Super-hydrophobic anti-pollution flashover coating with hydrophobic mobility and preparation method thereof

A technology for hydrophobic migration and anti-pollution flashover coatings, which can be applied in anti-fouling/underwater coatings, fire-retardant coatings, coatings, etc. , to ensure long-term effectiveness, the effect of extending service life

Active Publication Date: 2020-08-25
ELECTRIC POWER RESEARCH INSTITUTE OF STATE GRID SHANDONG ELECTRIC POWER COMPANY +1
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the initial hydrophobicity of the RTV antifouling flashover coating is only 110-120°, and as the operating time increases, its hydrophobicity will continue to decrease, resulting in a decrease in its antifouling flashover capability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The application also provides a method for preparing a super-hydrophobic anti-fouling flashover coating described in any one of the above, comprising the following steps in sequence:

[0036] 1) Prepare the organic solvent: take the organic solvent according to the formula and stir evenly, then divide the evenly stirred organic solvent into two parts: 1 part of organic solvent and II part of organic solvent;

[0037] 2) Preparation of particle dispersion: add silicon oxide and flame retardant to 1 part of organic solvent prepared in step 1) according to the formula, and disperse by ultrasonic, shearing or stirring to obtain a system with uniform particle dispersion;

[0038] 3) Prepare the film-forming material dispersion: add the silicone resin to the II organic solvent prepared in step 1) according to the formula, and disperse by shearing or stirring;

[0039] 4) Add the particle dispersion prepared in step 2) to the film-former dispersion prepared in step 3), then ad...

Embodiment 1

[0048] A super-hydrophobic anti-fouling flashover coating with hydrophobic migration, made by mixing component A and component B, the quality of component A: the quality of component B=100:1;

[0049] Among them, component A is made of the following raw materials by mass: 10 parts of silicone resin, 78 parts of a mixture of xylene and ethyl acetate (the mass ratio of xylene and ethyl acetate is 1:1), 3 parts Silicon oxide, 6 parts of aluminum hydroxide, 2 parts of methyl tributyl ketoxime silane crosslinking agent, 3 parts of silane coupling agent, 1 part of BYK-163, 0.5 parts of BYK-066N, 1.5 parts The leveling agent BYK-355;

[0050] B component is silicone resin curing agent.

[0051] The preparation method of the super-hydrophobic antifouling flashover coating with hydrophobic migration of above-mentioned embodiment 1 comprises the following steps carried out in sequence:

[0052] 1) Prepare the organic solvent: take the organic solvent according to the formula and stir ev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application provides a super-hydrophobic anti-pollution flashover coating with hydrophobic mobility. The super-hydrophobic anti-pollution flashover coating is prepared from the following raw materials: organic silicon resin, an organic solvent, silicon oxide, a flame retardant, a cross-linking agent, a coupling agent, a dispersing agent, an antifoaming agent, a leveling agent and an organic silicon resin curing agent. The invention also provides a preparation method of the super-hydrophobic anti-pollution flashover coating with hydrophobic mobility. The anti-pollution flashover coating provided by the invention has super-hydrophobicity and hydrophobic mobility at the same time; the surface hydrophobicity of the anti-pollution flashover coating is improved, the long-term effectiveness of the anti-pollution flashover coating is ensured, the service life of the anti-pollution flashover coating is prolonged, and the occurrence probability of pollution flashover accidents is reduced, sothat problems of low hydrophobicity and easy deposition of dirt on the surface of the existing anti-pollution flashover coating are solved, and the occurrence probability of pollution flashover accidents is reduced.

Description

technical field [0001] The invention relates to the technical field of super-hydrophobic anti-fouling flashover coatings, in particular to a super-hydrophobic anti-fouling flashover coating with hydrophobic mobility and a preparation method thereof. Background technique [0002] A super-hydrophobic surface refers to a surface with a hydrophobic angle greater than 150° and a rolling angle less than 10°. In recent years, superhydrophobic surfaces have attracted widespread attention due to their unique superhydrophobic properties and self-cleaning properties, and have shown broad application prospects in production and life. [0003] With the increasing pollution of the air environment, pollution flashover accidents of transmission lines occur frequently, which seriously threatens the safe and stable operation of the power grid. Pollution flashover accidents mainly go through the following processes: the accumulation of dirt on the surface of the external insulation equipment;...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/16C09D7/61C09D7/63
CPCC09D183/04C09D5/1687C08K2003/2227C08L33/04C08K13/02C08K3/36C08K3/22C08K5/5465C09D5/1675C09D7/61C09D7/48C08L83/04C09D5/18
Inventor 李文静王晓明李辛庚田双姜波朱耿增姚硕王蝶高智悦闫风洁樊志彬郭凯张振岳吴亚平米春旭宗立君赵洺哲王倩王维娜
Owner ELECTRIC POWER RESEARCH INSTITUTE OF STATE GRID SHANDONG ELECTRIC POWER COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com