An optical structure film and its patterning method for electrode patterning of nano-silver wire transparent conductive film

A technology of transparent conductive film and nano-silver wire, which is applied in the direction of electrical digital data processing, input/output process of data processing, instruments, etc., can solve the problems of serious etching marks of transparent conductive film of nano-silver wire, silver migration, etc., and achieve good results Optical performance and stability, prevent silver migration, low cost effect

Active Publication Date: 2021-09-24
合肥微晶材料科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems existing in the above-mentioned prior art, the present invention provides an optical structure film and a patterning method for electrode patterning of silver nanowire transparent conductive film, in order to effectively solve the problem of etching of transparent conductive film of silver nanowire. Severe marks and problems of silver migration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An optical structure film and its patterning method for electrode patterning of nano-silver wire transparent conductive film
  • An optical structure film and its patterning method for electrode patterning of nano-silver wire transparent conductive film
  • An optical structure film and its patterning method for electrode patterning of nano-silver wire transparent conductive film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] The UV hardening solution formula used in this embodiment is as follows:

[0077]

[0078] The specific preparation method is: weigh each raw material according to the proportion, first add pentaerythritol tetraacrylate to CN8885NS resin, stir at 500r / min for 25min, then add dodecyl mercaptan, light stabilizer 292, BYK- 333 and photoinitiator 754, continue to stir for 20 minutes to obtain UV hardening solution.

[0079] Such as figure 1 As shown, based on the above-mentioned UV hardening solution, an optical structure film is produced in this embodiment:

[0080] Firstly, the UV hardening solution is coated on the surface of the flexible substrate PET through the dimple coating process;

[0081] The UV hardening solution on the surface of the flexible substrate is then embossed using a mold roll with the desired pattern (made in advance by an electron beam etching process) to form a positioning insertion structure of the desired pattern;

[0082] Finally, UV curin...

Embodiment 2

[0088] This embodiment is the same as Embodiment 1, the only difference being that the formula of the UV hardening liquid used is as follows:

[0089]

Embodiment 3

[0091] This embodiment is the same as Embodiment 2, the only difference is that the UV hardening liquid formula used is as follows:

[0092]

[0093] Table 1 shows the performance comparison results of the silver nanowire transparent conductive film obtained in the above examples and comparative examples after electrode patterning.

[0094] Table 1: Comparison of the performance of the patterned conductive film obtained in the comparative example and each embodiment

[0095]

[0096]

[0097] It can be seen from Table 1 that the optical structure layer in the silver nano wire flexible transparent conductive film of the present invention does not affect the performance of the conductive film, and the etching marks of the silver nano wire conductive film of the embodiment are obviously improved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
rate of changeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an optical structure film and a patterning method thereof for electrode patterning of a nano-silver wire transparent conductive film, which uses the optical structure film with a positioning insertion structure and the nano The silver wire transparent conductive film is heat-pressed, so that the positioning insertion structure with high hardness is embedded in the nano-silver wire conductive film, and the electrode patterning of the conductive film is realized, and the required conductive electrode pattern is obtained. The invention can effectively improve the problems of silver migration and etching marks of the nano-silver wire transparent conductive film, and the method is simple and has high reliability.

Description

technical field [0001] The invention belongs to the field of nano-silver wire transparent conductive films, in particular to an optical structure film and a patterning method for electrode patterning of nano-silver wire transparent conductive films. Background technique [0002] The application of nano-silver wire transparent conductive film in the field of touch control is becoming more and more mature. It needs to be processed by electrode patterning, and then laminated with optical transparent adhesive to form a composite film, and then laminated with liquid crystal display module or OLED display module. Made into a touch screen. The electrode patterning method is mainly laser etching, that is, using laser to remove part of the conductive film between the electrode area and the non-electrode area, so as to separate the electrode area from the non-electrode area. The diameter of the laser beam is 25-35 μm. Therefore, the distance between the electrode patterns made by las...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14G06F3/041
CPCC09D175/14G06F3/041G06F2203/04103
Inventor 张梓晗吕鹏姚成鹏张运奇聂彪
Owner 合肥微晶材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com