Preparation method of carbonized loofah/graphene-carbon nanotube composite material

A carbon nanotube and composite material technology, which is applied in the field of preparation of carbonized loofah/graphene-carbon nanotube composite materials, can solve the problems of low electromagnetic shielding performance of composite materials, and achieves easy mass production, low production cost, high The effect of electromagnetic shielding performance

Active Publication Date: 2020-06-12
西安昊友航天复合材料有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of preparation method of carbonized loofah / graphene-carbon nanotube (CL / GNSs-CNT / CE) composite material, solve the problem that the electromagnetic shielding performance of composite material is low in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of carbonized loofah/graphene-carbon nanotube composite material
  • Preparation method of carbonized loofah/graphene-carbon nanotube composite material
  • Preparation method of carbonized loofah/graphene-carbon nanotube composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A kind of preparation method of carbonized loofah / graphene-carbon nanotube (CL / GNSs-CNT / CE) composite material of the present invention, concrete steps are as follows:

[0026] Step 1, dissolving polyvinyl alcohol particles in deionized water and reacting in a water bath at 90°C for 1-2 hours to obtain a polyvinyl alcohol solution with a mass concentration of 80 mg / mL;

[0027] Step 2, dispersing graphene and carbon nanotubes in a polyvinyl alcohol solution, and ultrasonically stirring for 30 to 60 minutes to obtain a graphene-carbon nanotube / polyvinyl alcohol solution;

[0028] The mass ratio of graphene, carbon nanotubes and polyvinyl alcohol solution is 0.025-0.062:0.008:10;

[0029] The producers of graphene are Xiamen Knano Graphene Company; the producers of carbon nanotubes are Nanocyl S.A.Nanocyl NC7000 of Belgium.

[0030] The thickness of graphene is <30nm; the average diameter of carbon nanotubes is 9.5nm;

[0031] Step 3, preparing carbonized loofah / graphen...

Embodiment 1

[0040] A kind of preparation method of CL / GNSs-CNT / CE composite material, concrete steps are as follows:

[0041] Step 1: Dissolve 8g of polyvinyl alcohol particles in 92ml of deionized water and react in a water bath at 90°C for 1 hour to obtain a polyvinyl alcohol solution with a mass concentration of 80mg / mL;

[0042] Step 2, disperse 3wt% graphene and 1wt% carbon nanotubes in 10ml of the above-mentioned polyvinyl alcohol solution, and ultrasonically stir for 30min to 60min to obtain a graphene-carbon nanotube / polyvinyl alcohol solution;

[0043] Step 3, preparing CL / GNSs-CNT composite material, the specific steps are as follows:

[0044] Step 3.1, wash the loofah, cut out a rectangle with a size of 40×30mm, place it in a vacuum oven at 60°C for drying, and pour the graphene-carbon nanotube / polyvinyl alcohol solution on the loofah, so that the solution is evenly wrapped in the On the loofah fiber, place it in a 60°C vacuum oven for drying and then compact it;

[0045] Ste...

Embodiment 2

[0050] A kind of preparation method of CL / GNSs-CNT / CE composite material, concrete steps are as follows:

[0051] Step 1: Dissolve 8g of polyvinyl alcohol particles in 92ml of deionized water and react in a water bath at 90°C for 1-2 hours to obtain a polyvinyl alcohol solution with a mass concentration of 80mg / ml;

[0052] Step 2, disperse 5wt% graphene and 1wt% carbon nanotubes in the above-mentioned polyvinyl alcohol solution of 10ml, and ultrasonically stir for 40min to obtain a graphene-carbon nanotube / polyvinyl alcohol solution;

[0053] Step 3, preparing CL / GNSs-CNT composite material, the specific steps are as follows:

[0054] Step 3.1, wash the loofah, cut out a rectangle with a size of 40×30mm, place it in a vacuum oven at 60°C for drying, and pour the graphene-carbon nanotube / polyvinyl alcohol solution on the loofah, so that the solution is evenly wrapped in the On the loofah fiber, place it in a 60°C vacuum oven for drying and then compact it;

[0055] Step 3.2,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a carbonized loofah / graphene-carbon nanotube composite material. The preparation method specifically comprises the following steps: dispersing grapheneand carbon nanotubes into a polyvinyl alcohol solution, pouring the obtained mixture on rectangular loofah sponge, drying in vacuum, compacting, carbonizing in a tubular furnace to obtain a CL / GNSs-CNT composite material, mixing and stirring cyanate ester and epoxy resin, casting on the CL / GNSs-CNT composite material, and curing to obtain the carbonized loofah / graphene-carbon nanotube / cyanate ester resin composite material. The CL / GNSs-CNT / CE composite material prepared by the method has excellent electromagnetic shielding performance and certain mechanical properties, and can meet the application requirements in the fields of aerospace, electronic packaging and the like.

Description

technical field [0001] The invention belongs to the technical field of composite material preparation, and in particular relates to a method for preparing a carbonized loofah / graphene-carbon nanotube composite material. Background technique [0002] With the development of electronic devices and electromagnetic wave technology in civilian and military fields, electromagnetic wave pollution has increasingly become a serious threat to human health and the inherent performance of nearby devices. Therefore, it is very important to design and prepare high-efficiency electromagnetic interference (EMI) shielding materials with strong shielding performance and environmental adaptability to solve this problem. [0003] The formation of a porous structure is a major technological advancement that significantly alleviates the propagation of electromagnetic waves from the air to electromagnetic shielding materials, and significantly reduces secondary electromagnetic radiation pollution....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L79/04C08L63/00C08K9/10C08K3/04
CPCC08L79/04C08K2201/001C08L63/00C08K9/10C08K3/042C08K3/041C08K3/04
Inventor 任鹏刚郭铮铮宗泽任芳靳彦岭
Owner 西安昊友航天复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com