A technology of amino baking varnish and vacuum coating, which is applied in the field of paint materials, can solve problems such as poor adhesion, and achieve the effect of excellent adhesion and good construction tolerance
Inactive Publication Date: 2021-08-13
安徽六缘新材料科技有限公司
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The object of the present invention is to provide a kind of water-based amino baking varnish for vacuum coating, to solve the problem of poor adhesion
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] A water-based amino baking varnish for vacuum coating, comprising the following raw materials in mass percent: 40% water-soluble epoxy-modified acrylic resin, 15% crosslinking agent, 6% miscible transparent dye, hydrophilic alcohol ether Co-solvent 9%, defoamer 0.1%, leveling agent 0.1%, deionized water 29.8%.
[0017] The crosslinking agent is methyl etherified melamine resin.
[0018] The defoamer is polyether modified siloxane.
[0019] The leveling agent is polyacrylate.
[0020] The miscible transparent dye is Orisol 2B red.
Embodiment 2
[0022] A water-based amino baking varnish for vacuum coating, comprising the following raw materials in mass percentage: 50% water-soluble epoxy-modified acrylic resin, 9% crosslinking agent, 8% miscible transparent dye, hydrophilic alcohol ether Co-solvent 13%, defoamer 0.3%, leveling agent 0.2%, deionized water 19.5%.
[0023] The crosslinking agent is methyl etherified melamine resin.
[0024] The defoamer is polyether modified siloxane.
[0025] The leveling agent is polyacrylate.
[0026] The miscible transparent dye is Orisol 2B red.
Embodiment 3
[0028] A water-based amino baking varnish for vacuum coating, comprising the following raw materials in mass percent: 45% water-soluble epoxy-modified acrylic resin, 10% crosslinking agent, 8% miscible transparent dye, hydrophilic alcohol ether Co-solvent 16%, defoamer 0.5%, leveling agent 0.5%, deionized water 20%.
[0029] The crosslinking agent is methyl etherified melamine resin.
[0030] The defoamer is polyether modified siloxane.
[0031] The leveling agent is polyacrylate.
[0032] The miscible transparent dye is Orisol 2B red.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a water-based amino baking varnish for vacuum coating. The water-based amino baking varnish is prepared from, by mass, 40 to 50 percent of water-soluble epoxy modified acrylic resin, 9 to 15 percent of a cross-linking agent, 2 to 8 percent of a miscible transparent dye, 8 to 16 percent of a hydrophilic alcohol ether cosolvent, 0.1 to 0.5 percent of a defoaming agent, 0.1 to 0.5 percent of a leveling agent and 10 to 30 percent of deionized water. According to the water-based amino baking varnish for vacuum coating, the water-soluble epoxy modified acrylic resin is used as a main body, and the cross-linking agent, the hydrophilic cosolvent, the leveling agent, the defoaming agent, the miscible transparent dye and deionized water in a certain proportion are prepared as auxiliary film-forming materials. By adjusting the proportion and dosage of the auxiliary film-forming materials, the prepared water-based amino baking varnish for vacuum coating has excellent adhesive force, weather resistance, friction resistance and recoatability, and has good construction tolerance and water dilutability.
Description
technical field [0001] The invention relates to the technical field of paints, in particular to a water-based amino baking varnish for vacuum coating. Background technique [0002] Vacuum coating is a technology that produces thin film materials by physical methods. The atoms of the material in the vacuum chamber are separated from the heating source and hit the surface of the object to be plated. This technology was first used to produce optical lenses, such as nautical telescope lenses. Later extended to other functional films, disc aluminum, decorative coating and surface modification of materials, etc. [0003] A water-based amino baking varnish is often attached to the surface of the vacuum coating. The existing water-based amino baking varnish has problems such as poor friction resistance, long drying time, and poor adhesion. Contents of the invention [0004] The purpose of the present invention is to provide a water-based amino baking varnish for vacuum coating ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more