A kind of gh2132 alloy and preparation method thereof

A GH2132 and alloy technology, which is applied in the field of metal material preparation, can solve the problem that the yield strength of GH2132 alloy is difficult to be further improved, and achieve the effects of shortening the production cycle, improving the performance and strengthening the performance of the alloy.

Active Publication Date: 2022-02-11
INST OF RES OF IRON & STEEL JIANGSU PROVINCE
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the technical problem to be solved in the present invention is to overcome defects such as the difficulty in further improving the yield strength of the GH2132 alloy in the prior art, thereby providing a preparation method of the GH2132 alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of gh2132 alloy and preparation method thereof
  • A kind of gh2132 alloy and preparation method thereof
  • A kind of gh2132 alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] This embodiment provides a method for preparing a GH2132 alloy, which specifically includes the following steps,

[0055] Put the raw materials of GH2132 alloy at 1510°C for vacuum melting, and then cast them into ingots; then carry out electroslag remelting of the ingots, control the working current 8000A, voltage 60V, the slag used is CaF 2 -AlO-CaO-MgO, the remelted ingot is forged and billeted, and a 130mm×130mm square billet is obtained after air cooling; wherein, the initial forging temperature of forging billet is 1050°C, and the final forging temperature is 950°C.

[0056] Grind the surface of the billet clean to make it bright and smooth without any defects such as cracks visible to the naked eye, then heat to 1000°C, preheat for 100 minutes, then heat to 1210°C, soak at 1210°C for 140 minutes, and then control the initial rolling The temperature is 1090°C, and hot rolling is carried out for multiple passes until it is rolled into a Ф13 wire rod; the final roll...

Embodiment 2

[0060] This example provides a method for preparing a GH2132 alloy. The difference from Example 1 is that this example changes the holding time of the intermediate pretreatment from 30 minutes to 60 minutes, and the others are the same as Example 1.

[0061] Figure 4 is the SEM image of the alloy material after intermediate pretreatment, indicating that the alloy sample with γ' phase precipitation is obtained after intermediate pretreatment; Figure 5 It is the SEM picture of the alloy material after aging heat treatment, indicating that after aging heat treatment, a large number of γ' phases with a size of 20-30nm are precipitated in the alloy material.

Embodiment 3

[0063] This example provides a method for preparing a GH2132 alloy. The difference from Example 1 is that in this example, the temperature of the intermediate pretreatment is changed from 650°C to 600°C, and the others are the same as in Example 1.

[0064] Alloy samples with γ' phase precipitation were obtained after intermediate pretreatment, and a large amount of alloy materials with γ' phase precipitation were obtained after aging heat treatment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of metal material preparation, and in particular relates to a GH2132 alloy and a preparation method thereof. The steps of the preparation method at least include solution heat treatment, intermediate pretreatment and aging heat treatment; the temperature of the intermediate pretreatment is 600-650°C, and the time is 30-60min, and the grain size of the GH2132 alloy obtained by this method is 9-9- Grade 10, the grain size is uniform, the yield strength is at least 780MPa, and the tensile strength is at least 1090MPa. Compared with the prior art GH2132, the properties such as yield strength and tensile strength have been significantly improved, and the alloy also has better elongation Rate.

Description

technical field [0001] The invention belongs to the technical field of metal material preparation, and in particular relates to a GH2132 alloy and a preparation method thereof. Background technique [0002] GH2132 is a Fe-15Cr-25Ni-based high-temperature alloy, and on this basis, alloying elements such as Mo, Ti, Al, V and trace B are added for comprehensive strengthening. It belongs to precipitation hardening stainless steel. It still maintains good strength and oxidation resistance, and also has good machinability. Due to the many excellent properties of GH2132, this alloy is often used in structural materials in aerospace and other major fields. Such as various fasteners under high temperature and high load, common fasteners such as bolts need to bear tensile stress and bending stress at the same time when they work stably under stress relaxation conditions, and their materials should have high yield strength, plasticity and toughness , while the GH2132 alloy can meet i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D6/00C22C38/02C22C38/04C22C38/06C22C38/42C22C38/46C22C38/44C22C38/50C22C38/54C22C38/60
CPCC21D6/004C21D6/005C21D6/008C22C38/02C22C38/04C22C38/06C22C38/42C22C38/46C22C38/44C22C38/50C22C38/54C22C38/60C22C38/007C22C38/002
Inventor 胡显军许满伟廖岳太成建强刘建民方峰
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com