Flame-retardant non-woven fabric and preparation method thereof

A technology of flame retardant non-woven fabrics and non-woven fabrics, used in flame-retardant fibers, textiles and papermaking, fiber processing, etc. performance, the effect of stabilizing flame retardant performance

Active Publication Date: 2021-04-06
浙江雅宝无纺布制品有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the polypropylene raw materials used in non-woven fabrics currently on the market are hydrocarbon materials, which are more likely to cause combustion and cannot meet the needs of safety and fire prevention.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant non-woven fabric and preparation method thereof
  • Flame-retardant non-woven fabric and preparation method thereof
  • Flame-retardant non-woven fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The application discloses a flame-retardant non-woven fabric and a preparation method thereof. The non-woven fabric is treated with a flame-retardant treatment agent. The preparation method includes the following steps:

[0041] S1. Preparation of flame retardant finishing agent; first mix styrene-acrylic emulsion and zinc borate evenly, then add dimethyl methyl phosphate, stir for 5 minutes; continue to add sodium sulfamate and catalyst thionyl chloride, and heat up to After 50°C, add 5-methylisophthalaldehyde, stir the polymer obtained after 30 minutes of reaction, finally add deionized water, and stir at 30°C for 50 minutes to obtain a flame retardant finishing agent;

[0042] S2. Flame-retardant finishing of non-woven fabrics; soak the non-woven fabrics in the flame-retardant finishing agent obtained in S1 and let it stand for 15 minutes; arrange the soaked non-woven fabrics between the two rubber rollers of the roller press, squeeze The excess liquid was removed by...

Embodiment 2

[0045] The application discloses a flame-retardant non-woven fabric and a preparation method thereof. The non-woven fabric is treated with a flame-retardant treatment agent. The preparation method includes the following steps:

[0046] S1. Preparation of flame retardant finishing agent; first mix styrene-acrylic emulsion and zinc borate evenly, then add dimethyl methyl phosphate, stir for 8 minutes; continue to add sodium sulfamate and catalyst thionyl chloride, and heat up to After 55°C, add 5-methylisophthalaldehyde, stir the polymer obtained after 40 minutes of reaction, finally add deionized water, and stir at 40°C for 60 minutes to obtain a flame retardant finishing agent;

[0047] S2. Flame-retardant finishing of non-woven fabrics; soak the non-woven fabrics in the flame-retardant finishing agent obtained in S1 and let it stand for 20 minutes; arrange the soaked non-woven fabrics between the two rubber rollers of the roller press, squeeze The excess liquid was removed by...

Embodiment 3

[0050] The application discloses a flame-retardant non-woven fabric and a preparation method thereof. The non-woven fabric is treated with a flame-retardant treatment agent. The preparation method includes the following steps:

[0051] S1. Preparation of flame retardant finishing agent; first mix styrene-acrylic emulsion and zinc borate evenly, then add dimethyl methyl phosphate, stir for 7 minutes; continue to add sodium sulfamate and catalyst thionyl chloride, and heat up to After 52°C, add 5-methylisophthalaldehyde, stir and react for 35 minutes to obtain the polymer, finally add deionized water, and stir at 35°C for 55 minutes to obtain a flame retardant finishing agent;

[0052] S2. Flame-retardant finishing of non-woven fabrics; soak the non-woven fabrics in the flame-retardant finishing agent obtained in S1 and let it stand for 18 minutes; arrange the soaked non-woven fabrics between the two rubber rollers of the roller press, squeeze The excess liquid was removed by pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of non-woven fabrics, and discloses a flame-retardant non-woven fabric and a preparation method thereof. The non-woven fabric is treated by a flame-retardant treatment agent, and the flame-retardant treatment agent is prepared from the following raw materials in parts by weight: 20-25 parts of dimethyl methylphosphate, 4-5 parts of zinc borate, 3-4 parts of ammonium sulfamate, 1-2 parts of 5-methyl isophthalaldehyde, 0.2-0.3 part of a catalyst, 6-8 parts of a styrene-acrylic emulsion and 40-50 parts of deionized water; the preparation method comprises the following steps: S1, preparing the flame-retardant finishing agent; and S2, flame-retardant finishing of the non-woven fabric. The non-woven fabric has the following advantages and effects: dimethyl methylphosphate and zinc borate with flame retardant effects are added together to play a synergistic flame retardant effect; the styrene-acrylic emulsion assists the components to form a homogeneous system; and the polymer obtained by the polymerization reaction of ammonium sulfamate and 5-methyl isophthalaldehyde can be carbonized under the dehydration action of phosphoric acid to form a carbonized layer, thereby being beneficial to isolating the non-woven fabric from oxygen and achieving the purpose of flame retardancy.

Description

technical field [0001] The present application relates to the field of non-woven fabrics, in particular to a flame-retardant non-woven fabric and a preparation method thereof. Background technique [0002] Non-woven fabrics, also known as non-woven fabrics, are composed of directional or random fibers, and are called cloth because of their appearance and certain properties; non-woven fabrics are moisture-proof, breathable, flexible, light, easy to decompose, and non-woven. Non-toxic, non-irritating, rich in color, low in price, recyclable, etc.; for example, polypropylene (pp material) pellets are mostly used as raw materials, which are produced in one continuous step by high-temperature melting, spinning, laying, and hot-pressing coiling. made. [0003] However, the polypropylene raw materials used in non-woven fabrics currently on the market are hydrocarbon materials, which are more likely to cause combustion and cannot meet the needs of safety and fire prevention. Cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/288D06M11/82D06M15/09D06M15/233D06M15/263D06M15/45D06M15/356
CPCD06M13/288D06M15/45D06M11/82D06M15/233D06M15/263D06M15/09D06M15/3562D06M2200/30
Inventor 陆臣省陆文俊
Owner 浙江雅宝无纺布制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com