A method for stress relief annealing and homogenization annealing of 7000 series aluminum alloy ingot

A technology of aluminum alloy ingot casting and homogenization annealing is applied in the field of heat treatment of hard aluminum alloys, which can solve the problems of aggravating cracking risk, influence, and unsatisfactory resolubilization effect, and achieve the effect of reducing crack generation and improving treatment effect.

Active Publication Date: 2021-08-03
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, high alloying will lead to the formation of more coarse intermediate phases in the as-cast structure of the alloy. If the remelting effect is not ideal during the homogenization annealing process, it will have a bad influence on the subsequent thermal processing and other processes and aggravate cracking. risk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for stress relief annealing and homogenization annealing of 7000 series aluminum alloy ingot

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] The preparation method of the present invention will be further described in detail in conjunction with specific examples below. It should be understood that the following examples are only for illustrating and explaining the present invention, and should not be construed as limiting the protection scope of the present invention. All technologies realized based on the above contents of the present invention are covered within the scope of protection intended by the present invention.

[0063] The experimental methods used in the following examples and comparative examples are conventional methods unless otherwise specified; the reagents and materials used in the following examples can be obtained from commercial sources unless otherwise specified.

[0064] The aluminum alloy slab casting process used in the following examples and comparative examples illustratively includes the following steps: preparing the alloy, after the alloy is completely melted and the temperatur...

Embodiment 1

[0075]The 7050 aluminum alloy flat ingot with the size of 520mm×1620mm is transferred to the heat treatment furnace within 1 hour after casting. The initial temperature of the heat treatment furnace is 400°C, and the ingot is slowly cooled with the furnace at a rate of 50°C / h, and the temperature is lowered to 240°C. The last holding time is 16h; after the holding time is up, the temperature is raised directly for three-stage homogenization annealing treatment: once the temperature is raised to 420°C, the heating rate is 50°C / h, and the constant temperature holding time is 16h; the second time is raised to 465°C, and the heating rate is 50°C / h, holding time at constant temperature for 16 hours; heating up to 470°C three times, with a heating rate of 10°C / h, holding time at constant temperature for 60 hours; after the heat preservation time expires, turn off the power and cool slowly to 230°C with the furnace, then take out the furnace and air cool.

Embodiment 2

[0077] The 7010 aluminum alloy flat ingot with the size of 520mm×1620mm is transferred to the heat treatment furnace within 1 hour after casting. The initial temperature of the heat treatment furnace is 350°C. The last holding time is 12 hours; after the time is up, the temperature is raised directly for three-stage homogenization annealing treatment: once the temperature is raised to 390°C, the heating rate is 100°C / h, and the constant temperature holding time is 12h; the second time is raised to 460°C, and the heating rate is 100°C / h, holding time at constant temperature for 12 hours; heating up to 465~470°C three times, heating rate at 20°C / h, holding time at constant temperature for 48 hours; after the heat preservation time expires, turn off the power and cool slowly with the furnace to 200°C, then take out the furnace and air cool.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for stress relief annealing and homogenization annealing of a 7000 series aluminum alloy ingot. The melting and casting process adopts the smelting process of 7000 series aluminum alloy and the direct cooling semi-continuous casting process. After the casting is formed, the ingot is transferred to the heat treatment furnace for slow cooling treatment, and then the stress relief annealing treatment is carried out at a fixed temperature, and finally the temperature is directly raised for multi-level homogenization annealing treatment . This operation can not only reduce the high and low temperature switching times of heating and heat dissipation, reduce the risk of ingot cracking, save energy, shorten the annealing treatment cycle, but also combine the multi-level homogenization annealing process to force the alloy to dissolve the coarse intermediate phase, and significantly improve the homogenization of the ingot processing effect.

Description

technical field [0001] The invention belongs to the technical field of heat treatment of hard aluminum alloys, and relates to a method for stress-relief annealing and homogenization annealing of 7000 series aluminum alloy ingots, in particular to a direct-cooling semi-continuous method for large-scale, high-alloyed 7000-series aluminum alloys Continuous treatment method for stress relief annealing and homogenization annealing of flat cast ingots. Background technique [0002] The 7000 series aluminum alloy is a high-strength / ultra-high-strength heat-treatable aluminum alloy, which has the characteristics of high strength, excellent toughness, and good processability. It is one of the most widely used aluminum alloy materials in the aviation industry and is mainly used for the preparation of aircraft structural parts. . With the rapid development of the aviation field, low-cost overall manufacturing is the most important development direction at present, and higher requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/053
CPCC22F1/053
Inventor 戴圣龙何维维臧金鑫伊琳娜
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com