Enhanced bipolar plate structure and manufacturing method thereof

A production method and bipolar plate technology, applied in the direction of final product manufacturing, sustainable manufacturing/processing, fuel cells, etc., can solve the problems of high production cost, excessive graphite material, easy to break, etc., and achieve the effect of high production cost

Pending Publication Date: 2020-12-04
重庆市海龙模具有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to solve the existing bipolar plates, which have poor corrosion resistance of metal bipolar plates, resulting in short service life of metal bipolar plate stacks, low strength of composite bipolar plates, and easy fracture. By increasing the thickness of graphite plates Although it can solve the defects of low strength and easy fracture, but the problem of high graphite material and high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Enhanced bipolar plate structure and manufacturing method thereof
  • Enhanced bipolar plate structure and manufacturing method thereof
  • Enhanced bipolar plate structure and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the drawings in the embodiments of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0036] Such as Figures 1 to 3 Shown, a kind of reinforced bipolar plate structure comprises cathode plate 1 and anode plate 2, and cathode plate 1 or anode plate 2 are provided with three-layer structure, and the first layer is the first graphite resin composite layer 11 (by graphite and resin composite), the second layer is metal fiber graphite resin composite layer 12 (composite by metal fiber, graphite and resin), the third layer is the second graphite r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an enhanced bipolar plate structure. The enhanced bipolar plate structure comprises a cathode plate, an anode plate, wherein the cathode plate or the anode plate is provided with a three-layer structure, the first layer is a first graphite resin composite layer, the second layer is a metal fiber graphite resin composite layer, the third layer is a second graphite resin composite layer, and the metal fiber graphite resin composite layer is arranged in the middle area of the cathode plate or the anode plate and peripherally wrapped by the graphite resin composite layer.The cathode plate and the anode plate are bonded into the bipolar plate through glue. The thickness of the first graphite resin composite layer and the thickness of the second graphite resin compositelayer are both 0.1-5 mm, and the thickness of the metal fiber graphite resin composite layer is 0.1-1 mm. According to the invention, metal fibers can greatly improve the structural strength of the graphite resin composite layer; and meanwhile, since the metal fibers are wrapped in the graphite resin composite layer, the metal fibers are isolated from an acid environment generated during operation of a fuel cell and cannot be corroded.

Description

technical field [0001] The invention relates to the technical field of battery manufacturing, in particular to an enhanced bipolar plate structure and a manufacturing method. Background technique [0002] Fuel cell—proton exchange membrane fuel cell (proton exchange membrane fuel cell is abbreviated as PEMFC in English) as a high-efficiency, low-pollution power source has broad applications in future vehicle drive power, portable power and household electricity. It is recognized as an important new energy source in the future. Although PEMFC presents many attractive advantages, it also has some serious shortcomings. In addition to catalytic technology, the main bottlenecks restricting its application are: high manufacturing cost, low volume specific power, etc. As one of the key components of PEMFC, the quality of the bipolar plate accounts for 60% to 80% of the entire fuel cell stack, and its cost accounts for 40% to 60% of the total cost. A simple bipolar plate is one o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M8/0228H01M8/0213H01M8/0258H01M8/0267
CPCH01M8/0213H01M8/0228H01M8/0258H01M8/0267Y02E60/50Y02P70/50
Inventor 宋阳阳颜美聪赵金华李气强黄建权
Owner 重庆市海龙模具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com