Method for modifying PET obtained by depolymerization of polyester waste textiles, purification and polymerization and extrusion PA6
A polyester and modified technology, applied in the field of new materials for alloy extrusion, can solve the problems of landfill or incineration, inability to directly reprocess, waste of land resources and second pollution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0009] A method of chemically depolymerizing and purifying polymerized PET with polyester waste textiles according to the present invention, and PA6 extruded material, modified into an alloy material method is implemented according to the following process procedures:
[0010] Depolymerize polyester waste textiles with glycerin residue heated to 260-280 degrees, filter the dregs in the solution, decolorize and purify to obtain liquid PET. Prepare PET and PA6 extrusion grade raw materials according to the following parts by weight.
[0011] PET 50 copies
[0012] PA6 45 copies
[0013] Compatibilizer 5 parts
[0014] Test results
[0015]
[0016] The above-mentioned prepared components and parts by weight are mixed, extruded and granulated, and a new alloy material of PET and PA6 extrusion grade is obtained.
Embodiment 2
[0018] With reference to the method of Example 1, each component and parts by weight were prepared in the following ratios to prepare PET / PA6 extrusion grade raw materials.
[0019] PET 48 servings
[0020] PA6 48 copies
[0021] Compatibilizer 4 parts
[0022] Test results
[0023]
[0024] The above-mentioned prepared components and parts by weight are mixed, extruded and granulated, and a new alloy material of PET and PA6 extrusion grade is obtained.
Embodiment 3
[0026] Referring to Examples 1 and 2, each component and parts by weight were prepared in the following proportions to prepare PET / PA6 extrusion grade raw materials.
[0027] PET 45 parts
[0028] PA6 50 copies
[0029] Compatibilizer 5 parts
[0030] Test results
[0031]
[0032] The above-mentioned prepared components and parts by weight are mixed, extruded and granulated, and a new alloy material of PET and PA6 extrusion grade is obtained.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com