A technology of aluminum alloy materials and intermediate alloys, which is applied in the field of aluminum alloy materials and can solve the problems of poor comprehensive mechanical properties and high formula cost of cast aluminum alloys
Pending Publication Date: 2021-05-18
湖北华力科技有限公司
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The purpose of the present invention is to provide an aluminum alloy material for casting, which reasonably solve
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0022] The aluminum alloy material for casting in this embodiment is composed of the following substances in weight percentage: Si7.25%, Fe0.35%, Cu 3.2%, Mn 0.4%, Mg 0.35%, Zn 0.25%, Cr 0.02%, Ni 0.15%, Ti 0.16%, Pb 0.04%, Sr 0.008%, the balance is Al and unavoidable impurities. The aluminum alloy material for casting has a tensile strength of 223Mpa, a yield limit of 180Mpa, an elongation of 3.14 and a hardness of 91HBw.
Embodiment 2
[0024] The aluminum alloy material for casting in this embodiment is composed of the following substances in weight percentage: Si7.25%, Fe0.38%, Cu 3.55%, Mn 0.38%, Mg 0.35%, Zn 0.25%, Cr 0.02%, Ni0.15% , Ti 0.16%, Pb 0.05%, Sr 0.008%, the balance is Al and unavoidable impurities. The aluminum alloy material for casting has a tensile strength of 241Mpa, a yield limit of 182Mpa, an elongation of 3.02, and a hardness of 92HBw.
Embodiment 3
[0026] The aluminum alloy material for casting in this embodiment is composed of the following substances in weight percentage: 7.5% Si, 0.42% Fe, 3.3% Cu, 0.36% Mn, 0.38% Mg, 0.25% Zn, 0.02% Cr, 0.15% Ni, Ti 0.16%, Pb 0.06%, Sr 0.008%, the balance is Al and unavoidable impurities. The aluminum alloy material for casting has a tensile strength of 232Mpa, a yield limit of 175Mpa, an elongation of 3.15 and a hardness of 92HBw.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Tensile strength
aaaaa
aaaaa
Bow to extremes
aaaaa
aaaaa
Tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an aluminum alloy material for casting. The aluminum alloy material comprises the following compositions in percentage by mass: 7.2 percent to 7.8 percent of Si, less than or equal to 0.45 percent of Fe, 3.1 percent to 3.6 percent of Cu, 0.2 percent to 0.5 percent of Mn, 0.25 percent to 0.4 percent of Mg, 0.2 percent to 0.3 percent of Zn, less than or equal to 0.04 percent of Cr, 0.1 percent to 0.25 percent of Ni, 0.12 percent to 0.2 percent of Ti, 0.004 percent to 0.01 percent of Sr, less than or equal to 0.1 percent of Pb, and the balance of Al and inevitable impurities. By adopting the aluminum alloy material for casting disclosed by the invention, the problems of poor comprehensive mechanical properties and high formula costs of casting aluminum alloys in the prior art can be reasonably solved.
Description
technical field [0001] The invention relates to the technical field of aluminum alloy materials, in particular to an aluminum alloy material for casting. Background technique [0002] Casting is a method of smelting metal, making a mold, injecting molten metal into the mold, cooling and solidifying to obtain a metal part blank with a certain shape, size and performance. Most of the raw materials used in traditional casting castings are only a single metal, or several metals are melted and mixed, but the weight is heavy, the strength is average, and the mechanical properties are low, especially in high temperature, high pressure, and corrosive extreme environments for a long time. In the middle, the working life is short, and it is prone to deformation and even fracture. Chromium, titanium, tin, cadmium and other metals can improve the mechanical strength of aluminum alloys, making castings resistant to high temperature and corrosion. Among them, the compounds formed by tin ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more