Process for preparing slag by pelletization of steel-making dust slime

A manufacturing process and dust sludge technology, applied in the field of comprehensive utilization of steel-making dust sludge, can solve the problems of difficult to guarantee thermal strength, large site maintenance, high cost of binder, reduce bursting phenomenon, ensure strength, and reduce cracking and the effect of the fault

Inactive Publication Date: 2005-09-07
张清学
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally speaking, the wheel kiln sintering method needs to be equipped with uniformly heated high-temperature equipment and extrusion equipment. Its disadvantages are large investment and high energy consumption. The sintered product needs to be broken into a certain particle size before it can be used in steelmaking; The group method is to dry the steelmaking dust to a certain extent, add various binders, press the balls, and then carry out natural stacking and maintenance to obtain a certain strength. The disadvantage of this process is that it requires a large space And long-term maintenance, the cost of the binder used is relatively high, and the obtained pellet strength, especially the hot strength, is difficult to guarantee

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing slag by pelletization of steel-making dust slime

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0024] A batch of raw materials of steelmaking dust and mud after natural air drying is mixed with 5% quicklime and 0.7% binder to make a primary mixture; the primary mixture is mixed with the returned material for the second time, and 4 tons of secondary mixture are taken It is sent to the spiral mixer by belt conveyor for stirring for 5 minutes, and then sent to the wheel mill by belt conveyor for wheel milling. After 10 minutes of wheel milling, it is sent to the double-roller pelletizing machine for pelletizing by belt conveyor; when pelletizing, mix The moisture content of the material is controlled at 10%, and the pressure is controlled at 50KN; the green pellets produced are passed through a vibrating screen, and the green pellets on the screen are loaded into the hopper through the feeding system and sent to the shaft furnace for consolidation, and the crushed material under the screen is returned to the mixer as return material Reuse: After the raw pellets are put into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a comprehensive utilization method of dust and mud in steelmaking process, which is specifically a spheroiditic slagging agent production process. The invention comprises the following steps: drying dust and mud in the open, adding 2-6% burnt lime and 0.5-1% adhensive to the mud to produce mixture, sending the mixture to agitator to intimate mixing, sending the mixture to roller to be pulverized fully, sending it to pelletizer to produce green-ball of phi20-phi30mm size by roll-type briquetting process in presure of 40-60KN, processing green-ball in jigging screen to get green-ball end product on sifter and sliver as return material under sifter and sending green-ball to tower furnace via charging system to be adglutinate and get end product.

Description

technical field [0001] The invention relates to a comprehensive utilization technology of steelmaking dust and mud, in particular to a manufacturing process of a steelmaking dust and mud pelletizing agent for steelmaking. Background technique [0002] At present, the comprehensive utilization technology of steelmaking dust is mainly to process steelmaking dust into steelmaking slag agent, which is returned to steelmaking production and application. The steelmaking process research and production application show that steelmaking dust is used as steelmaking slag agent. Slag agent, with cooling, slag, dephosphorization, desulfurization and other functions. In the existing technology of processing steelmaking dust into steelmaking slag agent, there are mainly wheel kiln sintering method and cold pressing pelletizing method. Generally speaking, the wheel kiln sintering method needs to be equipped with uniformly heated high-temperature equipment and extrusion equipment. Its disa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B30B9/28C21C5/36C21C7/076
CPCY02P10/20
Inventor 张清学吕心刚张怀宾孟永刚张道刚张仲波李子林赵振峰陈铁军王锐张玉林赵海修步云生毛尽华田晓霞马越
Owner 张清学
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com