Duplex stainless steel and manufacturing method thereof

A technology of duplex stainless steel and manufacturing method, applied in the direction of manufacturing tools, furnaces, heat treatment equipment, etc., to achieve the effect of cheap manufacturing and excellent resistance to carbon dioxide gas corrosion

Active Publication Date: 2021-07-23
JFE STEEL CORP
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, in the technology described in Patent Document 1, the yield strength can only reach a maximum level of about 80 ksi, and there is a problem that it can only be applied to some steel pipes as oil country tubular goods.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Duplex stainless steel and manufacturing method thereof
  • Duplex stainless steel and manufacturing method thereof
  • Duplex stainless steel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0125] Hereinafter, the present invention will be described by way of examples. In addition, this invention is not limited to the following Example.

[0126] In this example, the molten steel with the composition shown in Table 1 was smelted using a converter, cast into a billet (steel pipe raw material) by continuous casting, and the steel pipe raw material was heated at 1150 to 1250°C, and then, by using a heating model The hot working of the seamless rolling mill was performed to produce a seamless steel pipe having an outer diameter of 83.8 mm x a wall thickness of 12.7 mm. It should be noted that the seamless steel pipe was air-cooled after the pipe production.

[0127] The obtained seamless steel pipes were subjected to a solution heat treatment in which heating was performed under the conditions shown in Table 2, followed by cooling. Then, an aging heat treatment of heating under the conditions shown in Table 2 and then air cooling was further performed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides a duplex stainless steel with excellent corrosion resistance having excellent carbon dioxide gas corrosion resistance, excellent sulfide stress corrosion cracking resistance and excellent sulfide stress cracking resistance. This duplex stainless steel has the following composition, containing C: 0.03% or less, Si: 1.0% or less, Mn: 0.10 to 1.5%, P: 0.030% or less, S: 0.005% or less, Cr: 20.0 to 30.0% in mass % , Ni: 5.0-10.0%, Mo: 2.0-5.0%, Cu: 2.0-6.0%, N: less than 0.07%, and contain Al: 0.05-1.0%, Ti: 0.02-1.0%, Nb: 0.02 ~1.0% of one or more types, and the balance is composed of Fe and unavoidable impurities. The structure of the duplex stainless steel has a volume ratio of 20-70% austenite phase, 30-80% the ferrite phase.

Description

technical field [0001] The present invention relates to a duplex stainless steel suitable for use in oil wells and gas wells of crude oil or natural gas (hereinafter also simply referred to as oil wells) and a method for producing the same. The duplex stainless steel of the present invention can be suitable for use as a suitable stainless steel seamless steel pipe for oil wells, which has high strength and corrosion resistance, especially in the presence of carbon dioxide gas (CO 2 ) and chloride ions (Cl - ) and high temperature extremely severe corrosion resistance to carbon dioxide gas corrosion, and hydrogen sulfide (H 2 S) is excellent in high temperature sulfide stress corrosion cracking resistance (SCC resistance) and sulfide stress cracking resistance (SSC resistance) at room temperature, respectively. Background technique [0002] In recent years, from the standpoint of rising crude oil prices and the prospect of depletion of oil resources in the near future, deep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C22C38/60C21D6/00C21D8/10C21D9/08C22C38/50
CPCC21D9/08C22C38/50C22C38/60C22C38/001C22C38/004C22C38/02C22C38/04C22C38/42C22C38/44C22C38/46C22C38/48C22C38/52C22C38/54C21D6/004C21D8/105C21D2211/001C21D2211/005C21D6/008C21D9/085C22C38/06
Inventor 江口健一郎柚贺正雄
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com