Preparation method of Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material

A composite wave absorbing material, graphite carbon technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of harsh reaction conditions, waste of time and raw materials, etc., and achieve the effect of good electromagnetic wave absorption performance

Active Publication Date: 2019-09-27
DALIAN UNIV OF TECH
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Not only waste of time and raw materials, but also harsh reaction conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material
  • Preparation method of Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material
  • Preparation method of Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Example 1 Preparation of Ni-Co alloy embedded N-doped graphite-like carbon capsule composite absorbing material Air@NCs€Ni-Co-1

[0026] 1) Preparation of Ni(OH) 2 / ZIF-67-1

[0027] 1.1) Ni(OH) 2 Preparation of methanol solution

[0028] NiCl 2 ·6H 2 The aqueous solution of O was added to the NaOH solution, ultrasonically stirred for 2 hours, washed with water and centrifuged until the solution was neutral, and then dried to prepare a certain concentration of Ni(OH) 2 Methanol solution, the concentration is 40mg / mL.

[0029] 1. Ni(OH) 2 / Preparation of ZIF-67-1

[0030] 1.2) Mix 0.6g PVP, 1g CoCl 2 ·6H 2 O, 40mL methanol magnetic stirring 10min is recorded as solution 1; Measure the Ni(OH) of 0.5mL 2 The methanol solution was dispersed in 2.63g of 40mL dimethylimidazole methanol solution, ultrasonically stirred for 10min and recorded as solution 2, solution 2 was added dropwise to solution 1, after mechanical stirring for 2h, after standing at room temperatu...

Embodiment 2

[0041] Example 2 Preparation of Ni-Co alloy embedded N-doped graphite-like carbon capsule composite absorbing material Air@NCs€Ni-Co-2

[0042] 1) Preparation of Ni(OH) 2 / ZIF-67-2

[0043] 1.1) Ni(OH) 2 The preparation of methanol solution: with embodiment 1.

[0044] 1.2) Preparation of Ni(OH) 2 / ZIF-67-2

[0045] 0.6g PVP, 1.6g CoCl 2 ·6H 2 O, 40mL methanol magnetic stirring for 10min is recorded as solution 1; measure 0mL Ni(OH) 2 The methanol solution was dispersed in 2.63g of 40mL dimethylimidazole methanol solution, ultrasonically stirred for 10min and recorded as solution 2, solution 2 was added dropwise to solution 1, after mechanical stirring for 4h, after standing at room temperature, it was washed with ethanol and centrifuged. Vacuum drying gives the intermediate Ni(OH) 2 / ZIF-67-2.

[0046] 2) Preparation of Ni(OH) 2 / ZIF-67@PDA-2

[0047] 0.2g Ni(OH) 2 / ZIF-67, 0.4g dopamine hydrochloride and 0.4g THAM were ultrasonically stirred in an ice-water bath ...

Embodiment 3

[0050] Example 3 Preparation of Ni-Co alloy embedded N-doped graphite-like carbon capsule composite absorbing material Air@NCs€Ni-Co-3

[0051] 1) Preparation of Ni(OH) 2 / ZIF-67-3

[0052] 1.1) Preparation of Ni(OH) 2 Methanol solution: with embodiment 1.

[0053] 1.2) Preparation of Ni(OH) 2 / ZIF-67-3

[0054] 0.6g PVP, 0.5g CoCl 2 ·6H 2 O, 40mL methanol magnetic stirring 10min is recorded as solution 1; Measure the Ni(OH) of 2mL 2 The methanol solution was dispersed in 2.63g of 40mL dimethylimidazole methanol solution, ultrasonically stirred for 10min and recorded as solution 2, solution 2 was added dropwise to solution 1, after mechanical stirring for 2h, after standing at room temperature, it was washed with ethanol and centrifuged. Vacuum drying gives the intermediate Ni(OH) 2 / ZIF-67-3.

[0055] 2)Ni(OH) 2 / Preparation of ZIF-67@PDA-3;

[0056] 0.2g Ni(OH) 2 / ZIF-67, 0.4g dopamine hydrochloride and 0.32g THAM were ultrasonically stirred in an ice-water bath...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Return lossaaaaaaaaaa
Bandwidthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of an Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material, and belongs to the field of synthesis of composite materials. The method is characterized in that Ni(OH)2 particles are designed and synthesized, an Ni(OH)2 methanol solution is prepared, and Ni(OH)2 / ZIF-67 is synthesized by adding a certain quantity of the Ni(OH)2 solution during the synthesis of ZIF-67; the Ni(OH)2 / ZIF-67 is taken as a template, trishydroxymethylaminomethane is taken as a buffer agent, in situ polymerization of dopamine hydrochloride is carried out on the surface to form Ni(OH)2 / ZIF-67@PDA, the ZIF template is subjected to self-etching during dopamine coating, and a hollow dodecahedral capsule is formed; high-temperature calcination and aftertreatment are carried out to prepare the Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material (Air@NCs euro Ni-Co). The synthetic method provided by the invention has universality, and N-doped graphite carbon capsule composite wave-absorbing materials embedded with different alloys (Fe-Co, Co-Cu, Co-Zn, FeCoNi, FeCoZn ternary alloy, and the like) can be synthesized. The Ni-Co alloy embedded N-doped graphite carbon capsule composite wave-absorbing material prepared by a three-step method has good wave-absorbing properties.

Description

technical field [0001] The invention belongs to the field of composite material synthesis, and relates to a novel preparation method of a Ni-Co alloy embedded N-doped graphite-like carbon capsule composite wave-absorbing material. Background technique [0002] With the improvement of people's living standards and the continuous updating of various electronic equipment, electromagnetic radiation is flooding around us. Electromagnetic pollution has become another major pollution source after water pollution, air pollution, and noise pollution, seriously endangering human beings. health. In addition, modern warfare in the military has been oriented towards informationization, and stealth technology is becoming more and more important. Electromagnetic wave absorbing materials are the core of radar stealth technology, so absorbing materials have become a hot spot in military development. [0003] At present, people are paying attention to composite absorbing materials, because ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K3/00
CPCC09K3/00
Inventor 陈平邱红芳朱晓宇于祺熊需海王静
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com