Soft PE non-woven fabric applied to hygienic products and manufacturing method of soft PE non-woven fabric

A technology for hygiene products and manufacturing methods, applied in textiles, papermaking, non-woven fabrics, etc., can solve problems such as increased frictional resistance, poor spinnability, and poor composite effect.

Inactive Publication Date: 2020-11-03
山东恒鹏卫生用品有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the non-woven fabrics in the prior art are usually made of polyolefin resins. When using such non-woven fabrics, in the case of resins with high crystallinity, although the spinnability is good, the softness is poor, and the hand feeling is poor. Problem: In the case of using a polypropylene resin with low crystallinity and melting point, although there is flexibility, the frictional resistance between fibers and between fibers and other metals becomes large during spinning, resulting in extremely poor spinnability The problem of making it stable is not good, and the composite effect is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soft PE non-woven fabric applied to hygienic products and manufacturing method of soft PE non-woven fabric
  • Soft PE non-woven fabric applied to hygienic products and manufacturing method of soft PE non-woven fabric
  • Soft PE non-woven fabric applied to hygienic products and manufacturing method of soft PE non-woven fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A soft PE non-woven fabric used in hygiene products, including a soft layer and a composite layer, the soft layer is made of low-melting PE raw material, the composite layer is made of PP raw material and adhesive material, the PE raw material is KS560T, the The PP raw material is H39S-2, and the binder is OMBM.

[0030] A kind of manufacturing method of the soft PE non-woven fabric that is applied to hygienic article, adopts following steps to operate:

[0031] S1. Add low-melting PE raw material KS560T into the first die head A, add conventional PP raw material H39S-2 and binder OMBM into the second die head B at a ratio of 1:1, and then mix and stir to form a slurry material;

[0032] S2. Extrude and melt the mixed and stirred slurry into the screw through the feeding system to obtain a hot melt;

[0033] S3, filtering, metering and distributing the hot melt at a certain temperature and a certain pressure;

[0034] S4. Spinning the distributed and metered hot melt...

Embodiment 2

[0049] A soft PE non-woven fabric used in hygiene products, including a soft layer and a composite layer, the soft layer is made of low-melting PE raw material, the composite layer is made of PP raw material and adhesive material, the PE raw material is KS560T, the The PP raw material is H39S-2, and the binder is OMBM.

[0050] A kind of manufacturing method of the soft PE non-woven fabric that is applied to hygienic article, adopts following steps to operate:

[0051] S1. Add low-melting PE raw material KS560T into the first die head A, add conventional PP raw material H39S-2 and binder OMBM into the second die head B at a ratio of 1:1, and then mix and stir to form a slurry material;

[0052] S2. Extrude and melt the mixed and stirred slurry into the screw through the feeding system to obtain a hot melt;

[0053] S3, filtering, metering and distributing the hot melt at a certain temperature and a certain pressure;

[0054] S4. Spinning the distributed and metered hot melt...

Embodiment 3

[0071] A soft PE non-woven fabric used in hygiene products, including a soft layer and a composite layer, the soft layer is made of low-melting PE raw material, the composite layer is made of PP raw material and adhesive material, the PE raw material is KS560T, the The PP raw material is H39S-2, and the binder is OMBM.

[0072] A kind of manufacturing method of the soft PE non-woven fabric that is applied to hygienic article, adopts following steps to operate:

[0073] S1. Add the low melting point PE raw material KS560T into the first die head, add the conventional PP raw material H39S-2 and the binder OMBM into the second die head according to the ratio of 1:1, and then make it mix and stir to form a slurry;

[0074] S2. Extrude and melt the mixed and stirred slurry into the screw through the feeding system to obtain a hot melt;

[0075] S3, filtering, metering and distributing the hot melt at a certain temperature and a certain pressure;

[0076] S4. Spinning the distribu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a soft PE non-woven fabric applied to hygienic products and a manufacturing method of the soft PE non-woven fabric, and belongs to the field of PE non-woven fabrics. The soft PE non-woven fabric applied to the hygienic products comprises a soft layer and a composite layer, the soft layer is made of a low-melting-point PE raw material, the composite layer is made of a PP rawmaterial and a binding material, KS560T is selected as the PE raw material, H39S-2 is selected as the PP raw material, and OMBM is selected as the binding material; and a double-layer structure is adopted, the soft layer is made of a PE raw material with low melt indexes, the soft effect is extremely good, the composite layer is made of the PP raw material and the binding material in a mixed manner, the composite effect of the composite layer, the PE layer and a paper diaper can be guaranteed, more stability is achieved, meanwhile, the good soft effect can be kept, the dual-layer composite technology is adopted, the PE layer and a PP spunbond layer are composited, the soft effect of the PE can be kept, and the composite application to the waistline and other positions of the paper diaperis not influenced.

Description

technical field [0001] The invention relates to the technical field of PE nonwoven fabrics, in particular to a soft PE nonwoven fabric used in sanitary products and a manufacturing method thereof. Background technique [0002] Non-woven fabric, also known as non-woven fabric, is composed of oriented or random fibers. It is called cloth because of its appearance and certain properties. Polyethylene (PE) non-woven fabric is a new type of non-woven fabric. It has the characteristics of non-toxic, skin-friendly, good thermal adhesion, and soft hand feeling. It is especially suitable for the medical and health field. It is an excellent material for surgical gowns, protective clothing, sanitary napkins, and diapers. [0003] At present, the non-woven fabrics in the prior art are usually made of polyolefin resins. When using such non-woven fabrics, in the case of resins with high crystallinity, although the spinnability is good, the softness is poor, and the hand feeling is poor. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H3/14D04H3/10
CPCD04H3/14D04H3/10
Inventor 马德勋王玉梅张志毅鲍汉鑫李凡成邓林林蔡源蒋乃文徐延梅
Owner 山东恒鹏卫生用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap