Preparation method of ultraviolet full-barrier TPU automobile paint surface protective film

A UV and protective film technology, applied in the direction of film/sheet adhesive, pressure-sensitive film/sheet, film/sheet release liner, etc. Barrier products and other problems, to avoid aging and fading, to prolong the service life

Inactive Publication Date: 2021-08-20
南通纳科达聚氨酯科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current market products have a certain function of blocking ultraviolet rays, but there is no fully blocking product
Due to the strong penetrating power of ultraviolet rays (200-400nm) and the wide range of peaks, it is difficult to achieve a product that completely blocks ultraviolet rays

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] A kind of preparation method of ultraviolet full barrier TPU car paint protection film, comprises the steps:

[0023] Step 1. Raw material processing: first weigh a certain weight of high-performance ultraviolet absorber and TPU particles of model 92A, and stir and mix;

[0024] Step 2. Production of TPU granules: use small-scale granulation equipment, use high-performance ultraviolet absorbers and TPU granules to mix and melt at 112°C, and then extrude to make functional TPU granules;

[0025] Step 3. Prepare TPU original film: use precision casting equipment to add functional TPU particles into the trough, and heat it through the extruder at a heating temperature of 117°C. After melting, extrude and cast the TPU original film ;

[0026] Step 4. Prepare the finished product: Use a precision coating production line to coat one side of the original TPU film with high-performance pressure-sensitive adhesive. The production temperature is 87°C, the speed is 11m / min, and t...

specific Embodiment 2

[0029] A kind of preparation method of ultraviolet full barrier TPU car paint protection film, comprises the steps:

[0030] Step 1. Raw material processing: first weigh a certain weight of high-performance ultraviolet absorber and TPU particles of model 92A, and stir and mix;

[0031] Step 2. Production of TPU granules: use small-scale granulation equipment, use high-performance ultraviolet absorbers and TPU granules to mix and melt at 188°C, and then extrude to make functional TPU granules;

[0032] Step 3. Prepare TPU original film: use precision casting equipment to add functional TPU particles into the trough, and heat through the extruder at a heating temperature of 183°C. After melting, extrude and cast to form TPU original film ;

[0033] Step 4. Prepare the finished product: Use a precision coating production line to coat one side of the original TPU film with high-performance pressure-sensitive adhesive. The production temperature is 133°C, the speed is 19m / min, and...

specific Embodiment 3

[0036] A kind of preparation method of ultraviolet full barrier TPU car paint protection film, comprises the steps:

[0037] Step 1. Raw material processing: first weigh a certain weight of high-performance ultraviolet absorber and TPU particles of model 92A, and stir and mix;

[0038] Step 2. Production of TPU granules: use small-scale granulation equipment, use high-performance ultraviolet absorbers and TPU granules to mix and melt at 162°C, and then extrude to make functional TPU granules;

[0039] Step 3. Prepare TPU original film: use precision casting equipment to add functional TPU particles into the trough, and heat it through the extruder at a heating temperature of 153°C. After melting, extrude and cast the original TPU film ;

[0040] Step 4. Prepare the finished product: Use a precision coating production line to coat one side of the original TPU film with high-performance pressure-sensitive adhesive. The production temperature is 120°C, the speed is 14m / min, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of an ultraviolet full-barrier TPU automobile paint surface protective film. The preparation method comprises the following steps: step 1, treating raw materials; step 2, manufacturing TPU particles; step 3, preparing an original TPU film; and 4, preparing a finished product. A product prepared in the invention has a function of blocking ultraviolet rays in a full wave band, and achieves a zero penetration effect. With the product, the aging of an automobile paint surface is well protected, so the paint surface always looks new. The product provided by the invention is a thermoplastic high-polymer transparent film for protecting the automobile paint surface from damage, is widely applied to automobile surface protection, and can be also applied to aviation equipment such as furniture, high-speed rails and airplanes and top-end luxury cruise ships of the world. The product is measured by a PE950S spectrophotometer, and a measurement result show that the ultraviolet blocking rate of the product is 100% and a total blocking effect is achieved. The product provided by the invention has the effect of comprehensively protecting the automobile paint surface, avoids the aging and fading of automobile paint, and prolongs the service life of original paint.

Description

technical field [0001] The invention belongs to the field of paint surface protection films, and in particular relates to a preparation method of an ultraviolet full-blocking TPU automobile paint surface protection film. Background technique [0002] The current market products have relatively basic functional product functions, such as protection of the appearance of car paint, anti-scratch performance; super anti-corrosion properties; excellent self-recovery properties; certain functions such as stain resistance and easy cleaning. [0003] The current production process in the market is as follows: 1. Using precision casting technology, the TPU particles are made into a TPU original film with uniform thickness and no defects on the surface through the extrusion casting process. 2. Using a coating production line, through precision coating technology, one side of the original TPU film is coated with high-performance pressure-sensitive adhesive and a composite release film; ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/25C09J7/38C09J7/40
CPCC09J2203/306C09J2475/006C09J7/25C09J7/38C09J7/40
Inventor 蔡志强肖琳
Owner 南通纳科达聚氨酯科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap