Degradable high-heat-resistance jelly glue and preparation method thereof

A jelly glue, high heat-resistant technology, applied in the preparation of animal glue or gelatin, adhesives, adhesive types, etc., can solve problems such as general bonding strength, difficulty in meeting the packaging requirements of high-end paper products, and poor heat resistance , to achieve the effect of improving the initial adhesive force, improving the degradability, improving the bonding strength and heat resistance

Pending Publication Date: 2021-12-10
顶立新材料科技股份有限公司 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention is aimed at the research demand of the market for degradable materials, and the defects that jelly glue can only be applied to the packaging of low-end fast-moving consumer goods due to its general bonding strength and poor heat resistance, and it is difficult to meet the packaging requirements of high-end paper products. The invention provides a new type of degradable high heat-resistant jelly glue and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Degradable high-heat-resistance jelly glue and preparation method thereof
  • Degradable high-heat-resistance jelly glue and preparation method thereof
  • Degradable high-heat-resistance jelly glue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The present invention provides a novel degradable high heat-resistant jelly glue, which is obtained by the following method:

[0019] Weigh 14 parts by weight of deionized water, add 24 parts by weight of industrial gelatin with a freezing strength of 180 Bloom g, add the deionized water and industrial gelatin into the kettle to dissolve and raise the temperature to 68-72°C for 1.5h-2h, and then dissolve it completely Add 0.1 parts by weight of Digo 800 mineral oil defoamer, 0.1 parts by weight of Rocima BTNV2 preservative and 0.1 parts by weight of sodium bisulfite, keep warm for 0.5h to 1h, then slowly add 10 parts by weight of magnesium sulfate heptahydrate, Keep warm for 0.5h to 1h, and slowly add 15 parts by weight of polylactic acid solution dropwise. The polylactic acid solution includes the following raw materials in units of weight: 50 parts of polylactic acid resin, 10 parts of 0.03mol / L sodium hydroxide solution, co-solvent 2 parts, 38 parts of deionized wate...

Embodiment 2

[0022] Weigh 20 parts by weight of deionized water, add 22 parts by weight of industrial gelatin with a freezing strength of 180 Bloom g, add the deionized water and industrial gelatin into the kettle to dissolve and heat up to 68-72°C for 1.5h-2h, and then dissolve them completely Add 0.1 parts by weight of Digo 800 mineral oil defoamer, 0.1 parts by weight of Rocima BTNV2 preservative, 0.05 parts by weight of sodium dithionite and 0.1 parts by weight of sodium bisulfite, keep warm for 0.5h to 1h, and then slowly add 10 Magnesium sulfate heptahydrate by weight, keep warm for 0.5h-1h, slowly add 19 parts by weight of polylactic acid solution dropwise, the polylactic acid solution includes the following raw materials in units of weight: 50 parts of polylactic acid resin, 0.03mol / L hydrogenated 10 parts of sodium solution, 2 parts of co-solvent, 38 parts of deionized water, the polylactic acid resin includes but not limited to SYNTERRA PLLA 2011, heat preservation for 1h to 2h, a...

Embodiment 3

[0025] Weigh 15 parts by weight of deionized water, add 25 parts by weight of industrial gelatin with a freezing strength of 180 Bloom g, add the deionized water and industrial gelatin into the kettle to dissolve and raise the temperature to 68-72°C for 1.5h-2h, and then dissolve it completely Add 0.2 parts by weight of Digo 800 mineral oil defoamer, 0.2 parts by weight of Rocima BTNV2 preservative, 0.1 parts by weight of sodium dithionite and 0.2 parts by weight of sodium bisulfite, keep warm for 0.5h to 1h, and then slowly add 8 Magnesium sulfate heptahydrate by weight, keep warm for 0.5h~1h, slowly add 25 parts by weight of polylactic acid solution dropwise, and the polylactic acid solution includes the following raw materials in units of weight: 50 parts of polylactic acid resin, 0.03mol / L hydroxide 10 parts of sodium solution, 2 parts of co-solvent, 38 parts of deionized water, the polylactic acid resin includes but not limited to SYNTERRA PLLA 2011, heat preservation for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses degradable high-heat-resistance jelly glue and a preparation method thereof, and the jelly glue comprises the following components in parts by weight: deionized water, industrial gelatin, glucose syrup, magnesium sulfate heptahydrate, a polylactic acid dissolving solution, sodium hydrosulfite, a defoaming agent, sodium hydrogen sulfite, a preservative and carrageenan. A main body of the jelly glue is made of biodegradable materials such as gelatin, sugar and polylactic acid, and the jelly glue is mainly used for packaging paper products, has better degradability, can be fully degraded by microorganisms in the environment after being used, and belongs to an environment-friendly adhesive. The jelly glue disclosed by the invention has excellent bonding strength and heat resistance, has relatively good bonding strength for a PP / PE plastic film with a low dyne value, and meanwhile, is relatively high in heat resistance.

Description

technical field [0001] The invention belongs to the technical field of glue, and in particular relates to a degradable high heat-resistant jelly glue and a preparation method thereof. Background technique [0002] In life and industry, all kinds of packaging are inseparable. Most of the packaging materials are made of paper products. The use of paper product packaging is very wide. The use of various paper product packaging pervades all aspects of human life and production. Paper packaging has a wide range of raw materials, low cost of ownership, light weight, and recyclable waste. It is widely used in daily chemicals, food, medicine, tobacco, health care products, gift boxes, and transportation. When paper products are discarded after use, their recycling has become the focus of research in recent years. [0003] With the improvement of requirements for packaging and printing products, there are more and more products with bright colors, strong three-dimensional effect, mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J189/00C09J167/04C09J11/08
CPCC09J189/00C09J11/08C08L2201/06C08L2201/08C08L67/04C08L5/00
Inventor 阮灿伟万江钟冬芸叶鹏金赵丽
Owner 顶立新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com