A kind of flame-retardant self-adhesive adhesive for composite gas isolation board and its preparation method

A technology of self-adhesive and isolation boards, applied in the direction of adhesives, adhesive types, adhesive additives, etc., can solve problems such as structural leakage, and achieve the effects of improving flame retardancy, reducing flow, and reducing aggregation

Active Publication Date: 2021-12-21
SICHUAN WEIDUN JIANGXIN CONSTR CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a kind of flame-retardant self-adhesive adhesive for composite gas separation board and its preparation method, to solve the problem in the prior art of composite gas separation board in the prior art, ordinary waterproof board cannot be fully glued to the secondary lining structure If there is a water channel between the primary lining and the secondary lining structure, it will cause technical problems of large-scale leakage of the structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of flame-retardant self-adhesive adhesive for composite gas isolation board and its preparation method
  • A kind of flame-retardant self-adhesive adhesive for composite gas isolation board and its preparation method
  • A kind of flame-retardant self-adhesive adhesive for composite gas isolation board and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] Preparation of flame retardant self-adhesive for composite gas insulation board:

[0066] 1.1 Raw materials, as shown in Table 1 below:

[0067] The raw material that table 1 embodiment 1 adopts

[0068]

[0069] 1.2 Preparation method:

[0070] (1) Liquid material feeding: put the first polyisobutylene, the first C5 petroleum resin and the second C5 petroleum resin into the reaction kettle after weighing according to the proportion, and carry out high-speed stirring for 20min at a temperature of 100°C. The stirring of the high-speed stirring The speed is 8HZ until the mixture is uniform;

[0071] (2) Solid material feeding: put SIS elastomer, the second polyisobutylene, flame retardant, polyethylene wax, antioxidant and anti-ultraviolet agent into the reaction kettle under the condition of high-speed stirring after weighing according to the proportion, the described The stirring speed of high-speed stirring is 8HZ, and the temperature is raised to 160°C at the same...

Embodiment 2

[0074] Preparation of flame retardant self-adhesive for composite gas insulation board:

[0075] 2.1 Raw materials, as shown in Table 2 below:

[0076] The raw material that table 2 embodiment 2 adopts

[0077]

[0078] 2.2 Preparation method:

[0079] (1) Liquid material feeding: put the first polyisobutylene, the first C5 petroleum resin and the second C5 petroleum resin into the reaction kettle after weighing according to the proportion, and carry out high-speed stirring for 25min at a temperature of 90°C. The stirring of the high-speed stirring The speed is 5HZ until the mixture is uniform;

[0080] (2) Solid material feeding: put SIS elastomer, the second polyisobutylene, flame retardant, polyethylene wax, antioxidant and anti-ultraviolet agent into the reaction kettle under the condition of high-speed stirring after weighing according to the proportion, the described The stirring speed of high-speed stirring is 10HZ, and the temperature is raised to 150°C at the sa...

Embodiment 3

[0083] Preparation of flame retardant self-adhesive for composite gas insulation board:

[0084] 3.1 Raw materials, as shown in Table 3 below:

[0085] The raw material that table 3 embodiment 3 adopts

[0086]

[0087] 3.2 Preparation method:

[0088] (1) Liquid material feeding: put the first polyisobutylene, the first C5 petroleum resin and the second C5 petroleum resin into the reaction kettle after weighing according to the proportion, and carry out high-speed stirring for 18 minutes at a temperature of 110 ° C. The stirring of the high-speed stirring The speed is 10HZ until the mixture is uniform;

[0089] (2) Solid material feeding: put SIS elastomer, the second polyisobutylene, flame retardant, polyethylene wax, antioxidant and anti-ultraviolet agent into the reaction kettle under the condition of high-speed stirring after weighing according to the proportion, the described The stirring speed of high-speed stirring is 5HZ, and the temperature is raised to 170°C a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a flame-retardant self-adhesive for a composite gas isolation board and a preparation method thereof, which solves the problem of the composite gas isolation board in the prior art, where the ordinary waterproof board cannot be fully bonded to the second lining structure, causing the primary lining to be separated from the second lining. The occurrence of water channeling between the structures will cause the technical problem of large-area leakage of the structure. It is prepared from the following raw materials in weight percentage: SIS elastomer 18%-21%; first polyisobutylene 10%-18%; second polyisobutylene 6%-8%; first C5 petroleum resin 25%-30%; The second C5 petroleum resin 5%-12%; flame retardant 10%-20%; polyethylene wax 2%-5%; antioxidant 1%-1.5%; anti-ultraviolet agent 0.5%-1.5%; The sum of weight percentages is 100%. When the present invention is applied to the composite gas isolation board, water channeling between the primary lining and the secondary lining structure is avoided, and large-area leakage of the structure can be avoided.

Description

technical field [0001] The invention relates to a composite gas isolation board, in particular to a flame-retardant self-adhesive adhesive for a composite gas isolation board and a preparation method thereof. Background technique [0002] The anti-gas and waterproof isolation projects of tunnels in my country mainly need to meet gas barrier properties, flame retardancy, antistatic properties and excellent mechanical properties. Most of the gas barrier panels currently in use have poor gas barrier properties, are not antistatic, and are hard Due to the long-term high and low temperature changes in the use environment, there are dimensional changes in the plastic sheet, which leads to gas insulation performance defects; because of the long-term harsh use environment, the material has performance attenuation, and due to the lack of flexibility of the material, It is not easy to fold, which also causes some troubles for road transportation, and has the disadvantage of poor constru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J157/02C09J153/02C09J123/20C09J11/08C09J11/04C09J11/06
CPCC09J157/02C09J11/08C09J11/04C09J11/06C08L2205/035C08L2205/025C08L2201/02C08L2201/22C08L53/02C08L23/22C08K13/02C08K3/016C08K5/0066
Inventor 楚珑晟曹潇尹李雷袁志涛郑贤方刘勇
Owner SICHUAN WEIDUN JIANGXIN CONSTR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More