Flame-retardant and water-resistant ultraviolet curing adhesive and preparation method thereof

A technology of curing glue and ultraviolet light, which is applied in coatings, polyether coatings, polyurea/polyurethane coatings, etc., can solve the problems of further improvement of water resistance, weather resistance and flame retardancy of ultraviolet curing agents, and achieve the goal of preparation Low cost, good overall performance, and low brittleness

Active Publication Date: 2020-09-01
湖南弘擎电子材料科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water resistance, weather resistance and flame retardancy of the UV curing agent need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030]A flame-retardant and water-resistant UV-curable adhesive is characterized in that it is composed of the following components in parts by weight: 10 parts of ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of chloroacetate, 10 parts of cinnamic acid modified Hyperbranched polytetrahydrofuran 30 parts, 16,17-epoxypregnenolone acetate 1 part, (R)-limonene oxide modified 2,4,6-tris(4-aminophenyl)-1,3,5 - 3 parts of triazine, 1 part of tetraethyl Michler's ketone.

[0031] The preparation method of the ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of propylene chloroacetate comprises the following steps: adding propylene chloroacetate and hydroxyl-terminated nano-hybrid hyperbranched polymer into tetrahydrofuran, at 30°C The reaction was stirred for 3 hours, and the solvent was removed by rotary evaporation to obtain chloroacetate ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer; the chloro-acetate, hydrox...

Embodiment 2

[0036] A flame-retardant and water-resistant UV-curable adhesive is characterized in that it is composed of the following components in parts by weight: 13 parts of ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of chloroacetate, 13 parts of cinnamic acid modified Hyperbranched polytetrahydrofuran 32 parts, 16,17-epoxypregnenolone acetate 1.5 parts, (R)-limonene oxide modified 2,4,6-tris(4-aminophenyl)-1,3,5 - 3.5 parts of triazine, 1.5 parts of benzoin ether.

[0037] The preparation method of the ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of propylene chloroacetate comprises the following steps: adding propylene chloroacetate and hydroxyl-terminated nano-hybrid hyperbranched polymer into dichloromethane, Stirring and reacting at 33°C for 4 hours, and then removing the solvent by rotary evaporation to obtain ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of chloroacetate; said chloro-acetate, hydroxyl...

Embodiment 3

[0042] A flame-retardant and water-resistant UV-curable adhesive is characterized in that it is composed of the following components in parts by weight: 15 parts of ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymers of chloroacetate, 15 parts of cinnamic acid modified Hyperbranched polytetrahydrofuran 35 parts, 16,17-epoxypregnenolone acetate 2 parts, (R)-limonene oxide modified 2,4,6-tris(4-aminophenyl)-1,3,5 - 4 parts of triazine, 2 parts of benzophenone.

[0043] The preparation method of the ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of chloroacetate comprises the following steps: adding chloro-acetate and hydroxyl-terminated nano-hybrid hyperbranched polymer to acetone, at 35°C The reaction was stirred for 4.5 hours, and the solvent was removed by rotary evaporation to obtain the ionized modified hydroxyl-terminated nano-hybrid hyperbranched polymer of chloroacetate; The mass ratio is 0.35:4:25.

[0044] The preparation m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a flame-retardant and water-resistant ultraviolet curing adhesive. The ultraviolet curing adhesive is prepared from, by weight, 10 to 20 parts of an allyl chloroacetate ionization modified hydroxyl-terminated nano-hybrid hyperbranched polymer, 30 to 40 parts of cinnamic acid modified hyperbranched polytetrahydrofuran, 1 to 3 parts of 16,17-epoxypregnenolone acetate, 3 to 5 parts of (R)-limonene oxide modified 2,4,6-tri(4-aminophenyl)-1,3,5-triazine and 1 to 3 parts of a photoinitiator. The invention also discloses a preparation method of the flame-retardant and water-resistant ultraviolet curing adhesive. The ultraviolet curing adhesive disclosed by the invention is good in comprehensive performance, relatively low in brittleness, high in weather resistance, water resistance, flame retardance, ultraviolet resistance and cold and hot impact resistance, high in bonding strength, long in service life and high in economic value, social value and ecological value.

Description

technical field [0001] The invention relates to the technical field of glue, in particular to a flame-retardant and water-resistant UV-curable glue and a preparation method thereof. Background technique [0002] In recent years, with the development of the times, the improvement of people's aesthetic concepts and the continuous improvement of various industry standards, higher requirements have been put forward for the glue used for bonding between different objects, not only requiring high bonding strength, but also It is also required to have sufficient toughness, fast curing speed and environmental friendliness. It is in this situation that UV-curable adhesives have come into people's sight, and its appearance has attracted widespread attention. [0003] UV light curing adhesive is to add a photoinitiator to the resin. After absorbing the high-intensity ultraviolet rays in the ultraviolet light curing equipment, active free radicals are generated, thereby initiating poly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D171/02C09D175/14C09D7/63C08G65/332C08G18/83
CPCC09D171/02C09D7/63C08G65/3326C08G18/831C08L2201/02C08L2201/08C08L75/14C08K5/3492
Inventor 不公告发明人
Owner 湖南弘擎电子材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com