A kind of porous silicon negative electrode material for lithium ion battery and preparation method thereof

A technology for lithium-ion batteries and negative electrode materials, applied in battery electrodes, nanotechnology for materials and surface science, negative electrodes, etc., can solve problems such as loss of active materials, sharp reduction in battery capacity, and collapse of material structure, reaching the first time. High efficiency, improved conductivity, and high specific capacity

Active Publication Date: 2021-10-22
MAANSHAN KEDA PURUI ENERGY TECH CO LTD +2
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor conductivity of the silicon material itself, and the volume expansion of silicon during charging is as high as 300%, the volume expansion during charging and discharging can easily lead to the collapse of the material structure and the peeling and pulverization of the electrodes, resulting in the loss of active materials, which in turn leads to a sharp drop in battery capacity. decrease, the cycle performance is seriously deteriorated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of porous silicon negative electrode material for lithium ion battery and preparation method thereof
  • A kind of porous silicon negative electrode material for lithium ion battery and preparation method thereof
  • A kind of porous silicon negative electrode material for lithium ion battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A method for preparing a porous silicon negative electrode material for a lithium ion battery, comprising the steps of:

[0036] (1) Preparation of nanoporous silicon: Add 1000 g of porous silicon powder with a median particle size of 1 μm and a purity of 99.99% and methanol into the dispersion tank of the sand mill, control the solid content of the mixed solution to be 10%, and then add grinding aid Aluminum chloride, the mass ratio of aluminum chloride and porous silicon powder is 1:100, and the stirring is started for 30 minutes; the material of the grinding beads is hard alloy, and the mass ratio of grinding beads and silicon powder is 30:1; The mixed solution of the mixed solution is introduced into the sand mill, the linear speed of the sand mill is 16m / s, and the grinding time is 50h to obtain a porous silicon slurry; the mass content of oxygen in the nanoporous silicon is obtained by testing. The mass content of the nanoporous silicon is 26%. The median particle...

Embodiment 2

[0040](2) Preparation of nanoporous silicon: 1000 g of porous silicon powder with a median particle size of 30 μm and a purity of 99.95% and ethanol are added to the dispersion tank of the sand mill, and the solid content of the mixed solution is controlled to be 20%, and then a grinding aid is added Sodium pyrophosphate, the mass ratio of sodium pyrophosphate and porous silicon powder is 3:100, start stirring for 30 minutes; the material of the grinding beads is zirconium silicate, and the mass ratio of grinding beads and silicon powder is 20:1; The mixed solution is introduced into the sand mill, the linear speed of the sand mill is 15m / s, and the grinding time is 70h to obtain the porous silicon slurry; the mass content of the oxygen element in the nanoporous silicon is 38% through detection, and the nanoporous silicon The median particle size is 63nm, and the silicon grain size is 8.9nm;

[0041] (2) Preparation of porous silicon negative electrode material precursor: addi...

Embodiment 3

[0044] (1) Preparation of nanoporous silicon: 1000 g of porous silicon powder with a median particle size of 60 μm and a purity of 99.91% and isopropanol are added to the dispersion tank of the sand mill to control the solid content of the mixed solution to be 30%, and then add auxiliary Abrasive sodium polyacrylate, the mass ratio of sodium polyacrylate to porous silicon powder is 6:100, start stirring for 30 minutes; the material of the grinding beads is zirconium silicate, and the mass ratio of grinding beads to silicon powder is 15:1; The mixed solution in the tank is introduced into a sand mill, the linear speed of the sand mill is 15m / s, and the grinding time is 40h to obtain a porous silicon slurry; the mass content of oxygen in the nanoporous silicon is 20% through detection, and the nanoporous The median particle size of silicon is 92nm, and the size of silicon grains is 12.9nm;

[0045] (2) Preparation of the porous silicon negative electrode material precursor: addi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of lithium ion batteries, and in particular relates to a porous silicon negative electrode material for lithium ion batteries and a preparation method thereof. The porous silicon negative electrode material includes nanoporous silicon, conductive carbon and amorphous carbon, and the nanoporous silicon contains Contains oxygen, the oxygen content is 10-40wt.%, the proportion of nanoporous silicon in the negative electrode material is 30%-80wt.%; the proportion of conductive carbon is 5%-30wt.%; the proportion of amorphous carbon %, the median particle size D50 of the nanoporous silicon is below 110nm, and the maximum particle size D100 is below 260nm. The nanoporous silicon is prepared by a wet grinding process, and the raw material is porous silicon powder. The porous silicon powder disclosed by the present invention Silicon anode materials have excellent electrochemical properties, high specific capacity, excellent cycle performance, and high initial efficiency.

Description

technical field [0001] The invention belongs to the technical field of lithium ion batteries, and in particular relates to a porous silicon negative electrode material for lithium ion batteries and a preparation method thereof. Background technique [0002] At present, the conventional lithium ion negative electrode material is mainly graphite negative electrode, but the theoretical specific capacity of graphite negative electrode is only 372mAh / g, which cannot meet the urgent needs of users. The theoretical capacity of silicon is as high as 4200mAh / g, which is more than 10 times the capacity of graphite anode materials. At the same time, the coulombic efficiency of silicon-carbon composites is also close to that of graphite anodes. It is cheap, environmentally friendly, and has abundant earth reserves. It is a new generation of high-capacity The best choice for negative electrode materials. However, due to the poor conductivity of the silicon material itself, and the volum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/38H01M4/36H01M4/62H01M10/0525B82Y30/00B82Y40/00C09C1/56C01B33/02C01B32/05
CPCB82Y30/00B82Y40/00C01B33/02C09C1/56C01B32/05H01M4/364H01M4/366H01M4/386H01M4/625H01M4/628H01M10/0525H01M2004/027Y02E60/10
Inventor 胡亮张少波王浩张小龙俞有康
Owner MAANSHAN KEDA PURUI ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com