Stone-like coating added with ginger nut sand

A technology of real stone paint and slate, applied in the field of coatings, can solve the problems of poor weather resistance, water resistance and alkali resistance, and high cost, and achieve the effects of good bacteriostatic properties, simple construction and wide sources.

Inactive Publication Date: 2021-02-09
王立
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the raw materials for the preparation of existing real stone paints are made of 65% natural colored sand, 30% organic emulsion and 5% other functional additives, which have problems such as high cost, poor weather resistance, water resistance, and alkali resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stone-like coating added with ginger nut sand
  • Stone-like coating added with ginger nut sand
  • Stone-like coating added with ginger nut sand

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] A kind of genuine stone paint added with limestone sand is composed of the following raw materials in parts by weight:

[0085] 200 parts of pure acrylic emulsion-pure acrylic copolymer emulsion;

[0086] 56 parts of elastic emulsion;

[0087] 3 parts of film-forming aid;

[0088] 3 parts of ethylene glycol monobutyl ether;

[0089] 20 parts of steel slag powder;

[0090] 550 parts of limestone sand;

[0091] 30 parts of nano tourmaline powder;

[0092] Carbomer dispersion 5 parts;

[0093] 4 parts comfrey oil;

[0094] 2 parts of defoamer;

[0095] 70 parts of 2% hydroxyethyl cellulose;

[0096] 3 parts of thickener;

[0097] Appropriate amount of pure water.

[0098] The leptone sand is calcined at 1000° C. for 3 hours, cooled to room temperature, and crushed to a powder of 0.08-0.09 mm.

[0099] The mesh number of the steel slag powder is 50-70 mesh.

[0100] The film-forming aid is selected from the group consisting of 2,2,4-trimethyl-1,3-pentanediol dii...

Embodiment 2

[0113] A kind of genuine stone paint added with limestone sand is composed of the following raw materials in parts by weight:

[0114] 300 parts of pure acrylic emulsion-pure acrylic acid copolymer emulsion;

[0115] 100 parts of elastic emulsion;

[0116] 7 parts of film-forming aids;

[0117] 7 parts of ethylene glycol monobutyl ether;

[0118] 60 parts of steel slag powder;

[0119] 780 parts of lime sand;

[0120] 60 parts of nano tourmaline powder;

[0121] 10 parts of carbomer dispersion;

[0122] 10 parts of comfrey oil;

[0123] 5 parts of defoamer;

[0124] 120 parts of 2% hydroxyethyl cellulose;

[0125] 7 parts of thickener;

[0126] Appropriate amount of pure water.

[0127] The leptone sand is calcined at 1000° C. for 3 hours, cooled to room temperature, and crushed to a powder of 0.08-0.09 mm.

[0128] The mesh number of the steel slag powder is 50-70 mesh.

[0129] The thickener is a mixture of zinc stearate and distearyldimethylammonium chloride in ...

Embodiment 3

[0140] A kind of genuine stone paint added with limestone sand is composed of the following raw materials in parts by weight:

[0141] 280 parts of pure acrylic emulsion-pure acrylic copolymer emulsion;

[0142] 75 parts of elastic emulsion;

[0143] 5 parts of film-forming aids;

[0144] 5 parts of ethylene glycol monobutyl ether;

[0145] 42 parts of steel slag powder;

[0146] 700 parts of limestone sand;

[0147] 47 parts of nano tourmaline powder;

[0148] 8 parts of carbomer dispersion;

[0149] 7 parts of comfrey oil;

[0150] 3.5 parts of defoamer;

[0151] 95 parts of 2% hydroxyethyl cellulose;

[0152] 5 parts of thickener;

[0153] Appropriate amount of pure water.

[0154] The leptone sand is calcined at 1000° C. for 3 hours, cooled to room temperature, and crushed to a powder of 0.08-0.09 mm.

[0155] The mesh number of the steel slag powder is 50-70 mesh.

[0156] As the above-mentioned thickener, thickeners generally used in the art can be used witho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

The invention discloses stone-like coating added with ginger nut sand. The stone-like coating is prepared from the following raw materials in parts by weight: 200-300 parts of pure acrylic emulsion-pure acrylic copolymer emulsion; 56-100 parts of an elastic emulsion; 3-7 parts of a coalescing agent; 3-7 parts of ethylene glycol monobutyl ether; 20-60 parts of steel slag powder; 550-780 parts of ginger nut sand; 30-60 parts of nano tourmaline powder; 5-10 parts of a carbomer dispersion liquid; 4-10 parts of lithospermum oil; 2-5 parts of a defoaming agent; 70-120 parts of 2% hydroxyethyl cellulose; 3-7 parts of a thickening agent; proper amount of purified water. The stone-like coating is attractive, environment-friendly and excellent in waterproof performance, and can effectively protect abuilding from being eroded by a severe environment, so that the service life of the building is prolonged; the stone-like coating not only has good weather resistance and is suitable for various regions, but also is simple and convenient to construct, time-saving and easy to dry, the flexibility of the coating is enhanced, and the stone-like coating has good stain resistance and antibacterial activity.

Description

technical field [0001] The invention belongs to the field of coatings. It specifically relates to a real stone paint added with limestone sand. Background technique [0002] Real stone paint is a kind of decorative effect similar to marble and granite. The buildings decorated with real stone paint have natural and real natural color, giving people a sense of elegance, harmony and solemn beauty. It is suitable for indoor and outdoor decoration of various buildings. It can receive vivid, lifelike, and return to nature effects. The existing real stone paint is made of normal quartz sand as color sand. And the preparation raw material of existing real stone paint mostly adopts 65% natural colored sand and 30% organic emulsion and 5% other functional additives to be compounded, and there is cost higher, and problems such as weather resistance, water resistance, alkali resistance are poor. [0003] The use of industrial solid waste to replace natural colored sand can not only gr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/61C09D7/65C09D5/14
CPCC08K2201/011C08L2205/035C09D5/14C09D133/04C09D7/61C09D7/65C08L91/00C08K13/08C08K11/005C08K3/38
Inventor 王立李春成路玉许康
Owner 王立
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com