Life cultivation and health care composite and preparation method thereof

A composite material and material technology, which is applied in special materials for cooking utensils, water/sewage treatment with added substances, etc., can solve the problems of increasing production cost and production difficulty, poor production convenience, melting of elemental substances, and large differences in gasification temperature, etc. Achieve the effect of avoiding excessive intake, good mechanical strength and high temperature resistance, reducing production cost and production difficulty

Inactive Publication Date: 2019-07-26
杭州鼎好新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] It is very difficult to smelt all the elements with trace elements. For example, high-purity elements require special storage methods, and it is necessary to avoid oxidation and moisture.
Moreo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Life cultivation and health care composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method of a health care composite material, the specific steps are as follows:

[0030] (1) Add calcium nitrate and sodium phosphate to water, mix well, add zinc nitrate, selenium dioxide, and copper oxalate, heat up to 80°C for the first time, keep the temperature for 12 hours, filter the solid, dry, pulverize, and inert gas Under protection, the temperature was raised to 340°C for the second time, stirred and kept for 2 hours to obtain a composite material;

[0031] (2) The high-purity iron is melted into molten iron, and magnesium phosphate and the composite material obtained in step (1) are added to the molten iron while stirring to obtain a high-temperature mixture;

[0032] (3) Cool the high-temperature mixture to 800°C and let it stand for 2 hours to obtain the cooling mixture;

[0033] (4) Under the protection of inert gas, the cooling mixture is injected into the mold, and formed to obtain a billet;

[0034] (5) Homogenization treatment, multipl...

Embodiment 2

[0043] A preparation method of a health care composite material, the specific steps are as follows:

[0044] (1) Add calcium nitrate and sodium phosphate into water, mix well, add zinc nitrate, selenium dioxide, and copper oxalate, heat up to 90°C for the first time, keep it for 15 hours, filter the solid, dry, pulverize, and inert gas Under protection, the temperature was raised to 350°C for the second time, stirred and kept for 3 hours to obtain a composite material;

[0045] (2) The high-purity iron is melted into molten iron, and magnesium phosphate and the composite material obtained in step (1) are added to the molten iron while stirring to obtain a high-temperature mixture;

[0046] (3) Cool the high-temperature mixture to 900°C and let it stand for 3 hours to obtain the cooling mixture;

[0047] (4) Under the protection of inert gas, the cooling mixture is injected into the mold, and formed to obtain a billet;

[0048] (5) Homogenization treatment, multiple cold roll...

Embodiment 3

[0057] A preparation method of a health care composite material, the specific steps are as follows:

[0058] (1) Add calcium nitrate and sodium phosphate into water, mix well, add zinc nitrate, selenium dioxide, and copper oxalate, heat up to 80°C for the first time, keep it for 15 hours, filter the solid, dry, pulverize, and inert gas Under protection, the temperature was raised to 340°C for the second time, stirred and kept for 3 hours to obtain a composite material;

[0059] (2) The high-purity iron is melted into molten iron, and magnesium phosphate and the composite material obtained in step (1) are added to the molten iron while stirring to obtain a high-temperature mixture;

[0060] (3) Cool the high-temperature mixture to 800°C and let it stand for 3 hours to obtain the cooling mixture;

[0061] (4) Under the protection of inert gas, the cooling mixture is injected into the mold, and formed to obtain a billet;

[0062] (5) Homogenization treatment, multiple cold roll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a life cultivation and health care composite and a preparation method thereof. Calcium nitrate, sodium phosphate, zinc nitrate, selenium dioxide, cupric oxalate, magnesium phosphate and high-purity iron are used as raw materials. Calcium nitrate and sodium phosphate are added into water at first and mixed, then zinc nitrate, selenium dioxide and cupric oxalate are added, still standing is conducted after primary temperature increase, coprecipitating occurs in the formation process of calcium phosphate, secondary temperature increase and stirring are conducted under inert gas shielding after drying, and a composite material is obtained; then magnesium phosphate and the composite material are added into molten iron formed by melting high-purity iron, and a high-temperature mixture is obtained; and finally, the composite product is obtained through cooling, mold forming and post-treatment. Trace elements such as calcium, zinc, selenium, copper, magnesium and iron can be precipitated during use of the product, human health is benefited, human immunity is improved, the prevalence rate of shortage of trace elements is lowered, and the good health care effect is achieved.

Description

technical field [0001] The invention relates to the field of composite material processing, in particular to a health care composite material and a preparation method thereof. Background technique [0002] Aluminum or aluminum alloy products such as aluminum pots, aluminum pots, and aluminum basins will cause aluminum elements to enter the human body, resulting in excessive aluminum. After the human body ingests aluminum, only 10%-15% can be excreted outside the body, and most of it will accumulate in the body. A variety of proteins, enzymes and other important components of the human body are combined to affect a variety of biochemical reactions in the body. Long-term intake can damage the brain, lead to dementia, and may also cause anemia, osteoporosis and other diseases, especially for the elderly and children with weak body resistance Harmful to pregnant women, can cause growth retardation in children, dementia in the elderly, and ingestion by pregnant women can affect f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C33/04C22C38/16A47J36/02C02F1/68
CPCA47J36/02C02F1/68C22C33/04C22C38/002C22C38/16
Inventor 李可平
Owner 杭州鼎好新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap