Polyvinyl chloride plastic adhesive and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polyvinyl chloride and adhesive technology, applied in the direction of adhesives, etc., can solve the problems of large amount of solvent, high cost, poor solubility of PVC resin, etc. Effect
Active Publication Date: 2020-07-14
常熟市江南粘合剂有限公司
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The PVC adhesives in the prior art usually use PVC resin which is easy to obtain as the main resin. However, the solubility of PVC resin is poor, the amount of solvent required is large, and the durability of the adhesive force is not ideal. shorter lifespan
[0004] Especially in order to realize the recycling of PVC, there are currently some reports on recycling PVC plastic powder for the preparation of polyvinyl chloride plastic adhesives. Improvement, high recovery cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0030] Embodiment 1: a kind of polyvinyl chloride plastic adhesive, comprises the raw material of following parts by weight:
[0031]
[0032] For the preparation method of the polyvinyl chloride plastic adhesive of this embodiment, please refer to figure 1 shown, including the following steps:
[0033] S10), ethylene dichloride is introduced into the rubber barrel in advance, and ethylene dichloride is used as the primary dissolving solvent of PVC resin powder and CPVC resin powder;
[0034] S20), uniformly mixing PVC resin powder and CPVC resin powder to obtain dry blended resin;
[0035] S30), under stirring conditions, add the dry blended resin into the glue barrel, and use dichloroethane to primary dissolve the dry blended resin to obtain the primary dissolved adhesive. Preferably, in this step, the stirring time is not low In 1.5 hours, more preferably, the stirring time is 1.8-2.5 hours;
[0036] S40), under stirring conditions, add cyclohexanone and xylene in the...
Embodiment 2
[0037] Embodiment 2: the remaining technical solutions of this embodiment 2 are the same as embodiment 1, and the difference is that this embodiment 2 proposes a polyvinyl chloride plastic adhesive, including the raw materials of the following parts by weight:
[0038] Recycling 15 parts of PVC plastic powder, obtained after crushing and pulverizing recycled PVC plastic;
[0039]
Embodiment 3
[0040] Embodiment 3: all the other technical solutions of this embodiment 3 are the same as embodiment 1, the difference is that this embodiment 3 proposes a polyvinyl chloride plastic adhesive, comprising the raw materials of the following parts by weight:
[0041]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a polyvinyl chloride plastic adhesive which comprises the following raw materials in parts by weight: 10-20 parts of PVC resin; 10 to 20 parts of CPVC resin powder; 30 to 40 parts of cyclohexanone; 30 to 40 parts of xylene; 60 to 70 parts of dichloroethane. The invention also relates to a preparation method of the polyvinyl chloride plastic adhesive. CPVC resin powder and PVC resin are subjected to dry mixing to obtain dry mixed resin; dichloroethane is used as a primary dissolving solvent of the dry-mixed resin; dichloroethane is used for rapidly dissolving the CPVC resin powder in the dry-mixed resin; after the primary dissolving adhesive is obtained; ultimate dissolution of the primary dissolving adhesive is realized through cyclohexanone and xylene, the preparation method has the advantages that the amount of consumed solvent is small, and extra additives are not required to be added; the preparation process is simple, more importantly, the polyvinyl chloride plastic adhesive product prepared by the method has very excellent adhesive force durability, and is very suitable for being used as a large-scale preparation process route of a high-end polyvinyl chloride plastic adhesive product.
Description
technical field [0001] The invention relates to the field of adhesive preparation, in particular to a polyvinyl chloride plastic adhesive, and also relates to a preparation method of the polyvinyl chloride plastic adhesive. Background technique [0002] Polyvinyl chloride plastic is widely used because of its light weight, high strength, excellent corrosion resistance, and good durability. In order to achieve the bonding application of polyvinyl chloride plastics, it is necessary to configure and consume a large amount of corresponding polyvinyl chloride plastic adhesives (commonly known as PVC adhesives). Therefore, the market capacity of polyvinyl chloride plastic adhesives is huge. of. [0003] Specifically, the raw materials of existing polyvinyl chloride plastic adhesives usually consist of main resin, solvent and additives. Among them, the adhesive force and performance of polyvinyl chloride plastic adhesive mainly depend on the main resin. The performance of the mat...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.