Acrylic acid outer wall latex paint and preparation process thereof

A preparation process, pure acrylic emulsion technology, applied in the field of acrylic exterior wall latex paint and its preparation process, can solve the problems of aging, poor application effect of exterior wall latex paint, etc., achieve reduced cracks, good anti-ultraviolet performance, and improved physical and chemical properties performance effect

Active Publication Date: 2019-07-26
上海雷鸟涂料有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problem in the prior art that the exterior wall latex paint coating is easily affected by the external environment and causes aging, resulting in poor overall application effect of the exterior wall latex paint, the first purpose of the present invention is to provide an acrylic exterior wall latex paint, By adding pitaya seed extract and making it cooperate with kaolin to solve the above technical problems, it is not easy to age due to the influence of the external environment, and has a good application effect as a whole

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic acid outer wall latex paint and preparation process thereof
  • Acrylic acid outer wall latex paint and preparation process thereof
  • Acrylic acid outer wall latex paint and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Embodiment 1: a kind of acrylic exterior wall latex paint, each component and its corresponding parts by weight are shown in Table 1, and are prepared through the following steps:

[0053] Step 1, prepare the slurry, fully stir and mix the corresponding parts by weight of water, pure acrylic acid emulsion, ethylene glycol and hydroxyethyl cellulose in a mixing tank, the stirring speed is 650rpm, and the time is 50min, to obtain the slurry;

[0054] Step 2, mixing auxiliary agents, polydimethylsiloxane, titanium dioxide, ground calcium carbonate, Tex film forming agent, PT86 antifungal agent, kaolin, sodium hydroxide and lauryl sulfuric acid in corresponding parts by weight Add sodium into the mixing tank containing the slurry, keep the stirring speed at 900rpm, and the time is 40min to obtain the mixture;

[0055] Step 3, finished paint storage, adding dragon fruit seed extract and wollastonite powder into the mixture, stirring and mixing at a stirring speed of 400 rpm ...

Embodiment 2-8

[0060] Embodiment 2-8: an acrylic exterior wall latex paint, the difference from embodiment 1 is that each component and its corresponding parts by weight are shown in Table 1.

[0061] Each component and parts by weight thereof in table 1 embodiment 1-8

[0062]

[0063]

Embodiment 9

[0064] Embodiment 9: a kind of acrylic exterior wall latex paint, the difference with embodiment 1 is that step 2 is specifically set as, mixing auxiliary agent, the polydimethylsiloxane of corresponding parts by weight is 1.2 parts, 110 Parts of titanium dioxide, 260 parts of heavy calcium carbonate, 5 parts of Tex film-forming agent, 0.8 parts of PT86 antifungal agent, 95 parts of kaolin, 1.2 parts of sodium acetate and 4.5 parts of sodium lauryl sulfate Into the mixing tank containing the slurry, keep the stirring speed at 900 rpm for 40 minutes to obtain a mixture.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses acrylic acid outer wall latex paint and a preparation process thereof, relates to the technical field of paint, and solves the problems that due to the fact that an outer walllatex paint coating layer is easily aged under the effect of an external environment, the overall application effect of the outer wall latex paint is not good. The acrylic acid outer wall latex paintcomprises, by weight, 320-350 parts of water, 2-5 parts of hydroxyethyl cellulose, 8-12 parts of ethylene glycol, 1.2-1.6 parts of polydimethyl siloxane, 90-110 parts of titanium dioxide, 95-115 partsof kaolin, 4-5 parts of wollastonite powder, 260-280 parts of ground calcium carbonate, 170-190 parts of pure acrylic emulsion, 3-5 parts of Tex film-forming agent, 0.8-1 part of PT86 mildew preventive, 0.8-1.2 parts of neutralizer, 4.5-7.5 parts of dispersing agent and 1.2-2.4 parts of pitaya seed extract. The acrylic acid outer wall latex paint has the advantages that the coating layer after the acrylic acid outer wall latex paint is used is good in stability, the coating layer cannot be easily aged under the effect of the external environment, and the overall application effect of the acrylic acid outer wall latex paint is good.

Description

technical field [0001] The invention relates to the technical field of paints and coatings, more specifically, it relates to an acrylic exterior wall latex paint and a preparation process thereof. Background technique [0002] Glue paint is a water-dispersible paint. It is a paint made of synthetic resin emulsion as the base material. After the filler is ground and dispersed, various additives are added. It is also a large class of synthetic resin emulsion paint represented by acrylate copolymer emulsion. . [0003] In the Chinese invention patent whose application publication number is CN108641518A, a kind of exterior wall latex paint is disclosed. In parts by weight, 200-250 parts of acrylic emulsion, 200-220 parts of modified polyurethane emulsion, 80-100 parts of water , 8-12 parts of dispersant, 20-25 parts of propylene glycol, 140-160 parts of mixed filler, 20-40 parts of additive, 20-50 parts of pigment and filler, 8-12 parts of melamine and 15-20 parts of hydroxypro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/02C09D7/61C09D7/63C09D7/65
CPCC08K2003/2241C08K2201/011C08K2201/014C08L2205/035C08L2205/16C09D5/024C09D5/028C09D133/04C08L1/02C08K13/02C08K3/346C08K5/005C08K5/1345C08K3/22C08K5/053C08K3/36
Inventor 杨博文
Owner 上海雷鸟涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com