A kind of friction material and its preparation method and application

A technology of friction materials and raw materials, applied in friction linings, mechanical equipment, gear transmission mechanisms, etc., can solve the problems of poor material stability and consistency, improve the stability of friction coefficient, stable performance, and eliminate the performance variation of friction materials. poor effect

Active Publication Date: 2022-03-15
BEIJING TIANRENDAOHE NEW MATERIAL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problem of poor material stability and consistency caused by pressure unloading during the cooling process of the existing copper-based powder metallurgy friction material after high temperature and high pressure sintering, and to provide a friction material and its preparation method and use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of friction material and its preparation method and application
  • A kind of friction material and its preparation method and application
  • A kind of friction material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0049] The invention provides a method for preparing a friction material, which comprises the steps of batching, mixing, pressing and sintering the raw materials of the friction material in sequence, and the sintering step includes the following steps:

[0050] 1) In an atmosphere of hydrogen and / or nitrogen, heat the friction material compact at 950-1050°C and 2-4MPa for 15-30min once;

[0051] 2) After the first heat preservation is completed, the temperature of the friction material compact is lowered to 750-850°C at 2-4MPa, and a second heat preservation is carried out at 2-4MPa, 750-850°C for 15-30min;

[0052] 3) After the second heat preservation is completed, the temperature of the friction material compact is lowered to 550-650°C at 2-4MPa, and three heat preservations are carried out at 2-4MPa, 550-650°C for 15-30min;

[0053] 4) After three times of heat preservation, the pressure is released, and the friction material compact is cooled to room temperature to obtain...

Embodiment 1

[0092] This embodiment provides a friction material, which includes the following raw materials: copper powder 55kg, iron powder 28kg, ferrochrome powder 6kg, graphite 6kg, silicon dioxide 2kg, molybdenum disulfide 1.5kg, cast iron powder 1kg, zirconium corundum 2kg, the mass content of zirconium dioxide in the zirconium corundum is 8%.

[0093] The preparation method of the friction material comprises the following steps:

[0094] (1) batching: take described raw material respectively by above-mentioned proportioning;

[0095] (2) Mixing: mixing the weighed raw materials to obtain the friction material mixture;

[0096] (3) Pressing: pressing the friction material mixture into a compact to obtain a friction material compact, the pressing pressure is 6 MPa, and the pressing time is 5 s;

[0097] (4) sintering: the sintering step comprises the following steps:

[0098] 1) Under the atmosphere of hydrogen and nitrogen, heat the friction material compact at 950°C and 4MPa for ...

Embodiment 2

[0103] This embodiment provides a friction material, which includes the following raw materials: 60 kg of copper powder, 22 kg of iron powder, 8 kg of ferrochrome powder, 4 kg of graphite, 4 kg of silicon dioxide, 0.5 kg of molybdenum disulfide, 2 kg of cast iron powder, zirconium corundum 1 kg, the mass content of zirconium dioxide in the zirconium corundum is 12%.

[0104] The preparation method of the friction material comprises the following steps:

[0105] (1) batching: take described raw material respectively by above-mentioned proportioning;

[0106] (2) Mixing: mixing the weighed raw materials to obtain the friction material mixture;

[0107] (3) Pressing: pressing the friction material mixture into a compact to obtain a friction material compact, the pressing pressure is 15MPa, and the pressing time is 3s;

[0108] (4) sintering: the sintering step comprises the following steps:

[0109] 1) Under the atmosphere of hydrogen and nitrogen, heat the friction material c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of brake materials, in particular to a friction material and its preparation method and application. The preparation method of the friction material provided by the present invention includes the steps of batching, mixing, pressing and sintering the raw materials of the friction material in sequence, and the sintering step includes the following steps: 1) under the atmosphere of hydrogen and / or nitrogen, the friction The material compact is kept at 950-1050°C and 2-4MPa for 15-30min once; 2) the friction material compact is cooled to 750-850°C at 2-4MPa, and the second heat preservation is carried out for 15-30min; 3) Cool down the friction material green compact at 2-4MPa to 550-650°C, and conduct three times of heat preservation for 15-30min; 4) After the three times of heat preservation, remove the pressure and cool to room temperature to obtain the friction material. The preparation method of the friction material provided by the present invention can effectively avoid the problem that the friction coefficient of the friction material becomes poor in consistency due to the expansion of the friction material after the pressure is unloaded under high temperature conditions.

Description

technical field [0001] The invention relates to the technical field of brake materials, in particular to a friction material and its preparation method and application. Background technique [0002] Friction materials are the key materials for friction brakes and clutches in aviation, vehicles, machinery, etc. With the development of science and technology, the power, speed and load of the machine are increasing day by day, and the working conditions are becoming more and more severe. Therefore, higher requirements are put forward for the comprehensive performance of friction materials, that is, in addition to the requirements of good wear resistance, high strength, In addition to good thermal conductivity, corrosion resistance, and low noise, it also has a stable friction coefficient to keep the vehicle stable at high speed and high pressure. [0003] Existing friction materials generally include asbestos type, semi-metal type, and ceramic type. Asbestos-type friction mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F5/00B22F1/12B22F3/10B22F3/14C22C9/00F16D69/02
CPCB22F1/0003B22F5/00B22F3/14B22F3/1007B22F3/1028C22C9/00F16D69/027F16D2200/0026F16D2200/0082B22F2998/10B22F2999/00B22F2009/041B22F2201/013B22F2201/02
Inventor 吴佩芳释加才让赵尚节曹静武程景琳马成龙
Owner BEIJING TIANRENDAOHE NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com