High-strength steel fiber adhesive and preparation method thereof

A fiber adhesive, high-strength steel technology, applied in the directions of non-polymer adhesive additives, adhesive types, unsaturated alcohol copolymer adhesives, etc. Disintegration and other problems, to achieve the effect of strong anti-rust and anti-rust function, strong toughness and maintaining fluidity

Pending Publication Date: 2020-11-24
天津恒沣栩翔金属新材料股份有限公司 +1
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because steel fibers will produce prestress during wire drawing and forming, especially high-strength steel wires are deformed, which will cause the fiber rows to break, break, or even disperse and disintegrate during storage, loading and unloading, and transportation after processing, resulting in Unusable problems in engineering construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength steel fiber adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] see figure 1 , the present invention provides a scheme: a high-strength steel fiber adhesive and a preparation method thereof, the high-strength steel fiber adhesive consists of vinyl acetate copolymer, polyvinyl alcohol, polyvinyl alcohol phosphated resin, Composed of amine-based adhesive agent, emulsifier and deionized water, the parts by weight and addition ratio of each composition are 60-80 parts of vinyl acetate copolymer, 6-8 parts of polyvinyl alcohol, polyvinyl alcohol phosphate 15-20 parts of chemical resin, 0.1-1.0 parts of amino-based bonding agent, 2-5 parts of emulsifier and 5-10 parts of deionized water.

[0024] The preparation method of above-mentioned a kind of high-strength steel fiber adhesive comprises the following steps:

[0025] S1. Preparation materials: Prepare 60-80 parts of vinyl acetate copolymer, 6-8 parts of polyvinyl alcohol, 15-20 parts of polyvinyl alcohol phosphated resin, 0.1-1.0 parts of amino-based glue, emulsifier 2-5 parts and 5...

Embodiment 1

[0032] A high-strength steel fiber adhesive and a preparation method thereof, the high-strength steel fiber adhesive consists of vinyl acetate copolymer, polyvinyl alcohol, polyvinyl alcohol phosphated resin, amine-based bonding agent, emulsifier Composed of deionized water, the parts by weight and addition ratio of each composition are 40 parts of vinyl acetate copolymer, 6 parts of polyvinyl alcohol, 15 parts of polyvinyl alcohol phosphated resin, and 0.1 part of amino-based adhesive , 2 parts of emulsifier and 5 parts of deionized water.

[0033] The preparation method of above-mentioned a kind of high-strength steel fiber adhesive comprises the following steps:

[0034]S1. Preparation materials: Prepare 40 parts of vinyl acetate copolymer, 6 parts of polyvinyl alcohol, 15 parts of polyvinyl alcohol phosphated resin, 0.1 part of amino-based adhesive agent, 2 parts of emulsifier and 5 parts of deionized water , put aside;

[0035] S2. Preliminary dissolution: Take 6 parts ...

Embodiment 2

[0041] A high-strength steel fiber adhesive and a preparation method thereof, the high-strength steel fiber adhesive consists of vinyl acetate copolymer, polyvinyl alcohol, polyvinyl alcohol phosphated resin, amine-based bonding agent, emulsifier Composed of deionized water, the parts by weight and addition ratio of each composition are 50 parts of vinyl acetate copolymer, 7 parts of polyvinyl alcohol, 16 parts of polyvinyl alcohol phosphated resin, and 0.4 part of amino-based adhesive , 3 parts of emulsifier and 7 parts of deionized water.

[0042] The preparation method of above-mentioned a kind of high-strength steel fiber adhesive comprises the following steps:

[0043] S1. Preparation materials: 50 parts of vinyl acetate vinyl acid copolymer, 7 parts of polyvinyl alcohol, 16 parts of polyvinyl alcohol phosphated resin, 0.4 part of amino-based adhesive, 3 parts of emulsifier and 7 parts of deionized water, put aside;

[0044] S2. Preliminary dissolution: Take 7 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of industrial buildings and discloses a high-strength steel fiber adhesive and a preparation method thereof. The high-strength steel fiber adhesive comprises the following components in parts by weight: 60-80 parts of a vinyl acetate-ethylene copolymer, 6-8 parts of polyvinyl alcohol, 15-20 parts of phosphorylated polyvinyl alcohol resin, 0.1-1.0 part of an amine cross-linking agent, 2-5 parts of an emulsifier and 5-10 parts of deionized water. The preparation method of the high-strength steel fiber adhesive comprises the following steps of: S1, material preparation; S2, preliminary dissolution; S3, primary mixing; S4, secondary mixing; and S5, tertiary mixing. The high-strength steel fiber adhesive is high in toughness, high in bonding strength, high in water dissolving speed and higher in anti-rust function, the amount of an adhesive for producing tandem steel fiber is small, and the cost of a product is reduced.

Description

technical field [0001] The invention belongs to the technical field of industrial construction, in particular to a high-strength steel fiber adhesive and a preparation method thereof. Background technique [0002] The construction industry is developing rapidly in many aspects, and the requirements for the strength of building concrete are also higher. In order to enhance the structural performance of reinforced concrete, the application of steel fiber has gradually become popular. After a long period of application, there are many disadvantages in the application of loose steel fibers. For example, in the process of concrete mixing, the loose steel fibers are intertwined to form a magpie's nest effect; the steel fibers cannot be dispersed evenly in the concrete, so that they cannot meet expectations. The purpose of the design is to improve the strength of concrete, so the replacement of loose steel fibers with row steel fibers is the first choice. [0003] Rows of steel f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J129/04C09J11/06
CPCC08L2205/025C08L2205/03C08L2312/00C09J11/06C09J123/0853C08L29/04C08K5/3725
Inventor 宋俭黄英武王丽君莫灼庭
Owner 天津恒沣栩翔金属新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com