A zero-voc inorganic fire-resistant functional coating suitable for electronic clean workshops and its preparation method

A clean workshop, inorganic fire-resistant technology, applied in fireproof coatings, cement coatings, anti-fouling/underwater coatings, etc., can solve the problems affecting the product yield of electronic clean workshops, substandard fire performance, and easy production of toxic gases, etc., to achieve It is not easy to produce microorganisms, has excellent fire and heat insulation performance, and has the effect of preventing the growth of algae

Active Publication Date: 2021-11-23
THE IT ELECTRONICS ELEVENTH DESIGN & RES INST SCI & TECHNOLOGICAL ENG
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above object, the present invention provides a zero-VOC inorganic fire-resistant functional coating suitable for electronic clean workshops and its preparation method, to solve the problems in the prior art that contain VOC and other harmful substances, and easily produce toxic gases when burned. , fire performance is not up to standard, prone to mildew and technical problems that affect the yield rate of electronic clean workshop products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A zero-voc inorganic fire-resistant functional coating suitable for electronic clean workshops and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: A zero-VOC inorganic fire-resistant functional coating suitable for electronic clean workshops is characterized in that: in parts by weight, it consists of the following components:

[0033] 35 parts of stuffing;

[0034] Calcium 20 parts;

[0035] Tourmaline powder 10 parts;

[0036] 20 parts of inorganic mineral gel;

[0037] 15 parts of inorganic mineral pigments;

[0038] 5 parts floating beads;

[0039] 20 parts of clear water.

[0040] The fillers include kaolin, talcum powder and sericite, 15 parts of kaolin, 15 parts of talc, 5 parts of sericite, calcium carbonate is light calcium carbonate, tourmaline powder is tourmaline, inorganic mineral gel is made of cement It is made by mixing, the inorganic mineral pigment is colored earth, and the floating beads are high-vacuum glassy hollow microspheres with round silicon-aluminum spheres.

[0041] A corresponding preparation method of a zero-VOC inorganic refractory functional coating suitable for ...

Embodiment 2

[0048] Embodiment 2: A zero-VOC inorganic fire-resistant functional coating suitable for electronic clean workshops is characterized in that: in parts by weight, it consists of the following components:

[0049] 35 parts of stuffing;

[0050] Calcium 20 parts;

[0051] Tourmaline powder 10 parts;

[0052] 20 parts of inorganic mineral gel;

[0053] 15 parts of inorganic mineral pigments;

[0054] 25 parts of clear water.

[0055]The fillers include kaolin, talcum powder and sericite, 15 parts of kaolin, 15 parts of talc, 5 parts of sericite, calcium carbonate is light calcium carbonate, tourmaline powder is tourmaline, inorganic mineral gel is made of cement It is made by mixing, the inorganic mineral pigment is colored earth, and the floating beads are high-vacuum glassy hollow microspheres with round silicon-aluminum spheres.

[0056] A corresponding preparation method of a zero-VOC inorganic refractory functional coating suitable for electronic clean workshops comprise...

Embodiment 3

[0060] Embodiment 3: A zero-VOC inorganic refractory functional coating suitable for electronic clean workshops is characterized in that: in parts by weight, it consists of the following components:

[0061] Filling 35-45 parts;

[0062] Calcium 10-20 parts;

[0063] Tourmaline powder 5-15 parts;

[0064] 15-25 parts of inorganic mineral gel;

[0065] 5-25 parts of inorganic mineral pigments;

[0066] 15-30 parts of clear water.

[0067] The fillers include kaolin, talcum powder and sericite, 15 parts of kaolin, 15 parts of talc, 5 parts of sericite, calcium carbonate is ground calcium carbonate, tourmaline powder is tourmaline, and the inorganic mineral gel is made of cement It is made by mixing, the inorganic mineral pigment is colored earth, and the floating beads are high-vacuum glassy hollow microspheres with round silicon-aluminum spheres.

[0068] A corresponding preparation method of a zero-VOC inorganic refractory functional coating suitable for electronic clean ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a zero-VOC inorganic fire-resistant functional coating suitable for electronic clean workshops and a preparation method. The coating consists of the following components in parts by weight: 35-45 parts of filler; 10-20 parts of calcium; tourmaline powder 5‑15 parts; 15‑25 parts of inorganic mineral gel; 5‑25 parts of inorganic mineral pigment; 1‑5 parts of floating beads; 15‑30 parts of clear water. The invention has the advantages of no VOC, formaldehyde, benzene series, heavy metals and other harmful substances, no radioactive hazard, good fire resistance, antibacterial and mildew resistance, no peculiar smell and no reduction in the yield rate of products inside the electronic clean workshop.

Description

technical field [0001] The invention belongs to the technical field of architectural coatings, in particular to a zero-VOC inorganic fire-resistant functional coating suitable for electronic clean workshops and a preparation method thereof. Background technique [0002] In recent years, China's annual new building area has exceeded 2 billion square meters, and the wall area has reached 7 billion square meters. In the next few years, the annual output value of the entire decoration industry will reach 1.5 trillion yuan, and the home decoration will exceed 1 trillion yuan. As one of the important decorative materials of modern architecture, it has received more and more attention. However, there are still many problems in the current coatings. At first, there are a large number of harmful substances in the existing coatings, which will pose a hazard to life and property safety. The formaldehyde, ammonia, radon, VOC and organic volatiles contained in it will damage people. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D1/06C09D5/18C09D7/61C09D5/14
CPCC09D1/00C09D1/06C09D5/14C09D5/18C09D7/61C09D7/70
Inventor 贾尹杉聂茜陈飞刘阳
Owner THE IT ELECTRONICS ELEVENTH DESIGN & RES INST SCI & TECHNOLOGICAL ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com