Flux-cored welding wire for downward vertically

A vertical downward and chemical feeding technology, applied in welding media, welding equipment, welding/cutting media/materials, etc., can solve the problems of vertical downward welding of thin plate corner joints, etc., and achieve easy control and forming of molten pools. Beautiful, high toughness effect

Inactive Publication Date: 2003-12-17
ADVANCED TECHNOLOGY & MATERIALS CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is not suitable for vertical downward welding of thin plate corner joints.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] According to the composition range of the flux core of the flux cored wire of the present invention, three batches of flux cored wires were produced, and the flux core composition is shown in Table 1. The seamed O-shaped Φ1.2mm flux-cored welding wire is made by the method of coiling the steel strip. Composition (weight %) of the steel strip: C 0.04%, Si 0.01%, Mn 0.30%, P 0.013%, S0.008. The powder filling rate is 16%.

[0020] Three batches of flux-cored wires were used for welding experiments, and Q235C steel plates were used to process them into 4×120×300mm test plates, and the surface was derusted. Adopt DC (one) polarity, 260A, 28V, welding speed 600mm / min, CO 2 , 201 / min, the rod is extended by 15mm, and the welding is carried out vertically and downward, and the welding process is observed. The results show that the weld is well formed, the slag is removed well, the welding process is stable and there is less spatter. Use the same welding specification to su...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A flux-corex welding wire fed downward vertically for gas shielded welding is composed of skin made of low-carbon steel and flux core containing TiO2 (20-40 wt%), Al2O3 (1.2-7), ZrO2 (3-8.5), MgO (0.5-3), NaF+K2SiF6 (1.2-4), deoxidizing agent which is one or more of Si, Mn, Ti, Al and Mg (11-20), alloying agent which is one or more of Ni, Cr, MO, Cu and V (less than 5) and Fe (rest).

Description

technical field [0001] The invention belongs to the field of welding materials, in particular to a gas-shielded welding type vertically feeding flux-cored welding wire. Background technique [0002] In prior art, TiO 2 Type gas-shielded flux-cored welding wire has been widely used. This type of welding wire has the advantages of excellent welding processability and high welding efficiency. It has been widely used in all-position welding of carbon steel and 490Mpa high-strength steel. All-position welding generally includes horizontal position, horizontal welding, vertical upward welding, and overhead welding, but does not include vertical downward welding. In the vertical welding, the vertical upward welding is generally welded by the small current swing method, which is easier to realize in terms of technology, but the welding speed is slower; while the vertical downward welding can be welded in a straight line with a larger current, the welding speed is slower. Fast, but...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/22B23K35/24
Inventor 王禄田潘川佟淑英梁东图何长红
Owner ADVANCED TECHNOLOGY & MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products