Bamboo fiber medical quick hemostatic gauze

A technology of hemostatic gauze and bamboo fiber, which is applied in the field of medical gauze, can solve the problems of insufficient hemostatic effect and slow wound healing, and achieve the effects of promoting rapid healing, promoting platelet adhesion, and improving hemostatic effect

Inactive Publication Date: 2019-11-12
吴礼高
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to design a kind of bamboo fiber medical rapid hemostatic gauze, to solve the insufficient hemostatic effect of the existing medical hemostatic gauze and the side effect of slow wound healing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo fiber medical quick hemostatic gauze
  • Bamboo fiber medical quick hemostatic gauze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of bamboo fiber medical rapid hemostatic gauze, preparation method comprises the following steps:

[0023] (1) Explosive treatment of bamboo fiber: Take 2.2kg of bamboo fiber, put it into a NaOH solution with a pH of 9~10 and soak it at room temperature for 12 hours. Put it into a sealed tank, add a large amount of water vapor to the sealed tank, and heat the inside of the sealed tank simultaneously, so that the bamboo fiber is treated at a pressure of 1.8 MPa for 30 minutes;

[0024] (2) Preparation of rapid hemostatic powder: Take 80g of chitosan and put it into 1.8kg of dilute sulfuric acid solution with a mass concentration of 12%, and add 100g of lauric aldehyde to the dilute sulfuric acid solution, heat up to 80°C and stir for 4h , then drop NaOH solution into the dilute sulfuric acid solution until the pH in the dilute sulfuric acid solution is 5~6, then add 55g of NaOH solution into the dilute sulfuric acid solution 2 SO 3 , after stirring for 3 hours, ...

Embodiment 2

[0028] A kind of bamboo fiber medical rapid hemostatic gauze, preparation method comprises the following steps:

[0029] (1) Explosive treatment of bamboo fiber: Take 2.6kg of bamboo fiber, put it into a NaOH solution with a pH of 9~10 and soak it for 12 hours at room temperature. Put it into a sealed tank, add a large amount of water vapor to the sealed tank, and heat the inside of the sealed tank at the same time, so that the bamboo fiber is treated at a pressure of 1.6MPa for 50 minutes;

[0030] (2) Preparation of rapid hemostatic powder: Take 80g of chitosan and put it into 1.8kg of dilute sulfuric acid solution with a mass concentration of 10%, and add 120g of myristic aldehyde into the dilute sulfuric acid solution, heat up to 80°C and heat and stir 4h, then add NaOH solution dropwise to the dilute sulfuric acid solution until the pH in the dilute sulfuric acid solution is 5~6, then add 60g of NaOH solution to the dilute sulfuric acid solution 2 SO3 , after stirring fo...

Embodiment 3

[0034] A kind of bamboo fiber medical rapid hemostatic gauze, preparation method comprises the following steps:

[0035] (1) Explosive treatment of bamboo fiber: Take 2.8kg of bamboo fiber and put it into Na with a pH of 9~10 2 CO 3 Soak in the solution at room temperature for 12 hours. When soaking, pay attention to immerse the bamboo fibers in the NaOH solution, then pick up and rinse with water until neutral and put them in a sealed tank. Then add a large amount of water vapor to the sealed tank and heat the inside of the sealed tank at the same time. Make bamboo fiber be processed 30min under the pressure of 1.8MPa;

[0036] (2) Preparation of rapid hemostatic powder: Take 60g of chitosan and put it into 1.6kg of dilute sulfuric acid solution with a mass concentration of 16%, and add 85g of decanal to the dilute sulfuric acid solution, heat up to 70°C and heat and stir for 2.5 h, then dropwise add NaOH solution in the dilute sulfuric acid solution until the pH in the dil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of hemostatic gauze, in particular to bamboo fiber medical quick hemostatic gauze. Preparation of the bamboo fiber medical quick hemostatic gauze comprisesthe four steps of bamboo fiber explosion processing, quick hemostatic powder preparation, bamboo fiber soaking processing and gauze preparation. According to the bamboo fiber medical quick hemostaticgauze, compared with existing hemostatic gauze, the hygroscopicity, the gas permeability and the antibacterial property are greatly improved, quick healing of wounds is advantageously achieved; and furthermore, the hemostatic time is shortened to below 95s from 160-170s, the hemostatic effect of medical gauze is greatly improved, tissue damage can be avoided in the hemostatic process, the side effects are avoided, a very important significance is achieved for saving lives of wounded personnel and stabilizing traumatic condition.

Description

technical field [0001] The invention relates to the technical field of medical gauze, in particular to a bamboo fiber medical rapid hemostatic gauze. Background technique [0002] Medical gauze is a common medical product used to bandage wounds of wounded patients. Existing medical gauzes can only clean and disinfect wounds, but cannot effectively stop bleeding on wounds, and their medical functions are single. Bleeding is one of the important causes of death in wartime, natural disasters or accidents. If timely and effective hemostasis can be performed on the wound, it is of great significance to save the lives of the wounded and stabilize the injury. [0003] Most of the existing gauze is woven from cotton fibers. From the characteristics of cotton fibers, cotton fibers are natural fibers with good water absorption and some inherent advantages. But bamboo itself not only has stronger hygroscopicity and hygroscopicity, but also has a unique substance called "bamboo kun" in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L15/40A61L15/28A61L15/26A61L15/18A61L15/44A61F13/00
CPCA61F13/00063A61F13/00987A61L15/18A61L15/26A61L15/28A61L15/40A61L15/44A61L2300/10A61L2300/418A61L2400/04C08L5/08C08L1/284
Inventor 吴礼高
Owner 吴礼高
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com