Acrylate modified silicone oil and preparation method thereof

A technology of acrylate and allyl acrylate, which is applied in the field of acrylate-modified silicone oil and its preparation, can solve the problem of low product quality and yield of acrylate-modified silicone oil, difficulty in synthesizing acrylate-modified silicone oil, and preparation methods to be solved. Improvement and other problems, to achieve the effect of improving crosslinking phenomenon and self-polymerization phenomenon, promoting hydrosilylation reaction, and improving synthesis quality

Active Publication Date: 2022-03-22
杭州崇耀科技发展有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the catalyst used in the commonly used hydrosilylation reaction is a platinum catalyst, and the hydrosilylation reaction using a platinum catalyst is prone to crosslinking, resulting in self-polymerization, and the synthesis of acrylate-modified silicone oil is relatively difficult. , the quality and yield of the acrylate-modified silicone oil produced are relatively low
[0005] In view of the above-mentioned related technologies, the inventor believes that the current preparation method of acrylate-modified silicone oil produces poor product quality, and the preparation method still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylate modified silicone oil and preparation method thereof
  • Acrylate modified silicone oil and preparation method thereof
  • Acrylate modified silicone oil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The preparation method of the acrylic acid modified silicone oil provided by embodiment 1 may further comprise the steps:

[0051] S1: Stir allyl acrylate, rhodium catalyst and polymerization inhibitor in the preparation tank at a stirring speed of 200r / min for 1 hour according to the above ratio, and cool down to 8°C during the stirring process to obtain a mixed raw material;

[0052] S2: put hydrogen-containing silicone oil into the feeding tank, and stir at a stirring speed of 200r / min, and adjust the temperature to 15°C to obtain pretreated hydrogen-containing silicone oil;

[0053] S3: Add the pretreated hydrogen-containing silicone oil to the mixed raw materials, stir the mixed solution at a stirring speed of 100r / min, wait for the temperature to stabilize and then raise the temperature to 70°C, and continue the heat preservation reaction for 2h;

[0054] Step S1 and step S2 are in no particular order.

[0055] After the above steps, the acrylic modified silicone...

Embodiment 15

[0059] The difference from Example 13 is that when preparing the acrylic modified silicone oil, the temperature of the mixed raw material is controlled at 7°C, and the temperature of the hydrogen-containing silicone oil is 14°C.

Embodiment 16

[0061] The difference from Example 13 is that when preparing the acrylic modified silicone oil, the temperature of the mixed raw materials is controlled at 6°C, and the temperature of the hydrogen-containing silicone oil is 12°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of modified silicone oil, and particularly discloses acrylate modified silicone oil and a preparation method thereof. The acrylate modified silicone oil is characterized by being prepared from the following raw materials in parts by weight under the action of a catalyst: 100-120 parts of hydrogen-containing silicone oil, 150-200 parts of allyl acrylate, 2-5 parts of a polymerization inhibitor and 10-12 parts of a chain transfer agent, wherein the catalyst is a rhodium catalyst. The preparation method comprises the following steps: S1, uniformly mixing allyl acrylate, a rhodium catalyst and a polymerization inhibitor in proportion, and cooling to 5-8 DEG C to obtain a mixed raw material; s2, adjusting the temperature of the hydrogen-containing silicone oil to 10-15 DEG C to obtain pretreated hydrogen-containing silicone oil; s3, mixing the pretreated hydrogen-containing silicone oil and a mixed raw material for hydrosilylation reaction; the step S1 and the step S2 are not divided into a sequence. The method has the advantage that the product quality is improved.

Description

technical field [0001] The application relates to the technical field of UV resin additives, more specifically, it relates to an acrylate-modified silicone oil and a preparation method thereof. Background technique [0002] Acrylate-modified silicone oil, also known as silicone-modified acrylate, combines the advantages of silicone and acrylate, and has the advantages of cross-linking and non-migration. Adhesive and anti-scratch properties are improved. It can be used as an additive in UV light-curing system to help light-curing coatings improve special properties such as coolness, substrate wettability, anti-shrinkage, scratch resistance and leveling, and plays a very important role in the coatings industry. status. [0003] At present, the common acrylate-modified silicone oil is mainly prepared by reacting hydrogen-containing silicone oil and acrylate under the action of a catalyst by the method of hydrosilylation. [0004] However, the catalyst used in the commonly us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/38C08G77/08C08G77/10C08G77/34
CPCC08G77/38Y02P20/584
Inventor 汪瑜华童涛叶富杨雪忠宋新锋张霄胡庆
Owner 杭州崇耀科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com