Calcium silicate board and preparation method thereof

A technology of calcium silicate board and calcium oxide, applied in the field of building materials, can solve the problems of easy cracking, poor temperature resistance and high water absorption of calcium silicate board, and achieve easy operation, increase temperature resistance and fire resistance time, production low cost effect

Active Publication Date: 2020-07-31
唐山华纤科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing calcium silicate board often uses asbestos as the reinforcing fiber, the temperature resistance of the prepared calcium silicate board is poor, and it is prone to cracks, high water absorption and other disadvantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of calcium silicate board of the present embodiment, comprises following raw material to make: quartz sand 47kg, cement 15kg, fly ash 12kg, superfine ceramic fiber 15kg, paper fiber 3kg;

[0032] Wherein, the fly ash includes the following raw materials in parts by weight: 24 parts of silicon dioxide, 25 parts of aluminum oxide, 10 parts of calcium oxide, 2 parts of magnesium oxide, 5.6 parts of ferric oxide, and the paper fiber It is obtained by adding pulp debonding agent to the pulp board and dissolving it for 20 minutes.

[0033] The preparation method of the calcium silicate board of the present embodiment may further comprise the steps:

[0034] (1) take by weighing according to the parts by weight of each raw material for subsequent use;

[0035] (2) Mix cement and fly ash with water and mix evenly. The mass ratio of cement and fly ash to water is 2:7 to obtain a mixed slurry. Add quartz sand to the mixed slurry and stir evenly, and then add Stir until t...

Embodiment 2

[0040] A kind of calcium silicate board of the present embodiment, comprises following raw material to make: quartz sand 48.5kg, cement 16.5kg, fly ash 14kg, superfine ceramic fiber 16.5kg, paper fiber 5kg;

[0041] Wherein, the fly ash includes the following raw materials in parts by weight: 26.02 parts of silicon dioxide, 26.64 parts of aluminum oxide, 11.75 parts of calcium oxide, 2.27 parts of magnesium oxide, 5.88 parts of ferric oxide, and the paper fiber It is obtained by adding pulp debonding agent to the pulp board and dissolving it for 25 minutes.

[0042] The preparation method of the calcium silicate board of the present embodiment may further comprise the steps:

[0043] (1) take by weighing according to the parts by weight of each raw material for subsequent use;

[0044] (2) Mix cement and fly ash with water and mix evenly. The mass ratio of cement and fly ash to water is 3:7 to obtain a mixed slurry. Add quartz sand to the mixed slurry and stir evenly, and the...

Embodiment 3

[0049] A kind of calcium silicate board of the present embodiment, comprises following raw material to make: quartz sand 50kg, cement 18kg, fly ash 16kg, superfine ceramic fiber 18kg, paper fiber 7kg;

[0050] Wherein, the fly ash includes the following raw materials in parts by weight: 28 parts of silicon dioxide, 28 parts of aluminum oxide, 14 parts of calcium oxide, 2.5 parts of magnesium oxide, 6.0 parts of ferric oxide, and the paper fiber It is obtained by adding pulp debonding agent to the pulp board and dissolving it for 30 minutes.

[0051] The preparation method of the calcium silicate board of the present embodiment may further comprise the steps:

[0052] (1) take by weighing according to the parts by weight of each raw material for subsequent use;

[0053] (2) Cement and fly ash are mixed with water and stirred evenly, the mass ratio of cement and fly ash to water is 4:7 to obtain a mixed slurry, quartz sand is added to the mixed slurry and stirred evenly, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fire resistance timeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a calcium silicate board and a preparation method thereof. The calcium silicate board is prepared from the following raw materials: 47-50 parts of quartz sand, 15-18 parts ofcement, 12-16 parts of fly ash, 15-18 parts of ultrafine ceramic fibers and 3-7 parts of paper fibers. According to the calcium silicate board, quartz sand is used as a main raw material; fly ash is taken as an auxiliary material, under the synergistic effect of cement, the superfine ceramic fibers and the paper fibers, the effects of all the raw materials can be fully played, the refractory temperature of the superfine ceramic fibers can be 1300 DEG C or above, and when the superfine ceramic fibers are applied to the calcium silicate board, the temperature resistance and the refractory time of the calcium silicate board are improved through the synergistic effect of all the raw materials; the fly ash and the paper fibers are added, so that the crack rate of the calcium silicate board canbe reduced; the preparation method of the calcium silicate board is simple, easy to operate, low in production cost and easy for industrial production.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a calcium silicate board and a preparation method thereof. Background technique [0002] Calcium silicate board is a new type of inorganic building material with excellent fire resistance, moisture resistance and sound insulation. According to the composition of silicate, calcium silicate board is divided into two categories, one is tobermullite calcium silicate board; the other is hard calcium silicate type calcium silicate board. [0003] Calcium silicate board can be used as thermal insulation material or decorative material. Calcium silicate board for thermal insulation is mainly used for external wall hanging board, external wall veneer, etc. Decorative calcium silicate boards are mainly used for suspended ceilings, ceilings, house partition walls, and indoor floors. With the continuous expansion of the thermal insulation and decorative finished boar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B40/02C04B111/28
CPCC04B28/00C04B40/0245C04B2111/28C04B14/06C04B18/08C04B14/46C04B18/241
Inventor 王宝祥马立宏吴庆宇何君程师沛曹冠
Owner 唐山华纤科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com