Method for chemically depolymerizing polyester waste textiles to produce PET/PP black alloy color master batches

A technology for waste textiles and color masterbatches, applied in the direction of plastic recycling, recycling technology, etc., can solve the problems of inability to directly reprocess, waste of land resources, secondary pollution, landfill or incineration, etc.

Inactive Publication Date: 2019-08-06
PLASTIC UNION NEW MATERIAL TECH HUBEI
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As we all know, except for a very small amount of existing waste textiles that are used by people using physical methods, they can neither be reu...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for chemically depolymerizing polyester waste textiles to produce PET/PP black alloy color master batches
  • Method for chemically depolymerizing polyester waste textiles to produce PET/PP black alloy color master batches
  • Method for chemically depolymerizing polyester waste textiles to produce PET/PP black alloy color master batches

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A kind of chemical depolymerization of polyester waste and old textiles according to the present invention, the method for processing PET / PP black alloy color masterbatch, implements according to following process procedure:

[0010] Depolymerize polyester waste textiles with glycerin residue heated to 260-280 degrees, and filter the dregs in the solution to obtain liquid PET. Prepare PET / PP blown film type black alloy masterbatch according to the following parts by weight.

[0011] PET 20 copies

[0012] Blown film grade PP 40 parts

[0013] Black carbon black 30 parts

[0014] Compatibilizer 10 parts

[0015] Test results

[0016]

[0017] Mix the above prepared components and parts by weight, extrude and granulate, and obtain PET and PP black alloy blown film type

[0018] Masterbatch.

Embodiment 2

[0020] With reference to the method of Example 1, each component and parts by weight were prepared in the following proportions to prepare a PET / PP drawing-type black masterbatch.

[0021] PET 30 parts

[0022] Drawing grade PP 30 parts

[0023] Black carbon black 30 parts

[0024] Compatibilizer 10 parts

[0025] Test results

[0026]

[0027] Mix the above prepared components and parts by weight, extrude and granulate to obtain PET and PP black alloy wire drawing color masterbatch.

Embodiment 3

[0029] Referring to Examples 1 and 2, each component and parts by weight were prepared in the following proportions to prepare a PET / PP injection molding black masterbatch.

[0030] PET 40 copies

[0031] Injection grade PP 20 parts

[0032] Black carbon black 30 parts

[0033] Compatibilizer 10 parts

[0034] Test results

[0035]

[0036] Mix the above prepared components and parts by weight, extrude and granulate to obtain PET and PP black alloy injection molding color masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for chemically depolymerizing polyester waste textiles to produce PET/PP black alloy color master batches. The method comprises the following steps: heated glycerin residues with a temperature of 260-280 DEG C are used to depolymerize the polyester waste textiles, dregs in the obtained solution are filtered out completely, black carbon black, a compatilizer and a PP raw material for film blowing, wire drawing and injection molding of different models are added, and the obtained mixture is uniformly mixed, and undergoes extruding granulation to obtain the special PET and PP black alloy color master batches for film blowing, wire drawing and injection molding.

Description

technical field [0001] The invention discloses a method for chemically depolymerizing polyester waste textiles and processing PET / PP black alloy masterbatch. [0002] technical background [0003] As we all know, except for a very small amount of existing waste textiles that are used by people using physical methods, they can neither be reused nor directly reprocessed after recycling, and can only be landfilled or incinerated. Not only wasting land resources but also causing secondary pollution. Contents of the invention [0004] The purpose of the present invention is in order to overcome the defective of above-mentioned background technology, fundamentally completely eliminates this backward treatment mode, completely solves the second pollution. [0005] In order to achieve the above object, the technical solution of the present invention is as follows: [0006] The invention discloses a method for our factory to produce PET / PP black alloy color masterbatch by chemical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J3/22C08L67/02C08L23/12C08K3/04C08J11/24
CPCC08J3/226C08J11/24C08J2367/02C08J2423/12C08J2467/02C08K3/04Y02W30/62
Inventor 邓忠权邓军邓丽
Owner PLASTIC UNION NEW MATERIAL TECH HUBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap