Formula and processing method of quick-hardening and short-curing-period concrete

A processing method and concrete technology, applied in the field of concrete, can solve the problems of not meeting building construction requirements, long maintenance period, poor sound insulation, etc., and achieve good moisture-proof and waterproof effect, reduce maintenance period, and reduce weight.

Inactive Publication Date: 2020-06-16
广东碧鸿腾建材科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide fast hardening, short curing period concrete formula and processing method, which has the advantages of fast hardening and short curing period, and solves the problems of heavy quality, poor sound insulation and long curing period of existing concrete products. More and more problems that do not meet the needs of building construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Rapid hardening, short curing period concrete formula, the proportion of each product component is:

[0052] Magnesium oxide: 275 / kg;

[0053] Magnesium chloride: 175 / kg;

[0054] Sand: 150 / kg;

[0055] Stone: 200 / kg;

[0056] Fiber web: 58 / m;

[0057] Fly ash: 50 / kg;

[0058] Brown silk: 2 / kg;

[0059] Catalyst: 0.4 / kg;

[0060] Early strength agent: 0.6 / kg;

[0061] Water reducer: 0.5 / kg;

[0062] Water: 350 / kg.

[0063] Rapid hardening, short curing period concrete processing method:

[0064] First, add magnesium oxide, magnesium chloride, sand, stone, fiber net, fly ash, brown silk, catalyst, water reducer and water into the concrete mixer and stir for 5 minutes; then add the early strength agent into the concrete mixer, Then continue stirring for 10 minutes to obtain finished concrete.

Embodiment 2

[0066] In embodiment one, add following operation:

[0067] Its component ratio of catalyst is:

[0068] Sodium rosinate: 9.3-9.8%;

[0069] Sodium a-alkenyl sulfonate: 6.5-6.8%;

[0070] Fatty acid diethanolamide: 3.6-4.0%;

[0071] Sodium dodecylbenzenesulfonate: 1.7-2.0%;

[0072] Sodium chloride: 0.2-0.3%;

[0073] Sodium hydroxide: 0.04-0.05%, the rest is water.

[0074] Rapid hardening, short curing period concrete formula, the proportion of each product component is:

[0075] Magnesium oxide: 275 / kg;

[0076] Magnesium chloride: 175 / kg;

[0077] Sand: 150 / kg;

[0078] Stone: 200 / kg;

[0079] Fiber web: 58 / m;

[0080] Fly ash: 50 / kg;

[0081] Brown silk: 2 / kg;

[0082] Catalyst: 0.4 / kg;

[0083] Early strength agent: 0.6 / kg;

[0084] Water reducer: 0.5 / kg;

[0085] Water: 350 / kg.

[0086] Rapid hardening, short curing period concrete processing method:

[0087] First, add magnesium oxide, magnesium chloride, sand, stone, fiber net, fly ash, brown silk, c...

Embodiment 3

[0089] In embodiment two, add following operation:

[0090] The components of the early strength agent are proportioned according to the mass percentage:

[0091] Lithium carbonate: 30-40%;

[0092] Carboxyethyl cellulose: 35-45%;

[0093] Metaaluminate accelerator: 15-35%.

[0094] Rapid hardening, short curing period concrete formula, the proportion of each product component is:

[0095] Magnesium oxide: 275 / kg;

[0096] Magnesium chloride: 175 / kg;

[0097] Sand: 150 / kg;

[0098] Stone: 200 / kg;

[0099] Fiber web: 58 / m;

[0100] Fly ash: 50 / kg;

[0101] Brown silk: 2 / kg;

[0102] Catalyst: 0.4 / kg;

[0103] Early strength agent: 0.6 / kg;

[0104] Water reducer: 0.5 / kg;

[0105] Water: 350 / kg.

[0106] Rapid hardening, short curing period concrete processing method:

[0107] First, add magnesium oxide, magnesium chloride, sand, stone, fiber net, fly ash, brown silk, catalyst, water reducer and water into the concrete mixer and stir for 5 minutes; then add the early ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formula and processing method of quick-hardening and short-curing-period concrete. The formula of the quick-hardening and short-curing-period concrete comprises the components: 275 / kg of magnesium oxide, 175 / kg of magnesium chloride, 150 / kg of sand, 200 / kg of stone, 58 / m of a fiber net, 50 / kg of fly ash, 2 / kg of palm fibers, 0.4 / kg of a catalyst, 0.6 / kg of an early strength agent, 0.5 / kg of a water reducing agent, and 350 / kg of water. The processing method of the quick-hardening and short-curing-period concrete comprises the steps: firstly, sequentially adding the magnesium oxide, the magnesium chloride, the sand, the stone, the fiber net, the fly ash, the palm fibers, the catalyst, the water reducing agent and the water into a concrete stirrer, and stirring for 5min; and then adding the early strength agent into the concrete stirrer, and continuously stirring for 10 min. By adopting the concrete prepared by the preparation method, the weight of a concrete product can be reduced, the maintenance period of the concrete product can be shortened, the maintenance cost of building construction is reduced, and a product prepared from the concrete prepared by the preparation method has good damp-proof and waterproof effects.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to the formulation and processing method of concrete with rapid hardening and short curing period. Background technique [0002] Concrete is a general term for composite materials made of gel material, aggregate and water in an appropriate proportion, and then hardened after a certain period of time. It is the most widely used artificial civil construction material in the world. Concrete has high hardness and a wide range of raw materials. The cost is low, and it is widely used in structures such as houses, roads, military projects, and nuclear power plants. However, the existing concrete products are heavy, poor in sound insulation, and long in maintenance cycles, which are increasingly unsuitable for building construction. . Contents of the invention [0003] The purpose of the present invention is to provide fast hardening, short curing period concrete formula and processing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/32C04B24/34C04B24/38C04B111/27
CPCC04B28/32C04B40/0039C04B2111/27C04B14/02C04B14/06C04B18/08C04B18/248C04B2103/10C04B2103/302C04B24/34C04B24/16C04B24/124C04B24/20C04B22/124C04B22/062C04B22/10C04B24/383C04B22/08
Inventor 廖超继余常满杨伟邱振华周铜
Owner 广东碧鸿腾建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap