Acrylic and polyester fiber blended yarn and preparation method thereof

A polyester fiber and blended yarn technology, applied in the field of home textiles, can solve the problems of poor air permeability, poor comfort, strong stuffy feeling, etc., achieve good hygroscopicity and softness, improve hygroscopicity and softness, The effect of improving hygroscopicity

Pending Publication Date: 2021-12-10
LUOLAI LIFESTYLE TECH CO LTD +1
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above-mentioned shortcoming of prior art, the object of the present invention is to provide a kind of acrylic polyester fiber blended yarn and preparation method thereof, be used to solve the poor air permeability that acrylic polyester blended yarn is made in the prior art, have Strong stuffiness, poor comfort, and softness needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] The invention provides a kind of preparation method of acrylic polyester fiber blended yarn, comprising the following steps:

[0042] (1) Polyester modification treatment: add persulfate, N,N-dimethylformamide and acrylamide into water, stir well and prepare a solution, then put polyester fibers in the solution, and pass ultrasonication under nitrogen atmosphere grafting reaction, followed by washing and drying to obtain modified polyester;

[0043] Wherein, the fineness of acrylic fiber is 0.5-5dtex, preferably 0.5-1.2dtex; the fineness of polyester is 0.5-5dtex, preferably 0.5-1.2dtex;

[0044] The concentration of persulfate is 1-5g / L, preferably 1-2g / L; the concentration of N,N-dimethylformamide is 1-5g / L, preferably 1-2g / L; the concentration of acrylamide 0.8-1.5g / L, preferably 0.8-1.2g / L;

[0045] The mass ratio of acrylamide to polyester is 15:100-30:100, preferably 15:100-20:100;

[0046] The temperature of the grafting reaction is 85-115°C, preferably 90-115...

Embodiment 1

[0055] The present embodiment has prepared a kind of acrylic polyester fiber blended yarn, and concrete steps are as follows:

[0056] (1) Polyester modified treatment: Dissolve sodium persulfate, acrylamide and sodium alkylsulfonate in water, stir to mix evenly, then add N,N-dimethylformamide to the solution and stir evenly to make The concentration of sodium persulfate in the solution is 2g / L, the concentration of N-dimethylformamide is 2g / L, the concentration of acrylamide is 1.2g / L, and the concentration of sodium alkyl sulfonate is 0.5g / L, to obtain Mix the solution and heat it to 85°C, then place the polyester fiber with a fineness of 0.5dtex in the mixed solution, in a nitrogen atmosphere, at 400W / cm 2 The grafting reaction was performed under ultrasonic intensity for 1.5 hours, followed by washing twice and drying at 110°C for 20 minutes to obtain modified polyester;

[0057] Among them, the mass ratio of acrylamide and polyester is 20:100;

[0058] (2) the modified ...

Embodiment 2

[0061] The present embodiment has prepared a kind of acrylic polyester fiber blended yarn, and concrete steps are as follows:

[0062] (1) Polyester modification treatment: Dissolve potassium persulfate, acrylamide and sodium dodecylsulfonate in water, stir to mix evenly, then add N,N-dimethylformamide to the solution and stir evenly , so that the concentration of potassium persulfate in the solution is 5g / L, the concentration of N-dimethylformamide is 1g / L, the concentration of acrylamide is 1.5g / L, and the concentration of sodium dodecylsulfonate is 0.3g / L to obtain a mixed solution and heat it to 110°C, then place the polyester fiber with a fineness of 1.2dtex in the mixed solution, in a nitrogen atmosphere, at 200W / cm 2 Grafting reaction under ultrasonic intensity for 0.5h, followed by washing twice and drying at 120°C for 25min to obtain modified polyester;

[0063] Among them, the mass ratio of acrylamide and polyester is 15:100;

[0064] (2) The modified polyester ob...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Concentrationaaaaaaaaaa
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of household textiles, in particular to a preparation method of an acrylic and polyester fiber blended yarn. The method comprises the following steps of (1) performing polyester modification treatment: adding persulfate, N,N-dimethylformamide and acrylamide into water, uniformly stirring to prepare a solution, then putting polyester fibers into the solution, carrying out a grafting reaction under the ultrasonic action in a nitrogen atmosphere, and then carrying out washing and drying to obtain modified polyester; and (2) mixing the modified polyester obtained in the step (1) with acrylic fibers, and spinning a mixture into the blended yarn through open-end spinning. Hydrophilic groups are grafted to the polyester fibers through the grafting reaction, so that the hygroscopicity of polyester is improved; and the modified polyester and the acrylic fibers are blended to prepare the yarn, so that the hygroscopicity and softness of the acrylic and polyester blended yarn can be further improved. A textile prepared from the blended yarn is good in hygroscopicity and softness.

Description

technical field [0001] The invention relates to the technical field of household textiles, in particular to an acrylic polyester fiber blended yarn and a preparation method thereof. Background technique [0002] Acrylic fiber, also known as polyacrylonitrile fiber, is a synthetic fiber processed from polyacrylonitrile as the main monomer (the monomer content accounts for more than 85%), and its main repeating unit is -CH 2 CH(CN)-. [0003] The appearance, feel, elasticity and warmth of acrylic fiber are similar to that of wool. In addition, acrylic fiber is brightly dyed, light-resistant, heat-resistant, acid-resistant, oxidant-resistant, organic solvent-resistant, mildew-proof, moth-proof, aging-resistant, easy to wash and dry , and light weight (second only to polypropylene), it is an important raw material for sweaters, warm clothing and other fabrics. [0004] However, the wear resistance of acrylic fiber is not good, which is the worst wear resistance among synthetic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/04D02G3/44D06M14/14
CPCD02G3/045D02G3/442D02G3/449D06M14/14D10B2331/04D10B2321/10D06M2200/50
Inventor 宫怀瑞徐良平何留根张红艳张磊
Owner LUOLAI LIFESTYLE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap