Method for finely adjusting glossiness of water-based matte finish paint by improving spraying process

A glossy, micro-adjustment technology, applied in the device, coating, special surface and other directions of coating liquid on the surface, can solve the problem of not considering the influence of paint film gloss, unable to fully meet the customer's gloss stability, gloss deviation It can solve the problems of large and other problems, and achieve the effect of solving the gloss deviation of the paint film and improving the pass rate of the first inspection.

Inactive Publication Date: 2020-04-14
永济优耐特绝缘材料有限责任公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention adjusts the paint film formula only from the paint itself, but does not consider the influence of construction environment and other influencing factors on the paint film gloss
[0004] At present, in the northern region, the process conditions used in the spraying process of water-based epoxy topcoat are generally paint viscosity of 95s, flash-off time of 1h, baking at 60°C for 2h, and the average glossiness of the paint film of water-based topcoat is 16 / 60° , due to the ambient temperature below 15°C and humidity between 15% and 30% in winter in the north, the environmental conditions are dry and cold. Adjustment from the paint itself alone has a large deviation from the designed gloss, which cannot fully meet the customer's requirements for gloss. Stability requirements, the traditional process of general water-based topcoat is no longer applicable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for improving the spraying process and fine-tuning the glossiness of a water-based matte topcoat, specifically comprising the following process steps:

[0029] 1) Pickling and phosphating the parts to be sprayed to treat the oil and rust on the substrate;

[0030] 2) Control the moisture of the workpiece to be sprayed and place it in a normal temperature environment;

[0031] 3) Protect the part of the workpiece to be sprayed that does not need to be sprayed;

[0032] 4) Spray the primer, spray 3 times, each time at an interval of 10 minutes;

[0033] 5) After spraying the primer, flash for 45 minutes and bake at 60°C for 1.5 hours;

[0034] 6) After the sprayed workpiece is cooled, detect the paint film thickness and adhesion;

[0035] 7) Grind the sprayed workpiece and clean the dust;

[0036] 8) Adjust the viscosity of the topcoat to 20s, and spray the topcoat for 3 times, with an interval of 10 minutes between each spraying, to ensure that each spraying...

Embodiment 2

[0042] A method for improving the spraying process and fine-tuning the glossiness of a water-based matte topcoat, specifically comprising the following process steps:

[0043] 1) Pickling and phosphating the parts to be sprayed to treat the oil and rust on the substrate;

[0044] 2) Control the moisture of the workpiece to be sprayed and place it in a normal temperature environment;

[0045] 3) Protect the part of the workpiece to be sprayed that does not need to be sprayed;

[0046] 4) Spray the primer, spray 2 times, each time at an interval of 11 minutes;

[0047] 5) After spraying the primer, flash for 50 minutes and bake at 60°C for 2 hours;

[0048] 6) After the sprayed workpiece is cooled, detect the paint film thickness and adhesion;

[0049] 7) Grind the sprayed workpiece and clean the dust;

[0050] 8) Adjust the viscosity of the topcoat to 21s, and spray the topcoat for 3 times, with an interval of 11 minutes between each spraying, to ensure that each spraying i...

Embodiment 3

[0056] A method for improving the spraying process and fine-tuning the glossiness of a water-based matte topcoat, specifically comprising the following process steps:

[0057] 1) Pickling and phosphating the parts to be sprayed to treat the oil and rust on the substrate;

[0058] 2) Control the moisture of the workpiece to be sprayed and place it in a normal temperature environment;

[0059] 3) Protect the part of the workpiece to be sprayed that does not need to be sprayed;

[0060] 4) Spray the primer, spray 3 times, each time at an interval of 12 minutes;

[0061] 5) After spraying the primer, flash for 70 minutes and bake at 60°C for 2.5 hours;

[0062] 6) After the sprayed workpiece is cooled, detect the paint film thickness and adhesion;

[0063] 7) Grind the sprayed workpiece and clean the dust;

[0064] 8) Adjust the viscosity of the topcoat to 22s, and spray the topcoat for 3 times, with an interval of 12 minutes between each spraying, to ensure that the paint is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
glossaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention particularly relates to a method for finely adjusting the glossiness of a water-based matte finish paint by improving a spraying process, and belongs to the technical field of water-based coating spraying construction. The technical problem to be solved is paint film glossiness deviation caused by construction factors. The method for finely adjusting the glossiness of the water-basedmatte finish paint by improving the spraying process comprises the following process conditions: (1) the paint viscosity of the water-based epoxy finish paint spraying process is improved to be 20-23s; 2) the flash-drying time of the water-based epoxy finish paint is canceled, and 3) the finish paint is baked at 45-53 DEG C for 2-2.5 h. The problem of paint film glossiness deviation caused by construction factors is effectively solved by investigating the factors such as the drying mode, the flash-drying time and the paint viscosity, and the one-time delivery qualification rate of products is improved.

Description

technical field [0001] The invention belongs to the technical field of water-based paint spraying construction, and in particular relates to a method for finely adjusting the glossiness of a water-based matte finish paint by improving the spraying process. Background technique [0002] Paint film gloss, also known as specular gloss, refers to the ability of paint film to reflect light and is an important indicator of decorative coatings. Due to the advantages of water-based paint in terms of environmental protection and energy conservation, its output has increased year by year in recent years, and users have higher and higher requirements for the decorative performance of water-based paint. Water-based coatings are divided into bright water-based coatings, semi-matte water-based coatings and matte water-based coatings according to the gloss, and their applications are different. Glossy coatings are generally used outdoors, which can give people a full and bright color expe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D5/06B05B12/10B05D7/00B05D3/00B05D3/02
CPCB05D5/061B05B12/10B05D7/544B05D3/007B05D3/0254
Inventor 张芳芳高建疆吉星牟岩史淋丽
Owner 永济优耐特绝缘材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com