A matt coating with a soft, smooth touch

A smooth and coating technology, applied in the direction of coating, polyurea/polyurethane coating, etc., can solve the problems of high hardness, poor transparency, etc., to meet the requirements of temperature resistance and scratch resistance, good transparency, good adhesion and The effect of temperature resistance

Active Publication Date: 2022-01-07
安姆科惠州新材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The matt coating provided by this patent is multi-layered, and it also uses solid particles and resins, which still has the problems of poor transparency and high hardness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A matt coating with a soft, smooth touch
  • A matt coating with a soft, smooth touch
  • A matt coating with a soft, smooth touch

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A matte coating with a soft and smooth touch, which is obtained by coating the coating solution on a film and drying it. The added parts by weight, raw material information and addition ratio are as shown in Table 1. The amount of components in Example 1

[0055] The component consumption of the coating liquid of table 1 embodiment 1

[0056]

[0057] Among the above components, polyurethane A is a white aqueous dispersion with a glass transition temperature of 10°C and 36°C, a primary particle size of 0.6-1 μm, and a solid content of 50%;

[0058] Polyurethane resin B is a translucent white aqueous dispersion with a glass transition temperature of 18° C., a primary particle size of 0.3 μm, and a solid content of 50%.

[0059] The dispersion system is composed of water and n-propanol.

[0060] Among the additives, the anti-blocking agent polyethylene wax emulsion is a white water dispersion, its D50 particle size is 1.2 μm, and its solid content is 50%.

[0061] Mi...

Embodiment 2

[0071] A matte coating with a soft and smooth touch, which is obtained by rolling the coating solution onto the film and drying it. The added parts by weight, raw material information and addition ratio are as shown in the component dosage of Example 2 in Table 3

[0072] The component consumption of the coating liquid of table 3 embodiment 2

[0073]

[0074]

[0075] Among the above components, polyurethane A is a white aqueous dispersion with a glass transition temperature of 10°C and 36°C, a primary particle size of 0.6-1 μm, and a solid content of 50%;

[0076] Polyurethane resin B is a translucent white aqueous dispersion with a glass transition temperature of 12°C, a primary particle size of 0.4 μm, and a solid content of 40%.

[0077] The dispersion system is composed of water and isopropanol.

[0078] Among the additives, the anti-blocking agent polyethylene wax emulsion is a white water dispersion, its D50 particle size is 1.2 μm, and its solid content is 50%....

Embodiment 3

[0089] A kind of matt coating with soft and smooth touch, which is obtained by coating the coating solution on a film and drying it. The added parts by weight, raw material information and addition ratio are as shown in the component dosage of Example 3 in Table 5

[0090] The component consumption of the coating liquid of table 5 embodiment 3

[0091]

[0092] Among the above components, polyurethane E is a white aqueous dispersion with a glass transition temperature of 16°C and 40°C, a primary particle size of 1.0-1.4μm, and a solid content of 40%;

[0093] Acrylic resin D is a translucent white aqueous dispersion with a glass transition temperature of 16°C, a primary particle size of 0.3 μm, and a solid content of 35%.

[0094] The dispersion system is composed of water and ethanol.

[0095] Among the additives, the anti-blocking agent polyethylene wax emulsion is a white water dispersion with a D50 particle size of 2.2 μm and a solid content of 40%; the mineral oil def...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
particle diameteraaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention provides a matte coating with a soft and smooth touch, which is prepared by rolling a coating liquid onto a film and drying it. The coating liquid includes the following components in terms of mass percentage: water-dispersible resin 10- 40%, dispersing solvent 60-90%, opening agent 0-3%, defoaming agent 0-0.2%, slip agent 0-1%, leveling agent 0-0.5%, adhesion promoter 0.4-5%. The coating has good adhesion on the surface of PET, NY, BOPP and PE films, and can obtain excellent matte effects after full-scale coating or partial coating on the surface.

Description

technical field [0001] The invention relates to the technical field of packaging material encapsulation, in particular to a soft and smooth matte coating. Background technique [0002] In some packaging containers on the market, the use of various colorful flexible packaging can attract consumers' attention. And some packaging containers with matte effect on the surface give people a simple and elegant feeling. [0003] In flexible packaging, plastic films with a matte surface are used for packaging bags with a matte surface, such as matte BOPP and matte PET films. The surface matting or matte effect of these films is derived from the formation of incompatible polymer particles or inorganic particles uniformly dispersed on the surface. Due to the poor compatibility of the dispersed particles, there will be problems of poor transparency, rough hand feeling and high surface hardness. In addition, the factors of the production process determine that these films are often pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D7/65C09D7/63C08J7/043C08L67/02C08L77/00C08L23/12C08L23/06
CPCC09D175/04C09D7/65C09D7/63C08J7/043C08J7/0427C08L2205/025C08L2205/035C08J2367/02C08J2377/00C08J2323/12C08J2323/06C08L75/04C08L23/06C08L83/04C08K5/3412
Inventor 冯润财吴奇张羽朱妙清蒋建中高虎
Owner 安姆科惠州新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com