A dual-functional electrolytic water electrode with superwetting property and its preparation method

An electrolyzed water, dual-function technology, applied in the field of nanomaterials, can solve the problems of not being able to maximize the utilization of active sites, hindering electrolyte mass transfer, blocking active sites, etc., to overcome the bubble shielding effect, promote rapid diffusion, The effect of reducing sticking

Active Publication Date: 2021-02-19
ZHEJIANG FORESTRY UNIVERSITY
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In electrolyzed water, if the electrolyte cannot fully wet the electrode surface, the maximum utilization of the active sites cannot be achieved, resulting in poor hydrogen evolution activity
In addition, a large amount of hydrogen and oxygen will be generated on the electrode surface under high current density. If these bubbles cannot diffuse from the electrode surface in time, it will lead to a serious "shielding effect" of the bubbles—impeding the mass transfer of the electrolyte and blocking the active sites. , which eventually reduces the hydrogen evolution activity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A dual-functional electrolytic water electrode with superwetting property and its preparation method
  • A dual-functional electrolytic water electrode with superwetting property and its preparation method
  • A dual-functional electrolytic water electrode with superwetting property and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] S1: Pretreatment of foamed nickel substrate: Cut the foamed nickel material into a sheet with a length of 2 cm and a width of 2 cm, then ultrasonically clean it with acetone and absolute ethanol for 3 minutes, and then put it in a vacuum drying oven at 50 ° C for 24 hours to obtain ; S2: Preparation of precursor solution: Dissolve cobalt acetate tetrahydrate and sodium sulfide nonahydrate in 15mol ultrapure water at a molar ratio of 5mmol:3mmol, and stir for 25min until dissolved to obtain a precursor solution; S3: Hydrothermal reaction: Transfer the precursor solution into a 50mL reaction kettle with a carrier nickel foam, and carry out a hydrothermal reaction at 100°C. After reacting for 8 hours, the product was collected by natural cooling, cleaned with deionized water and absolute ethanol, and removed. Vacuum drying, that is.

Embodiment 2

[0028] S1: Pretreatment of foamed nickel substrate: Cut the foamed nickel material into a sheet with a length of 5 cm and a width of 5 cm, then ultrasonically clean it with acetone and absolute ethanol for 10 minutes, and then put it in a vacuum drying oven at 70 ° C for 15 hours to obtain ; S2: Preparation of precursor solution: Dissolve cobalt acetate tetrahydrate and sodium sulfide nonahydrate in 51.35mol ultrapure water at a molar ratio of 5mmol:5mmol, and stir for 50min until dissolved to obtain a precursor solution; S3: hydrothermal reaction : Transfer the precursor solution into a 50mL reaction kettle with carrier foam nickel, carry out hydrothermal reaction at 200°C, after reacting for 3h, cool and collect the product naturally, wash the product with deionized water and absolute ethanol and remove It is vacuum-dried and obtained.

Embodiment 3

[0030] S1: Pretreatment of foamed nickel substrate: Cut the foamed nickel material into a sheet with a length of 2 cm and a width of 3 cm, then ultrasonically clean it with acetone and absolute ethanol for 5 minutes, and then put it in a vacuum oven at 60°C for 20 hours to get the final product. ; S2: Preparation of precursor solution: Dissolve cobalt acetate tetrahydrate and sodium sulfide nonahydrate in 22mol ultrapure water at a molar ratio of 5mmol: 4mmol, stir magnetically for 30min until dissolved, and obtain a precursor solution; S3: hydrothermal reaction : Transfer the precursor solution into a 50mL reaction kettle with carrier nickel foam, carry out hydrothermal reaction at 150°C, after reacting for 5h, cool and collect the product naturally, wash the product with deionized water and absolute ethanol and remove It is vacuum-dried and obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a super-wetting dual-function electrolytic water electrode and its preparation method and application. The super-wetting dual-functional electrolytic water electrode of the present invention is formed by foaming nickel with cobalt acetate tetrahydrate and sodium sulfide nonahydrate. The surface reaction generates a dense nanosheet array structure. The electrode prepared by the method of the present invention has superhydrophilicity and supergas repellency, so that the electrolytic water reaction on the surface of the electrode continues to occur, which is beneficial to the mass transfer of reactants and the rapid diffusion of gas in the process of catalyzing hydrogen evolution, and finally makes The electrode exhibits excellent dual-functional water electrolysis performance, which significantly improves the efficiency of catalytic hydrogen evolution and reduces the cost of catalysis, which is of great significance to promote the development of hydrogen evolution technology and further use of clean energy.

Description

technical field [0001] The invention relates to the field of nanometer materials, in particular to a super-wetting dual-function electrolytic water electrode and a preparation method thereof. Background technique [0002] Renewable clean energy has always been a research hotspot in the field of energy utilization and conversion. Hydrogen energy is considered as an ideal green new energy due to its advantages of cleanness, high calorific value, renewable and various forms of utilization. Electrolysis of water is an efficient way to produce hydrogen energy. However, in the electrolysis of water to produce hydrogen, the high anodic and cathodic reaction barriers make it necessary to consume high electric energy to realize the decomposition of water, and the energy conversion efficiency is low. As a catalytic material for electrolysis of hydrogen evolution, noble metals have both good activity and stability. However, due to their high price, the cost of hydrogen production by ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/031C25B11/061C25B11/073C25B1/04H01M12/06H01M4/90H01M4/88H01G11/86H01G11/30
CPCC25B1/04C25B11/031C25B11/051C25B11/091H01G11/30H01G11/86H01M4/88H01M4/9016H01M12/06Y02E60/36
Inventor 李彩彩姜林伟孙庆丰杨彩霞徐璐璐
Owner ZHEJIANG FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com