Modified polypropylene material as well as preparation method and application thereof

A polypropylene material and polypropylene technology, applied in the field of modified polypropylene material and its preparation, can solve the problems of light waste, reduce the light source utilization rate of lamps, and light leakage of lamp shells, so as to improve the gloss and improve the light source utilization of lamps rate, the effect of fine crystal size

Pending Publication Date: 2022-01-21
安庆会通新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Polypropylene (PP) has excellent physical properties such as light specific gravity, low price, good mechanical properties and easy processing, as well as solvent resistance and high temperature resistance. It is the fastest growing material among general plastics and is widely used in automobiles. In decorative parts and small household appliances, due to its own material, the light shell of the existing lighting lamp has strong light transmittance, and the light transmission of the light bulb causes light leakage from the light shell, resulting in waste of light and reducing the utilization of the light source of the light source. rate, for this reason, the present invention proposes a kind of modified polypropylene material and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified polypropylene material as well as preparation method and application thereof
  • Modified polypropylene material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Raw material components and components: high crystalline polypropylene 66g, titanium white powder 15g, compativity 4g, nano-grade sulfate 15g, lubricant (calcium hard esteric) 0.2g, lubricant (polyethylene wax) 0.3g Antioxidant (four [β- (3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol ester) 0.3 g, silane coupling agent (vinyl triethoxysilane) 0.15 g.

[0037] The specific preparation method includes the following steps:

[0038] (1) Take 15 g of dry nanoscale barium sulfate, stirring with a liquid solution of a 1.0.15 g of a silane coupling agent for 30 min, here, the mass concentration of ethanol in ethanol solution is 10%, volume is 5 ml, room temperature was allowed to stand for 12 h, vacuum filtration, placed in an electric heated hemond dry box at 80 ° C to constant weight, and the surface treated nano sulfate is prepared;

[0039] (2) Take 66 g of high-crystalline polypropylene, (1), nano-stage sulfate, 4G compatibilizer, 15g titanium white powder...

Embodiment 2

[0042] Raw material components and components: high crystalline polypropylene 55g, titanium powder 5g, compatible agent 3g, nano-stage sulfate 15g, lubricant (calcium hard esteric acid) 0.2g, lubricant (polyethylene wax) 0.3g Antioxidant (four [β- (3,5-di-tert-butyl-4-hydroxyphenyl) 0.2 g, silane coupling agent (vinyl triethoxysilane) 0.1 g.

[0043] The specific preparation method includes the following steps:

[0044] (1) According to the ratio, 15 g of dry nano-stage sulfate, the ethanol solution of 0.1 g of the silane coupling agent is stirred at a low speed of 30 min, here, the mass concentration of ethanol in ethanol solution is 10%, volume is 5 ml, room temperature was allowed to stand for 12 h, vacuum filtration, placed in an electric heated hemond dry box at 80 ° C to constant weight, and the surface treated nano sulfate is prepared;

[0045](2) Take 77 g of high-crystalline polypropylene, nano-grade sulfate, 3G compatible agent, 5 g of titanium white powder, 0.2 g of ant...

Embodiment 3

[0048] Raw material components and components content: high crystalline polypropylene 77g, titanium powder 15g, compativity 5g, nano-grade sulfate 30g, lubricant (calcium hard ester) 0.5 g, lubricant (polyethylene wax) 0.5g Antioxidant (four [β- (3,5-di-tert-butyl-4-hydroxyphenyl) 1 g, silane coupling agent (vinyl triethoxysilane) 0.3 g.

[0049] The specific preparation method includes the following steps:

[0050] (1) It is highly stirred by a 25 g of dry nano-stage sulfate, and the ethanol solution of 0.3 g of silane coupling agent is stirred at a low speed of 30 min, here, the mass concentration of ethanol in ethanol solution is 10%, volume is 5 ml, room temperature was allowed to stand for 12 h, vacuum filtration, placed in an electric heated hemond dry box at 80 ° C to constant weight, and the surface treated nano sulfate is prepared;

[0051] (2) Take 77 g of high-crystalline polypropylene, (1), nano-stage sulfate, 5g compatible agent, 15g titanium powder, 1 g of antioxidan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
crystallinityaaaaaaaaaa
degree of graftingaaaaaaaaaa
glossaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of modified materials, in particular to a modified polypropylene material as well as a preparation method and application thereof, and provides the following scheme: the modified polypropylene material is prepared by mixing barium sulfate treated by a silane coupling agent, high-crystalline polypropylene, a compatilizer, titanium dioxide, an antioxidant and a lubricant to obtain a mixed material; and melting the mixed material at the temperature of 205-220 DEG C, and putting the mixed material in an extruder for extrusion and granulation to prepare the modified polypropylene material, wherein the temperature of a machine barrel of the extruder is 205-220 DEG C, the rotating speed of a screw is 400-600 r/min, and the vacuum degree is -0.04 to 0.1 MPa. The modified polypropylene material prepared by taking high-crystalline polypropylene as a modified base material and adding titanium dioxide, barium sulfate, the lubricant and the antioxidant has high surface glossiness and low light transmittance, and can well reduce light leakage of a lamp source and improve the light source utilization rate of the lamp when being applied to the illumination lamp or a lamp shell. Therefore, the problem of low light source utilization rate of the illumination lamp is solved.

Description

Technical field [0001] The present invention relates to the field of modified materials, in particular a modified polypropylene material and a preparation method thereof. Background technique [0002] As the daily consumables, the lighting equipment industry has the emergence of new light sources such as my country's economic and social, fluorescent, energy-saving lamps, LEDs, so that lighting fixtures have evolved, and everything works toward more energy-saving, greenery and environmental protection. ; [0003] Polypropylene (PP) has excellent physical properties, low price, good mechanical performance and easy processing, etc. Differences and small household appliances, the existing lighting lamp housing is due to their own material, the light transmittance, the lighting transmission of the lamp, resulting in light leakage, resulting in light waste, reduced light source utilization In this respect, the present invention has proposed a modified polypropylene material and a prepa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08K9/06C08K3/30C08K5/1565C08K3/22
CPCC08L23/12C08K2003/3045C08K2003/2241C08L51/06C08K9/06C08K3/30C08K5/1565C08K3/22
Inventor 周玉成宋钰韩春春李荣群
Owner 安庆会通新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap