Preparation method and application of three-dimensional self-supporting nitrogen-doped carbon sodium ion negative electrode material

A nitrogen-doped carbon and negative electrode material technology, applied in the field of electrochemical power supply, can solve the problems of unsuitable preparation technology for industrial production, poor safety of carbon materials, poor cycle stability, etc., and achieves improved battery safety, low cost, and increased content Effect

Active Publication Date: 2019-11-05
HUBEI UNIV
View PDF13 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem solved by the present invention is to overcome the defects of existing carbon materials such as poor safety, poor cycle stability, high cost and unsuitable preparation process for industrialized production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of three-dimensional self-supporting nitrogen-doped carbon sodium ion negative electrode material
  • Preparation method and application of three-dimensional self-supporting nitrogen-doped carbon sodium ion negative electrode material
  • Preparation method and application of three-dimensional self-supporting nitrogen-doped carbon sodium ion negative electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Preparation of three-dimensional carbon anode materials

[0037] A method for preparing a three-dimensional self-supporting nitrogen-doped carbon-sodium ion negative electrode material, comprising the following steps:

[0038] (1) Preparation of ZIF-8: Take a certain amount of Zn(NO 3 ) 2 ·6H 2O was dissolved in 100ml of methanol to obtain solution A; a certain amount of composite ligand was dissolved in 100ml of methanol to obtain solution B, wherein the composite ligand was composed of a rigid ligand and a flexible ligand in a molar ratio of 1:1. The combination of rigid ligand (2,2-bipyridyl) and flexible ligand (1,2-dipyridylethane) can not only ensure the strength, prevent the collapse of holes, but also improve the flexibility of the material; take a certain amount Poly N-isopropylacrylamide was dissolved in 100ml methanol to obtain solution C; wherein, Zn(NO 3 ) 2 ·6H 2 O, the molar ratio of complex ligand and poly-N-isopropylacrylamide is 1:4:1, the so...

Embodiment 2

[0051] This embodiment is basically the same as Embodiment 1, the difference is:

[0052] A method for preparing a three-dimensional self-supporting nitrogen-doped carbon-sodium ion negative electrode material, comprising the following steps:

[0053] (1) Preparation of ZIF-8: Take a certain amount of Zn(NO 3 ) 2 ·6H 2 O was dissolved in 100ml of methanol to obtain solution A; a certain amount of composite ligand was dissolved in 100ml of methanol to obtain solution B, wherein the composite ligand was composed of a rigid ligand and a flexible ligand in a molar ratio of 1:1. The combination of rigid ligand (2,2-bipyridyl) and flexible ligand (1,2-dipyridylethane) can not only ensure the strength, prevent the collapse of holes, but also improve the flexibility of the material; take a certain amount Poly N-isopropylacrylamide was dissolved in 100ml methanol to obtain solution C; wherein, Zn(NO 3 ) 2 ·6H 2 O, the molar ratio of composite ligand and poly-N-isopropylacrylamide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and application of a three-dimensional self-supporting nitrogen-doped carbon sodium ion negative electrode material. The preparation method comprises the following steps: (1) preparation of ZIF-8; (2) electrostatic spinning preparation; (3) annealing and carbonizing. Reversible sodium intercalation and deintercalation can be realized, a slope type voltage behavior is presented, and the problems that a secondary battery anode material prepared by an existing method is low in improvement specific capacity, poor in stability and cycle performance, incapable of realizing sodium intercalation of graphite and the like are solved. The negative electrode material is a nitrogen-doped three-dimensional self-supporting carbon material, can be directly usedas an electrode, has no binder, is low in cost and simple in method, is suitable for large-scale production, and has application potential.

Description

technical field [0001] The invention belongs to the field of electrochemical power sources, and in particular relates to a preparation method and application of a three-dimensional self-supporting nitrogen-doped carbon-sodium ion negative electrode material. Background technique [0002] Due to its high energy density and good cycle stability, lithium-ion batteries have attracted much attention since they were proposed in 1970. In 1991, SONY Corporation industrialized them and became even more famous. However, the application of lithium has encountered a bottleneck due to the scarcity of crustal resources. Lithium is a limited resource, which, like oil, is unevenly distributed around the world. At this time, sodium, which is in the same main group as it, has attracted attention. In contrast, they have similar chemical properties, with a crustal abundance of up to 2.75% for sodium, much higher than 0.0065% for lithium, greatly reducing the cost. Compared with lithium resour...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/587H01M4/62H01M10/0525H01M10/054
CPCH01M4/587H01M4/62H01M10/0525H01M10/054H01M2004/021H01M2004/027Y02E60/10
Inventor 郑自建苏琪王正帮曾思远
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com