Production method of high-barrier nylon PE co-extruded film

A production method and technology of co-extrusion film, applied in the direction of chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems that consumers cannot directly display the appearance of food, and the barrier performance cannot be satisfied.

Pending Publication Date: 2021-05-11
河源市合晶光电科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, films used in food packaging are required to have high oxygen barrier and water barrier properties. Usually, nylon or PET film is combined with PE or CPP film. PE or CPP mainly plays the role of water barrier, while for oxygen The barrier is mainly realized by nylon or PET film, so as to prevent food from oxidizing and moldy, and prolong the shelf life of food. However...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of high-barrier nylon PE co-extruded film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] as attached figure 1As shown, a production method of high-barrier nylon PE co-extrusion film, including inner film layer and outer film layer: inner film layer includes continuous bonded surface layer PE layer 1, PA layer 2, modified PE layer 3, middle PE layer The layer 4 and the surface layer PA layer 5 are composed of a symmetrical nylon film bonded sequentially and an asymmetric nylon film bonded sequentially; the outer film layer includes a printing layer, a barrier layer and a heat-sealing layer, and is distributed sequentially from the inside to the outside. The specific production method Proceed as follows:

[0032] Step 1: The symmetrical nylon membrane bonded in sequence is constructed by glue layer, BOPA layer, and symmetrical nylon membrane, and the symmetrical nylon membrane is co-extruded with PE layer, modified TO layer, PA layer 2, and modified PE3 layer arranged in sequence made;

[0033] Step 2: The asymmetric nylon membrane bonded in sequence is con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Transverse stretch temperatureaaaaaaaaaa
Thicknessaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of a high-barrier nylon PE co-extruded film, which comprises the steps that 1, a symmetric nylon film which is sequentially bonded is constructed by a glue layer, a BOPA layer and a symmetric nylon film, and the symmetric nylon film is formed by co-extruding a PE layer, a modified TO layer, a PA layer and a modified PE layer which are sequentially arranged; 2, the asymmetric nylon film which is bonded in sequence is constructed by a glue layer and a BOPA layer, and the asymmetric nylon film is formed by co-extruding a PE layer, a modified PE layer and a PA layer which are sequentially arranged; and 3, the raw materials of each layer are respectively addd into three extruders for melt processing, a three-layer co-extrusion structure is formed by means of co-extruding through a die head, cooling and molding are conducted to obtain a crude nylon film, the temperature is set at 210-300 DEG C in a molten state, the temperature of the die head is set at 210-300 DEG C, and the cooling and molding temperature is 22-50 DEG C. The product fully shows the excellent characteristics of quality guarantee, fresh keeping, long storage life, high temperature resistance, transparency and low temperature freezing resistance in use.

Description

technical field [0001] The invention relates to the technical field of co-extrusion film production, in particular to a production method of high-barrier nylon PE co-extrusion film. Background technique [0002] At present, films used in food packaging are required to have high oxygen barrier and water barrier properties. Usually, nylon or PET film is combined with PE or CPP film. PE or CPP mainly plays the role of water barrier, while for oxygen The barrier is mainly realized by nylon or PET film, so as to prevent food from oxidizing and moldy, and prolong the shelf life of food. However, the barrier performance of ordinary nylon or PET film to oxygen cannot meet the long-term shelf life of cooked food, seafood and pickled food. Storage requirements; In addition, plastic film is also used for food packaging with aluminization. Although the barrier property is good, due to the opaque aluminization film, it is impossible to directly show the appearance of food to consumers. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/32B32B27/34B32B27/30B32B27/08B32B27/06B32B37/15B29D7/01
CPCB32B27/32B32B27/327B32B27/34B32B27/306B32B27/08B32B37/153B29D7/01B32B2307/7244B32B2307/7246B32B2307/7248B32B2307/7242B32B2307/306B32B2307/54B32B2307/31B32B2307/558B32B2307/412B32B2439/70
Inventor 付立洲付南山
Owner 河源市合晶光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap