Rapid dehydration curing agent

A technology of rapid dehydration and curing agent, which is used in fixed/solidified sludge treatment, water pollutants, chemical instruments and methods, etc. Unsatisfactory curing effect and other problems, to achieve the effect of enhanced unconfined compressive strength, low heavy metal leaching content, and low cost

Active Publication Date: 2021-01-01
广州珠科院工程勘察设计有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In order to solve the problems of slow solidification speed, high pH value of dehydrated and solidified bottom mud cake and tail water, unsatisfactory solidification effect and high heavy metal leaching after solidification in the related art, the present invention provides a sludge solidification speed fast, dewatered bottom mud Rapid sediment dehydration and solidification agent with low pH value of mud cake and tail water, and low heavy metal leaching content after solidification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid dehydration curing agent
  • Rapid dehydration curing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A rapid dehydration curing agent, including the following components:

[0040] 20 parts of iron sulfate,

[0041] 20 parts of ferrous sulfate,

[0042] 15 parts of silicon powder,

[0043] 10 parts of organic bentonite,

[0044] 30 parts of quicklime,

[0045] 0.01 parts of polyacrylamide (M=12 million).

[0046] The preparation method of described dehydration curing agent is as follows:

[0047] Accurately weigh the components in parts by weight, mix and grind until the particle size is less than 200 mesh, and obtain the product.

[0048] Sludge treatment method using fast dehydration curing agent:

[0049] The fast dehydration solidifying agent that is prepared is added to the sludge of a certain lake in Guangzhou (the initial moisture content is 88.3%, the lead leaching content is 9.26mg / kg, the mercury leaching content is 0.56mg / kg, and the arsenic leaching content is 7.56mg / kg. kg) in solidification test; the addition of the solidifying agent is 10% of the s...

Embodiment 2

[0051] A rapid dehydration curing agent, including the following components:

[0052] 25 parts of iron sulfate,

[0053] 15 parts of ferrous sulfate,

[0054] 10 parts of silicon powder,

[0055] 10 parts of organic bentonite,

[0056] 15 parts quicklime,

[0057] 0.01 part of polyacrylamide (M=12 million).

[0058] The preparation method of described dehydration curing agent is as follows:

[0059] Accurately weigh the components in parts by weight, mix and grind until the particle size is less than 200 mesh, and obtain the product.

[0060] Sludge treatment method using fast dehydration curing agent:

[0061]The fast dehydration solidifying agent that is prepared is added to the sludge of a certain lake in Guangzhou (the initial moisture content is 88.3%, the lead leaching content is 9.26mg / kg, the mercury leaching content is 0.56mg / kg, and the arsenic leaching content is 7.56mg / kg. kg) in solidification test; the addition of the solidifying agent is 10% of the sludge...

Embodiment 3

[0063] A rapid dehydration curing agent, including the following components:

[0064] 30 parts of iron sulfate,

[0065] 10 parts of ferrous sulfate,

[0066] 20 parts of silicon powder,

[0067] 20 parts of organic bentonite,

[0068] 20 parts quicklime,

[0069] 0.02 parts of polyacrylamide (M=12 million).

[0070] The preparation method of described dehydration curing agent is as follows:

[0071] Accurately weigh the components in parts by weight, mix and grind until the particle size is less than 200 mesh, and obtain the product.

[0072] Sludge treatment method using fast dehydration curing agent:

[0073] The fast dehydration solidifying agent that is prepared is added to the sludge of a certain lake in Guangzhou (the initial moisture content is 88.3%, the lead leaching content is 9.26mg / kg, the mercury leaching content is 0.56mg / kg, and the arsenic leaching content is 7.56mg / kg. kg) in solidification test; the addition of the solidifying agent is 10% of the slud...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of sludge treatment, in particular to a rapid dehydration curing agent for lake and reservoir bottom mud. The rapid dehydration curing agent comprises the followingcomponents: ferric sulfate, ferrous sulfate, silicon powder, bentonite, quick lime and polyacrylamide. According to the rapid dehydration curing agent disclosed in the invention, organic and inorganicmaterials are compounded to obtain the rapid bottom mud dehydration curing agent which is high in lake and reservoir bottom mud dehydration curing speed, low in pH value of dehydrated bottom mud cakes and tail water, and low in heavy metal leaching content after curing.

Description

technical field [0001] The invention relates to the field of sewage sludge treatment, in particular to a rapid dehydration and solidification agent for lake bottom mud. Background technique [0002] Silt usually refers to the mixture (sediment, clay, organic matter and various minerals) in the water body, which sinks to the bottom under long-term physical, chemical and biological effects, and forms sediments (Wang Xue, Fan Guisheng. Fenhe Study on the distribution characteristics of lead, cadmium and mercury in river courses and beaches [J]. People's Yellow River, 2015, (10): 74-77.). Water bodies such as rivers and lakes produce silt. [0003] Lake and reservoir dyed sludge is an extremely complex heterogeneous body composed of inorganic silicon calcium, organic debris, bacterial cells, inorganic-inorganic colloidal particles, etc., which are mixed with sediment, fiber, animal and plant residues in domestic sewage or industrial and mining wastewater. Solid particles such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F11/00C02F11/148C02F101/20
CPCC02F11/008C02F2101/20C02F11/148
Inventor 黄伟杰陈豪刘学智张大伟闫晓满李慧婧张亮亮刘红岩张欣
Owner 广州珠科院工程勘察设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com