A composite antibacterial and composite material technology, applied in the direction of nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve the problems of weakened sterilization and disinfection effects of silver particles, achieve high-efficiency sterilization and disinfection, and simple manufacturing method , low toxicity effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] In a 250ml flask, put 100ml of ethylene glycol, 3g of polyvinyl pyrrolidone (PVPK60) with a molecular weight of about 360,000, and place it in an oil bath at 140 degrees to dissolve completely while stirring, and then add 1g of silver nitrate (AgNO3 ) to dissolve completely, continue to add 0.0036g of KBr and 0.0129g of AgCl as nucleating agents, continue to stir for 1 hour, then set the temperature to 150 degrees and continue to react for 1 hour;
[0045] The obtained solution was centrifuged, washed with acetone and pure water, dried to obtain a powder, and the powder was subjected to scanning electron microscope observation results as follows: figure 1 shown, from figure 1 It can be seen that the synthesized basically pure silver nanowires.
[0046] Dissolve 0.3g of the above-mentioned silver nanowires in 100g of water, add 0.1g of sodium lauryl sulfate dispersant and hydrolyzed solution containing 0.1g of tetraethyl orthosilicate (20.25g of absolute ethanol, 6g of ...
Embodiment 2
[0049] In a 250ml flask, put 100ml of ethylene glycol, 2.75g of polyvinylpyrrolidone (PVPK60) with a molecular weight of about 360,000 and 0.25g of polyvinylpyrrolidone (PVPK30) with a molecular weight of about 40,000, and Place it in an oil bath at 140 degrees and stir to dissolve completely, then add 1g of silver nitrate (AgNO3) to dissolve completely. Continue to add 0.0036g of KBr and 0.0129g of AgCl as a nucleating agent, continue to stir for 1 hour, then set the temperature to 150 degrees and continue to react for 1 hour;
[0050] The obtained solution was centrifuged, washed with acetone and pure water, dried to obtain a powder, and the powder was subjected to scanning electron microscope observation results as follows: figure 2 shown, from figure 2 It can be seen that there are obvious nano-silver particles attached to the synthesized nano-silver wire, and it can be determined that the nano-silver composite antibacterial and anti-virus materials, of which the nano-s...
Embodiment 3
[0054] In a 250ml flask, put 100ml of ethylene glycol, 2.50g of polyvinylpyrrolidone (PVPK60) with a molecular weight of about 360,000 and 0.5g of polyvinylpyrrolidone (PVP K30) with a molecular weight of about 40,000, and Place in an oil bath at 140°C and stir to dissolve completely, then add 1g of silver nitrate (AgNO3) to dissolve completely, continue to add 0.0036g of KBr and 0.0129g of AgCl as nucleating agents, continue to stir for 1 hour, then set the temperature to Set at 150 degrees to continue the reaction for 1 hour;
[0055] The obtained solution was centrifuged, washed with acetone and pure water, dried to obtain a powder, and the powder was subjected to scanning electron microscope observation results as follows: image 3 shown, from image 3 It can be seen that there are obvious nano-silver particles attached to the synthesized nano-silver wire, and it can be determined that the nano-silver composite antibacterial and anti-virus material, in which the nano-silv...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
length | aaaaa | aaaaa |
length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com