Superfine denier acrylic fiber and wool blended yarn and preparation method thereof

A wool blended yarn, wool blended technology, applied in yarn, fiber blending, textile and papermaking, etc., can solve problems such as affecting the production progress and product quality, winding aprons, top rollers, rollers, unreasonable proportion of raw materials, etc. , to achieve the effect of improving deodorant and bacteriostatic performance, deodorant comfort and softness, and high flatness.

Active Publication Date: 2020-09-08
JIANGYIN HAOYE TEXTILE
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the fineness of ultra-fine denier acrylic fiber, it is too soft and fluffy, it is easy to produce flying hairs in the production process, and it is easy to produce problems such as aprons, rollers, rollers, etc., which seriously affect the production progress and product quality.
[0004] Due to the rough preparation process of the existing acrylic and wool blended fabrics, the proportion of raw materials is unreasonable, and the strength of the final prepared fabric is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Superfine denier acrylic fiber and wool blended yarn and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0072] see figure 1 Shown, the present invention also provides a kind of preparation method of superfine denier acrylic fiber and wool blended yarn, comprises the following steps:

[0073] (1) B412 worsted blending 2 times;

[0074] (2) B423 worsted head needle;

[0075] (3) B432 worsted two needles;

[0076] (4) B442 worsted three needles;

[0077] (5) B452 worsted four needles;

[0078] (6) FB461 six-pin;

[0079] (7) FB441 roving;

[0080] (8) spun yarn;

[0081] (9) AC6 winds itself;

[0082] (10) FA705 high parallel yarn;

[0083] (11) VTS-08 Sura two-for-one twisting;

[0084] (12) Form superfine denier acrylic and wool blended yarn.

[0085] In the step (1) during the blending process, the surface of the blended yarn is sprayed with an oil agent, and the oil agent is composed of oil, antistatic agent, and water in a percentage by weight of 1:1:8; the spraying frequency of the oil agent is 10~30ml / min.

[0086] In the step (1), the first B412 worsted blending...

Embodiment 1

[0117] Embodiment 1: a blended yarn of ultra-fine denier acrylic fiber and wool, the mass percentage of raw material components of the blended yarn is: 60% ultra-fine denier acrylic fiber and 40% wool.

[0118] The specification of the wool is 20.8mic*85mm.

[0119] The specification of the superfine denier acrylic fiber is 0.9dtex*88mm.

[0120] The preparation of the above-mentioned superfine denier acrylic fiber and wool blended yarn adopts the following method steps:

[0121] (1) B412 worsted blending 2 times;

[0122] (2) B423 worsted head needle;

[0123] (3) B432 worsted two needles;

[0124] (4) B442 worsted three needles;

[0125] (5) B452 worsted four needles;

[0126] (6) FB461 six-pin;

[0127] (7) FB441 roving;

[0128] (8) spun yarn;

[0129] (9) AC6 winds itself;

[0130] (10) FA705 high parallel yarn;

[0131] (11) VTS-08 Sura two-for-one twister.

[0132] (12) Form superfine denier acrylic and wool blended yarn.

[0133] The step (1) sprays an oil ...

Embodiment 2

[0139] Embodiment 2: a blended yarn of superfine denier acrylic fiber and wool, the mass percentage of raw material components of the blended yarn is: 68% superfine denier acrylic fiber and 32% wool.

[0140] The specification of the wool is 20.8mic*85mm.

[0141] The specification of the superfine denier acrylic fiber is 0.9dtex*88mm.

[0142] The preparation of the above-mentioned superfine denier acrylic fiber and wool blended yarn adopts the following method steps:

[0143] (1) B412 worsted blending 2 times;

[0144] (2) B423 worsted head needle;

[0145] (3) B432 worsted two needles;

[0146] (4) B442 worsted three needles;

[0147] (5) B452 worsted four needles;

[0148] (6) FB461 six-pin;

[0149] (7) FB441 roving;

[0150] (8) spun yarn;

[0151] (9) AC6 winds itself;

[0152] (10) FA705 high parallel yarn;

[0153] (11) VTS-08 Sura two-for-one twister.

[0154] (12) Form superfine denier acrylic and wool blended yarn.

[0155] The step (1) sprays an oil ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of textiles, and particularly relates to a superfine denier acrylic fiber and wool blended yarn and a preparation method thereof. The blended yarn comprises the raw material components of, in percentage by mass, 60%-70% of superfine denier acrylic fibers and 30%-40% of wool, and the preparation method comprises the steps that B412 worsted sliver mixingis conducted twice; B432 is worsted for the first time; B432 is worsted two needles; the B442 is worsted three needles; B452 is worsted four needles; FB461 is worsted six needles; FB441 roving is prepared; spinning is prepared; a AC6 automatic winder carries out spooling; FA705 is subjected to high doubling; VTS-08 is subjected to Saurer two-for-one twisting. According to the superfine denier acrylic fiber and wool blended yarn and the preparation method thereof, the yarn is high in strength and has good anti-radiation, anti-static, deodorizing, antibacterial and waterproof performance.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a superfine denier acrylic fiber and wool blended yarn and a preparation method thereof. Background technique [0002] Blended yarn is a yarn spun from two or more fibers, which can make up for the deficiency of a single textile material, reflect the superiority of each component fiber, improve the wearing function of the fabric, and expand the scope of application. [0003] Ultra-fine denier acrylic fiber has the characteristics of soft hand feeling, high strength, soft luster, and higher hygroscopicity than ordinary acrylic fiber. However, due to the thinness of ultra-fine denier acrylic fibers, which are too soft and fluffy, it is easy to produce fly hairs in the production process, and problems such as aprons, top rollers, and rollers are easy to occur, which seriously affects the production progress and product quality. [0004] The existing acrylic fiber and w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/44D01G13/00D01G29/00D01H13/30
CPCD01G13/00D01G29/00D01H13/30D01H13/306D02G3/04D02G3/44D02G3/441D10B2101/12D10B2101/20D10B2201/02D10B2211/02D10B2321/10D10B2331/02D10B2401/021D10B2401/16D10B2401/22
Inventor 孙千涵王文娟许露蓉
Owner JIANGYIN HAOYE TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com