UV-resistant BMC material used outdoors and preparation method of material

A UV-resistant, outdoor technology, applied in the field of BMC materials, can solve problems such as unfavorable promotion and application, and achieve the effects of good storage, good compatibility, increased surface finish and aesthetics

Inactive Publication Date: 2019-08-20
绍兴金创意塑化电器有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the new weather-resistant resins, weather-resistant pigments, ultraviolet light absorbers, special process additives and other materials used in it are not conducive to the popularization and application of existing common BMC materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV-resistant BMC material used outdoors and preparation method of material
  • UV-resistant BMC material used outdoors and preparation method of material
  • UV-resistant BMC material used outdoors and preparation method of material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4

[0026] A UV-resistant BMC material for outdoor use, including unsaturated resin of 4 mass ratio components as shown in the following table, low shrinkage resin, aluminum hydroxide, calcium carbonate, curing agent, glass fiber, anti-UV agent, mold release agent , pigments, inhibitors.

[0027] A method for making an ultraviolet-resistant BMC material for outdoor use, comprising the steps of:

[0028] Step 1: Add resin, curing agent, anti-UV agent, release agent, and pigment into the dispersion tank, disperse and stir for 15-25 minutes, and obtain a uniformly mixed liquid.

[0029] Step 2: Add calcium carbonate and aluminum hydroxide into the kneader and stir for 10-20 minutes to obtain a uniformly stirred powder.

[0030] Step 3: Add the liquid in Step 1 to the powder in Step 2, and stir in a kneader for 10-30 minutes to obtain a uniformly mixed paste;

[0031] Step 4, evenly add glass fiber to the paste in step 3, stir for 5-15 minutes, and obtain a mixed material product. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a UV-resistant bulk moulding compound (BMC) material used outdoors. The material comprises resin, aluminum hydroxide, calcium carbonate, a curing agent, glass fibers and an anti-UV agent, wherein the resin is unsaturated resin and low-shrinkage resin, and the anti-UV agent is a benzoic acid anti-UV agent or a benzotriazole anti-UV agent. The invention also provides a preparation method of the ultraviolet-resistant BMC material used outdoors. According to the method provided by the invention, after analysis comparison and screening tests of current anti-UV agents, the benzoic acid or benzotriazole anti-UV agent is added into a current common BMC material, so that the BMC material has good compatibility with the unsaturated resin and can be colored, and the propertiesand forming of the material are not affected; and the product has a high-efficiency light stability effect, and the characteristics of no toxicity, non-flammable performance, non-explosive performance, corrosion resistance and good storage performance.

Description

technical field [0001] The invention belongs to the technical field of BMC materials, in particular to an outdoor UV-resistant BMC material and a manufacturing method. Background technique [0002] BMC material (bulk molding compound), that is, unsaturated polyester glass fiber reinforced molding compound, is a kind of thermosetting material mainly composed of resin, filler, glass fiber, curing agent, etc. through physical mixing, which can be applied to compression, injection , transmission and other thermoforming processes, the products have the characteristics of high mechanical strength, high temperature resistance, smooth surface, flame retardant, arc resistance, etc. Its excellent mechanical and electrical properties make it widely used in automobile, construction, electrical appliances, instrumentation and other industries Applications. [0003] However, after BMC products are applied to outdoor products, many performance defects are exposed, the more important ones ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/06C08L63/10C08L25/06C08L33/12C08L31/04C08L23/08C08L21/00C08L23/06C08L101/00C08K13/04C08K3/22C08K3/26C08K7/14C08K5/3475
CPCC08K2003/2227C08K2003/265C08L63/10C08L67/06C08L2201/08C08L25/06C08L33/12C08L31/04C08L23/08C08L21/00C08L23/06C08L101/00C08K13/04C08K3/22C08K3/26C08K7/14C08K5/3475
Inventor 杨永林霍飞明杨智凯陶冬芳
Owner 绍兴金创意塑化电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More