Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Square steel forging and pressing technology

A technology, steel forging technology, applied in the direction of metal extrusion, manufacturing tools, metal processing equipment, etc., can solve the problems of multiple hot forging processes, decarburization and burning, poor workpiece precision, etc., to reduce the number of drawing times, reduce Effect of heat stress and high yield

Inactive Publication Date: 2019-07-09
青岛金越隆机械有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are many hot forging processes, the precision of the workpiece is poor, the surface is not smooth, and the forging is prone to oxidation, decarburization and burning.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The invention provides a square steel forging process, which comprises the following steps:

[0033] 1) prepare square steel heating curve figure, the abscissa of described square steel heating curve figure is heating time, and ordinate is heating temperature:

[0034] 1.1) Select different steel types and obtain their own heating characteristics;

[0035] 1.2) According to the heating characteristics of different steel grades obtained in step 1.1), the furnace inlet temperature, initial forging temperature and furnace discharge temperature of different steel grades are determined;

[0036] 1.3) Determine the heating time of different steel types during forging;

[0037] 1.4) Draw the heating curves of different steel types with the abscissa as the heating time and the ordinate as the heating temperature.

[0038] 2) According to the square steel heating curve obtained in step 1), the square steel is subjected to heat treatment:

[0039] 2.1) The furnace temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a square steel forging and pressing technology. The square steel forging and pressing technology comprises the following steps that firstly, a square steel heating curve chartis prepared, the x-coordinate of the square steel heating curve chart is the heating time, and the y-coordinate of the square steel heating curve chart is the heating temperature; secondly, the square steel is subjected to heating treatment according to the square steel heating curve chart obtained in the first step; and thirdly, the heated square steel is subjected to upsetting and drawing-out treatment. The square steel forging and pressing technology is provided, the technology precision is high, the surface quality is good, and the casting technology is simple and reliable.

Description

technical field [0001] The invention belongs to the field of metal forging, and relates to a square steel forging process. Background technique [0002] During the forging process, forging can compact or weld defects such as shrinkage cavities, shrinkage porosity, voids, bubbles and cracks in the as-cast metal structure, and can also refine grains and break inclusions, so as to obtain a certain forging flow. line tissue. In actual production, various forgings are often used to produce various important and heavy-duty machine parts or blanks, such as main shafts and gears of machine tools, connecting rods of internal combustion engines, hooks of cranes, etc., according to production needs. During the processing process, it is necessary to deform it such as upsetting, drawing, reaming, bending, and deep drawing. Not good, coupled with the constraints of forging structure technology, forgings are usually only used as blanks for machine parts. Hot forging is a forging perform...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/04B21C1/02B21C43/04B21C43/02C21D9/52
CPCB21C1/02B21C37/042B21C43/02B21C43/04C21D9/525
Inventor 崔锡恩
Owner 青岛金越隆机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com