is 198min, the flexural strength is 5.8MPa / 3d, 8.6Mpa / 28d, the compressive strength is 27.6Mpa / 3d, 53.5Mpa / 28d, water-soluble hexavalent Chromium is zero.

Embodiment 2

[0027] a. Add 5kg of detoxified chromium slag, 1.3kg of natural dihydrate gypsum, and 93.7kg of cement clinker into a cement mill to grind finely to obtain finished cement.

[0028] b. The physical and chemical results of the finished product: the stability is qualified, the initial setting time is 161min, the final setting time is 205min, the flexural strength is 6.1MPa / 3d, 8.5Mpa / 28d, the compressive strength is 28.4Mpa / 3d, 52.5Mpa / 28d, water-soluble hexavalent Chromium is zero.

Embodiment 3

[0030] a. Add 9kg of detoxified chromium slag and 91kg of cement clinker into a cement mill and grind to obtain finished cement.

[0031] b. The physical and chemical results of the finished product: the stability is qualified, the initial setting time is 175min, the final setting time is 231min, the flexural strength is 6.1MPa / 3d, 8.6Mpa / 28d, the compressive strength is 29.0Mpa / 3d, 50.6Mpa / 28d, water-soluble hexavalent Chromium is zero.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Initial setting timeaaaaaaaaaa
Final setting timeaaaaaaaaaa
Initial setting timeaaaaaaaaaa
Login to View More

Abstract

An application of detoxicated Cr slags in preparing early-strenthening low-alkali cement and its products is disclosed. Said cement is prepared through proportionally mixing said detoxicated Cr slags with clinker and natural bihydrated gypsum. Its advantages are high quality of cement and no secondary pollution.

Description

Technical field: [0001] The invention relates to the use of detoxified chromium slag as admixture material to produce cement. The invention also relates to a method for producing cement by using detoxified chromium slag as admixture material and its products. Background technique: [0002] Most of today's cement production uses natural dihydrate gypsum as a retarder to relieve the rapid setting of cement, increase the strength of cement (especially the early strength), reduce the drying shrinkage of cement products in the air by 30-50%, and improve the cement's durability. Freeze resistance, chemical resistance and stability. [0003] Chromium slag is a chemical solid waste produced during the production of chromium salts. At present, the actual annual output of chromium salts has exceeded 160,000 tons. According to the calculation of slag discharge coefficient and chromium slag output, the annual discharge of chromium slag in my country is 350,000-420,000 tons, and 2.5 mi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B22/08C04B7/14C04B7/36C04B103/22
CPCY02P40/10
Inventor 李先荣张国庆马顺友王亭刚胡义华
Owner SICHUAN YINHE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com