Anti-ultraviolet light soft warm fabric and preparation method thereof

An anti-ultraviolet and fabric technology, applied in the field of fabrics, can solve the problems of poor anti-ultraviolet performance, increase the thickness of the fabric, and low thermal performance, and achieve the effect of improving wearing comfort.

Inactive Publication Date: 2019-10-18
南通明富纺织品有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although traditional fabrics have enough styles for people to choose from, traditional fabrics still have shortcomings such as low heat retention and poor UV resistance.
The traditional thermal insulation material is wool fabric, which will cause discomfort when it comes into direct contact with the human body. In order to improve the thermal insulation effect of traditional wool fabrics, the specific method is to increase the thickness of the fabric. Although this improves the thermal insulation performance, it also increases the thickness of the fabric. , so the application effect is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-ultraviolet light soft warm fabric and preparation method thereof
  • Anti-ultraviolet light soft warm fabric and preparation method thereof
  • Anti-ultraviolet light soft warm fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] A method for preparing an anti-ultraviolet light and warm fabric, comprising the following steps:

[0051] 1) the inner layer yarn and the outer layer yarn are double-sided knitted by a double-sided knitting machine to obtain a double-sided fabric gray cloth;

[0052] 2) Degreasing, dyeing, and padding the gray cloth with an anti-ultraviolet treatment solution to obtain the anti-ultraviolet soft and warm fabric.

Embodiment 1

[0055] A kind of anti-ultraviolet light and warm fabric, the fabric is a double-sided weave structure, including the inner layer yarn and the outer layer yarn; Anti-ultraviolet treatment liquid for gray cloth padding; the inner layer yarn is made of high-twist yarn, and the outer layer is made of soft-feeling siro-spun yarn;

[0056] In parts by weight, siro-spun yarns include the following parts by weight:

[0057]

[0058] Regenerated fibers include 75wt% acetate fiber and 25wt% soybean protein fiber; the thickness of the inner yarn is 22SS, and the thickness of the outer yarn is 4S; the twist of the inner yarn is 68 twists / 10cm, and the outer The twist of the layer yarn is 48 twists / 10 cm.

[0059] By parts by weight, high-twisted yarns include yarns of the following parts by weight:

[0060] 60 parts by weight of cotton fiber;

[0061] 13 parts by weight of Thermogear fiber;

[0062] 2 parts by weight of polyacrylonitrile fiber.

[0063] UV treatment fluid includes t...

Embodiment 2

[0069] A kind of anti-ultraviolet light and warm fabric, the fabric is a double-sided weave structure, including the inner layer yarn and the outer layer yarn; Anti-ultraviolet treatment liquid for gray cloth padding; the inner layer yarn is made of high-twist yarn, and the outer layer is made of soft-feeling siro-spun yarn;

[0070] In parts by weight, siro-spun yarns include the following parts by weight:

[0071]

[0072] Regenerated fibers include 78wt% acetate fiber and 22wt% soybean protein fiber; the thickness of the inner yarn is 25S, and the thickness of the outer yarn is 7S; the twist of the inner yarn is 72 twists / 10cm, the outer The twist of the layer yarn is 50 twists / 10 cm.

[0073] By parts by weight, high-twisted yarns include yarns of the following parts by weight:

[0074] Cotton fiber 64 parts by weight;

[0075] 14 parts by weight of Thermogear fiber;

[0076] 3 parts by weight of polyacrylonitrile fiber.

[0077] UV treatment fluid includes the fol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-ultraviolet light soft warm fabric which is of double-side weave structure and which comprises inner yarns and outer yarns. The inner yarns and the outer yarns are subjected to double-side knitting to obtain a double-side fabric body; the double-side fabric body is subjected to padding with an anti-ultraviolet treating liquid; the inner yarns are high twist yarns; the outer yarns are soft siro-spun yarns. The siro-spun yarns are made with, by weight 60-70 parts of cotton fibers, 15-17 parts of regenerated fibers and 3-6 parts of banana fibers. The anti-ultraviolet light soft warm fabric has the advantages that the double-side fabric body is subjected to padding with the anti-ultraviolet treating liquid, the ingredients of the anti-ultraviolet treating liquidcoordinatively promote one another through compatibility, and therefore, the prepared fabric has good ultraviolet resistance and better wearing comfort.

Description

technical field [0001] The invention relates to a fabric, in particular to an anti-ultraviolet soft and warm fabric and a preparation method thereof. Background technique [0002] In recent years, with the continuous development of fabrics, various styles of fabrics have appeared in the market to meet people's needs for different fabrics. At present, although traditional fabrics have enough styles for people to choose from, traditional fabrics still have shortcomings such as low heat retention performance and poor UV resistance. The traditional thermal insulation material is wool fabric, which will cause discomfort when it comes into direct contact with the human body. In order to improve the thermal insulation effect of traditional wool fabrics, the specific method is to increase the thickness of the fabric. Although this improves the thermal insulation performance, it also increases the thickness of the fabric. , so the application effect is not ideal. [0003] It can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04B1/16D04B1/14D02G3/04D06B9/04D06M13/358D06M13/342D06M13/262D06M15/643D06M13/335D06M101/06D06M101/12D06M101/28
CPCD04B1/16D04B1/14D02G3/04D06B9/04D06M13/358D06M13/342D06M13/262D06M15/643D06M13/335D06M16/00D10B2201/28D10B2211/26D10B2201/02D10B2321/10D06M2200/25D06M2200/50D06M2101/06D06M2101/12D06M2101/28
Inventor 陈飞
Owner 南通明富纺织品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap